Method of making closely spaced contacts to PN-junction using stacked polysilicon layers, differential etching and ion implantations
Assignee: NXP USA Inc
•
Filing: 1985-03-15
•
Granted: 1986-02-25
•
Expires: 2005-03-15
Abstract
Abstract A means and method is described for forming closely spaced contacts to adjacent semiconductor regions, such as the base and emitter of a bipolar transistor, so that the lateral voltage drops between the contacts and an intervening junction are minimized. The emitter and base and the contacts thereto are self-aligned. This is accomplished by a structure utilizing two poly-layers separated by one or more intermediate dielectric layers. The upper of the two poly-layers serves as a selective etching mask for defining the contact geometry and separation. The lower of the two poly-layers has one portion which becomes a poly-contact and diffusion source for the base region and a second portion which becomes a poly-contact and diffusion source for the emitter region. A single mask is used in connection with ion bombardment to alter the etch rate of portions of the poly-layers. This mask together with subsequent etch steps, defines the emitter width and location and the base-emitter contact separation. The process is self-aligning.
Inventors
- 👤 Mark S. Birritella
- 👤 Kevin McLaughlin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:50
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10D10/00; H10D10/40; H10D10/441; Y; Y10; Y10S; Y10S148/00; Y10S148/01; Y10S438/00; Y10S438/98
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
457 words
A method for fabricating closely spaced contacts to a PN junction comprising: providing a semiconductor substrate having therein a first region of a first conductivity type and a second region of a second conductivity type overlying said first region; covering said second region with a first polycrystalline semiconductor layer; covering said first polycrystalline layer with a first dielectric layer; covering said first dielectric layer with a second dielectric layer; covering said second dielectric layer with a second polycrystalline layer; covering said second polycrystalline layer with a first masking layer; patterning said first masking layer to form an open region above a first portion of said second polycrystalline layer and a mask region above a second portion of said second polycrystalline layer; doping first portions of said first and second polycrystalline layers with an etch rate reducing dopant through said open region of said masking layer leaving second portions of said first and second polycrystalline layers under said mask region substantially free of said etch rate reducing dopant; removing a peripheral portion of said mask region to reduce its lateral extent by a predetermined amount; removing a first part of said second portion of said second polycrystalline layer leaving a second part underneath said mask region; then performing steps (a)-(d) in any order: (a) removing the remaining part of said mask region; (b) removing a first part of said second dielectric layer underlying said first part of said second portion of said second polycrystalline layer; (c) removing said second part of said second polycrystalline layer; and (d) after said first part of said second dielectric layer has been removed, removing a first part of said first dielectric layer underlying said first part of said second dielectric layer; thereafter performing the steps (i)-(v) in any order: (i) replacing a first part of said second portion of said first polycrystalline layer with a dielectric isolation region, leaving a second part of said second portion of said polycrystalline layer; (ii) removing a second part of said second dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iii) removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iv) doping a first portion of said second region of said substrate underlying said dielectric isolation region; and (v) doping said second part of said second portion of said first polycrystalline layer; thereafter heating said substrate to drive the dopant provided in step (v) above into a second portion of said second region of said substrate proximate to said first portion of said second region of said substrate; and providing contact means for contacting said second part of said second portion of said first polycrystalline layer.
Claim 2
Independent Claim
457 words
A method for fabricating closely spaced contacts to a PN junction comprising: providing a semiconductor substrate having therein a first region of a first conductivity type and a second region of a second conductivity type overlying said first region; covering said second region with a first polycrystalline semiconductor layer; covering said first polycrystalline layer with a first dielectric layer; covering said first dielectric layer with a second dielectric layer; covering said second dielectric layer with a second polycrystalline layer; covering said second polycrystalline layer with a first masking layer; patterning said first masking layer to form an open region above a first portion of said second polycrystalline layer and a mask region above a second portion of said second polycrystalline layer; doping first portions of said first and second polycrystalline layers with an etch rate reducing dopant through said open region of said masking layer leaving second portions of said first and second polycrystalline layers under said mask region substantially free of said etch rate reducing dopant; removing a peripheral portion of said mask region to reduce its lateral extent by a predetermined amount; removing a first part of said second portion of said second polycrystalline layer leaving a second part underneath said mask region; then performing steps (a)-(d) in any order: (a) removing the remaining part of said mask region; (b) removing a first part of said second dielectric layer underlying said first part of said second portion of said second polycrystalline layer; (c) removing said second part of said second polycrystalline layer; and (d) after said first part of said second dielectric layer has been removed, removing a first part of said first dielectric layer underlying said first part of said second dielectric layer; thereafter performing the steps (i)-(v) in any order: (i) replacing a first part of said second portion of said first polycrystalline layer with a dielectric isolation region, leaving a second part of said second portion of said polycrystalline layer; (ii) removing a second part of said second dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iii) removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iv) doping a first portion of said second region of said substrate underlying said dielectric isolation region; and (v) doping said second part of said second portion of said first polycrystalline layer; thereafter heating said substrate to drive the dopant provided in step (v) above into a second portion of said second region of said substrate proximate to said first portion of said second region of said substrate; and providing contact means for contacting said second part of said second portion of said first polycrystalline layer.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the step of doping with said etch rate reducing dopant comprises doping with a dopant of said second conductivity type.
Claim 4
Dependent Claim
27 words
The method of claim 1 wherein said step of removing a peripheral portion of said mask region comprises removing said peripheral portion without a further masking operation.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein said step of removing a first part of said second portion of said second polycrystalline layer comprises removing said first part without a further masking operation.
Claim 6
Dependent Claim
56 words
The method of claim 1 wherein said step of removing a first part of said second portion of said second polycrystalline layer comprises removing said first part by means of differential etching with an etchant that attacks said first portion of said second polycrystalline layer less rapidly than said second portion of said second polycrystalline layer.
Claim 7
Dependent Claim
111 words
The method of claim 1 wherein said step of replacing a first part of said second portion of said first polycrystalline layer with a dielectric isolation region comprises removing a first part of said second portion of said first polycrystalline layer by means of differential etching with an etchant that attacks said first portion of said first polycrystalline layer less rapidly than said second portion of said first polycrystalline layer, leaving a second part of said second portion of said first polycrystalline layer, and then forming a dielectric isolation region between said first portion of said polycrystalline layer and said second part of said second portion of said first polycrystalline layer.
Claim 8
Dependent Claim
41 words
The method of claim 1 wherein said step of removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer comprises removing said second part without a further masking operation.
Claim 9
Dependent Claim
35 words
The method of claim 1 wherein said step of doping a first portion of said second region of said substrate underlying said dielectric isolation region comprises doping said first portion without a further masking operation.
Claim 10
Dependent Claim
39 words
The method of claim 1 wherein said step of doping a first portion of said second region of said substrate underlying said dielectric isolation region comprises doping said first portion to a higher level of said second conductivity type.
Claim 11
Dependent Claim
35 words
The method of claim 1 wherein said step of doping said second part of said second portion of said first polycrystalline layer comprises doping said second part with an impurity of said first conductivity type.
Claim 12
Dependent Claim
31 words
The method of claim 1 wherein said step of doping said second part of said second portion of said polycrystalline layer comprises doping said second part without a further masking operation.
Claim 13
Dependent Claim
23 words
The method of claim 1 wherein said first covering step comprises covering said second region with a substantially undoped first polycrystalline semiconductor layer.
Claim 14
Dependent Claim
24 words
The method of claim 1 wherein said fourth covering step comprises covering said second dielectric layer with a substantially undoped second polycrystalline semiconductor layer.
Claim 15
Dependent Claim
38 words
The method of claim 6 wherein said step of removing a first part of said second portion of said first polycrystalline layer comprises removing said first part so as to penetrate to said second region of said substrate.
Claim 16
Dependent Claim
46 words
The method of claim 6 wherein said step of forming a dielectric isolation region between said first portion of said polycrystalline layer and said second part of said second portion of said first polycrystalline layer comprises forming said dielectric isolation region without a further masking operation.
Claim 17
Independent Claim
414 words
A method for fabricating closely spaced contacts to a PN junction comprising: providing a semiconductor substrate having therein a first region of a first conductivity type and a second region of a second conductivity type overlying said first region; covering said second region with a first polycrystalline semiconductor layer; covering said first polycrystalline layer with a first dielectric layer; covering said first dielectric layer with a second polycrystalline layer; covering said second polycrystalline layer with a first masking layer; patterning said first masking layer to form an open region above a first portion of said second polycrystalline layer and a mask region above a second portion of said second polycrystalline layer; doping first portions of said first and second polycrystalline layers with an etch rate reducing dopant through said open region of said masking layer leaving second portions of said first and second polycrystalline layers under said mask region substantially free of said etch reducing dopant; removing a peripheral portion of said mask region to reduce its lateral extent by a predetermined amount; removing a first part of said second portion of said second polycrystalline layer leaving a second part underneath said mask region; then performing steps (a)-(c) in any order: (a) removing the remaining part of said mask region; (b) removing said second part of said second polycrystalline layer; and (c) removing a first part of said first dielectric layer underlying said first part of said second portion of said second polycrystalline layer; thereafter performing steps (i)-(v) in any order: (i) replacing a first part of said second portion of said first polycrystalline layer with a dielectric isolation region, leaving a second part of said second portion of said polycrystalline layer; (ii) removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iii) doping a first portion of said second region of said substrate underlying said dielectric isolation region; and (iv) doping said second part of said second portion of said first polycrystalline layer with said first conductivity type; thereafter performing the following: heating said substrate to drive the dopant provided in step (iv) above into a second portion of said second region of said substrate proximate to said first portion of said second region of said substrate; providing first contact means for contacting said second part of said second portion of said first polycrystalline layer; and providing second contact means for contacting said first portion of said first polycrystalline layer.
Claim 18
Independent Claim
414 words
A method for fabricating closely spaced contacts to a PN junction comprising: providing a semiconductor substrate having therein a first region of a first conductivity type and a second region of a second conductivity type overlying said first region; covering said second region with a first polycrystalline semiconductor layer; covering said first polycrystalline layer with a first dielectric layer; covering said first dielectric layer with a second polycrystalline layer; covering said second polycrystalline layer with a first masking layer; patterning said first masking layer to form an open region above a first portion of said second polycrystalline layer and a mask region above a second portion of said second polycrystalline layer; doping first portions of said first and second polycrystalline layers with an etch rate reducing dopant through said open region of said masking layer leaving second portions of said first and second polycrystalline layers under said mask region substantially free of said etch reducing dopant; removing a peripheral portion of said mask region to reduce its lateral extent by a predetermined amount; removing a first part of said second portion of said second polycrystalline layer leaving a second part underneath said mask region; then performing steps (a)-(c) in any order: (a) removing the remaining part of said mask region; (b) removing said second part of said second polycrystalline layer; and (c) removing a first part of said first dielectric layer underlying said first part of said second portion of said second polycrystalline layer; thereafter performing steps (i)-(v) in any order: (i) replacing a first part of said second portion of said first polycrystalline layer with a dielectric isolation region, leaving a second part of said second portion of said polycrystalline layer; (ii) removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer; (iii) doping a first portion of said second region of said substrate underlying said dielectric isolation region; and (iv) doping said second part of said second portion of said first polycrystalline layer with said first conductivity type; thereafter performing the following: heating said substrate to drive the dopant provided in step (iv) above into a second portion of said second region of said substrate proximate to said first portion of said second region of said substrate; providing first contact means for contacting said second part of said second portion of said first polycrystalline layer; and providing second contact means for contacting said first portion of said first polycrystalline layer.
Claim 19
Dependent Claim
26 words
The method of claim 16 wherein the step of doping with said etch rate reducing dopant comprises doping with a dopant of said second conductivity type.
Claim 20
Dependent Claim
27 words
The method of claim 16 wherein said step of removing a peripheral portion of said mask region comprises removing said peripheral portion without a further masking operation.
Claim 21
Dependent Claim
32 words
The method of claim 16 wherein said step of removing a first part of said second portion of said second polycrystalline layer comprises removing said first part without a further masking operation.
Claim 22
Dependent Claim
56 words
The method of claim 16 wherein said step of removing a first part of said second portion of said second polycrystalline layer comprises removing said first part by means of differential etching with an etchant that attacks said first portion of said second polycrystalline layer less rapidly than said second portion of said second polycrystalline layer.
Claim 23
Dependent Claim
64 words
The method of claim 16 wherein said step of replacing a first part of said second portion of said first polycrystalline layer comprises removing a first part of said second portion of said first polycrystalline layer and thereafter forming a dielectric isolation region between said first portion of said first polycrystalline layer and said second part of said second portion of said polycrystalline layer.
Claim 24
Dependent Claim
39 words
The method of claim 16 wherein said step of removing a second part of said first dielectric layer overlying said second part of said second portion of said first polycrystalline layer comprises removing part without a further masking operation.
Claim 25
Dependent Claim
35 words
The method of claim 16 wherein said step of doping a first portion of said second region of said substrate underlying said dielectric isolation region comprises doping said first portion without a further masking operation.
Claim 26
Dependent Claim
39 words
The method of claim 16 wherein said step of doping a first portion of said second region of said substrate underlying said dielectric isolation region comprises doping said first portion to a higher level of said second conductivity type.
Claim 27
Dependent Claim
32 words
The method of claim 16 wherein said step of doping said second part of said second portion of said first polycrystalline layer comprises doping said second part without a further masking operation.
Claim 28
Dependent Claim
32 words
The method of claim 16 wherein said step of doping said second part of said second portion of said first polycrystalline layer comprises doping with an impurity of said first conductivity type.
Claim 29
Dependent Claim
23 words
The method of claim 16 wherein said first covering step comprises covering said second region with a substantially undoped first polycrystalline semiconductor layer.
Claim 30
Dependent Claim
24 words
The method of claim 16 wherein said third covering step comprises covering said first dielectric layer with a substantially undoped second polycrystalline semiconductor layer.
Claim 31
Dependent Claim
55 words
The method of claim 21 wherein said step of removing a first part of said second portion of said first polycrystalline layer comprises removing said first part by means of differential etching with an etchant that attacks said first portion of said polycrystalline layer less rapidly than said second portion of said first polycrystalline layer.
Claim 32
Dependent Claim
38 words
The method of claim 21 wherein said step of removing a first part of said second portion of said first polycrystalline layer comprises removing said first part so as to penetrate to said second region of said substrate.
Claim 33
Dependent Claim
47 words
The method of claim 21 wherein said step of forming a dielectric isolation region between said first portion of said first polycrystalline layer and said second part of said second portion of said first polycrystalline layer comprises forming said dielectric isolation region without a further masking operation.
References Cited (Backward Citations)
US4368573A
Cited
US4252581A
Cited
US4404737A
Cited
US4252582A
Cited
US4408388A
Cited
US4378630A
Cited
US4378627A
Cited
US4418468A
Cited
US4433470A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-24 | 1989-08-26 | 1990-02-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-24 | 1993-08-26 | 1994-02-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-24 | 1997-08-26 | 1998-02-25 | $7700.00 | Window Closed / Lapsed |