Releasable film forming compositions
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1983-06-15
•
Granted: 1986-02-11
•
Expires: 2003-06-15
Abstract
Abstract PCT No. PCT/JP83/00192 Sec. 371 Date Feb. 15, 1984 Sec. 102(e) Date Feb. 15, 1984 PCT Filed Jun. 15, 1983 PCT Pub. No. WO84/00034 PCT Pub. Date Jan. 5, 1984.The present invention provides a releasable film forming composition comprising (1) an organopolysiloxane having hydroxyl groups at the ends of the molecular chain, (2) a finely divided silica, (3) a phenyl-containing organosilane or organopolysiloxane, (4) an organohydrogenpolysiloxane containing at least three SiH groups per molecule, (5) a metallic salt of an organic acid and (6) an organic solvent, and a process for preparing same, as well as a releasable film forming composition comprising (1) an organopolysiloxane containing at least two silicon atom-bonded alkenyl groups per molecule, (2) a finely divided silica, (3) a phenyl-containing organosilane or organopolysiloxane, (4) an organohydrogenpolysiloxane containing at least two SiH groups per molecule, (5) a platinic compound and (6) an organic solvent, and a process for preparing same. These compositions exhibit a superior printability and a stable releasability from adhesive materials and are less slippery.
Inventors
- 👤 Shosaku Sasaki
- 👤 Nobuo Kaiya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:13
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C08G77/20; C08G77/70; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
173 words
A releasable film forming composition comprising: (1) 100 parts by weight of a substantially straight-chain organopolysiloxane having hydroxyl groups at the ends of the molecular chain and having a viscosity not lower than 1,000 centipoise at 25° C., at least 80 mol % of the organic groups being methyl; (2) 5 to 80 parts by weight of a finely divided silica; (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR4## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100; (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane having at least three SiH groups per molecule; (5) a catalytic amount of a metal salt of an organic acid in which the metal is selected from the group consisting of tin, zinc, lead and iron; and (6) an amount of an organic solvent sufficient to dissolve component (1).
Claim 2
Dependent Claim
173 words
A releasable film forming composition comprising: (1) 100 parts by weight of a substantially straight-chain organopolysiloxane having hydroxyl groups at the ends of the molecular chain and having a viscosity not lower than 1,000 centipoise at 25° C., at least 80 mol % of the organic groups being methyl; (2) 5 to 80 parts by weight of a finely divided silica; (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR4## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100; (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane having at least three SiH groups per molecule; (5) a catalytic amount of a metal salt of an organic acid in which the metal is selected from the group consisting of tin, zinc, lead and iron; and (6) an amount of an organic solvent sufficient to dissolve component (1).
Claim 3
Dependent Claim
18 words
The composition of claim 1 wherein said finely divided silica as component (2) is a wet process silica.
Claim 4
Dependent Claim
26 words
The composition of claim 1 wherein said finely divided silica as component (2) is a mixture of a wet process silica and a dry process silica.
Claim 5
Dependent Claim
191 words
A process for preparing a releasable film forming composition, which process comprises kneading under heating (1) 100 parts by weight of a substantially straight-chain organosiloxane having hydroxyl groups at the ends of the molecular chain and having a viscosity not lower than 1,000 centipoise at 25° C., at least 80 mol % of the organic groups being methyl, (2) 5 to 80 parts by weight of a finely divided silica and (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR5## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100, and then dissolving the resulting mixture in an amount of an organic solvent sufficient to dissolve component (1) together with (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane having at least three SiH groups per molecule and (5) a catalytic amount of a metal salt of an organic acid in which the metal is selected from the group consisting of tin, zinc, lead and iron.
Claim 6
Dependent Claim
191 words
A process for preparing a releasable film forming composition, which process comprises kneading under heating (1) 100 parts by weight of a substantially straight-chain organosiloxane having hydroxyl groups at the ends of the molecular chain and having a viscosity not lower than 1,000 centipoise at 25° C., at least 80 mol % of the organic groups being methyl, (2) 5 to 80 parts by weight of a finely divided silica and (3) 2 to 40 parts by weight of a phenyl-containing organosilane or organopolysiloxane represented by the general formula ##STR5## wherein R 1 and R 2 are each a monovalent hydrocarbon group, at least 25 mol % of R 1 and R 2 being phenyl, and n is a number of 1 to 100, and then dissolving the resulting mixture in an amount of an organic solvent sufficient to dissolve component (1) together with (4) 0.5 to 40 parts by weight of an organohydrogenpolysiloxane having at least three SiH groups per molecule and (5) a catalytic amount of a metal salt of an organic acid in which the metal is selected from the group consisting of tin, zinc, lead and iron.
Claim 7
Dependent Claim
10 words
The composition of claim 1 wherein the metal is tin.
Claim 8
Dependent Claim
10 words
The process of claim 4 wherein the metal is tin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-10 | 1989-08-12 | 1990-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-10 | 1993-08-12 | 1994-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-10 | 1997-08-12 | 1998-02-11 | $7700.00 | Window Closed / Lapsed |