US4564541A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plastic laminate structure and vessel
Assignee: Henkel AG and Co KGaA
•
Filing: 1984-02-07
•
Granted: 1986-01-14
•
Expires: 2004-02-07
Abstract
Abstract Disclosed is a laminate structure comprising a layer of a creep-resistant resin composed mainly of ester recurring units and a gas barrier layer containing an olefin-vinyl alcohol copolymer, which are laminated through a thermoplastic resin adhesive layer, wherein the adhesive resin is composed of a copolyester or copolyester composition comprising in the main chain at least two acid components selected from (i) an isophthalic acid component, (ii) a terephthalic acid component and (iii) a linear or cyclic aliphatic dibasic acid component.
Inventors
- 👤 Kazuo Taira
- 👤 Akira Sakamoto
- 👤 Muneki Yamada
- 👤 Masanori Aizawa
- 👤 Hiroshi Ueno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:20
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B1/00; B32B27/30; B32B27/306; B32B27/308; B32B27/36; B32B27/365; B32B7/00; B32B7/04; B32B7/12; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B65D1/0215; B65D65/00; B65D65/38; B65D65/40; B32B2272/00; B32B2307/00; B32B2307/50; B32B2307/548; B32B2307/70; B32B2307/724; B32B2307/7242; B32B2367/00; B32B2369/00; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1334; Y10T428/1341; Y10T428/1352; Y10T428/1379; Y10T428/28; Y10T428/2852; Y10T428/31504; Y10T428/31507; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31909
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
138 words
A laminate structure comprising (1) a layer of a creep-resistant resin composed of ester recurring units selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate, polycarbonate and polyarylate and (2) a gas barrier layer containing an olefin-vinyl alcohol copolymer, said layers (1) and (2) being laminated through (3) a thermoplastic resin adhesive layer, wherein the adhesive resin is composed of a copolyester or copolyester composition comprising in the main chain at least two acid components selected from (i) an isophthalic acid component, (ii) a terephthalic acid component and (iii) a linear or cyclic aliphatic dibasic acid component, and at least one glycol component selected from the group consisting of ethylene glycol, propylene glycol, 1,4-butane diol, neopentyl glycol, cyclohexane diol, xylene glycol and hexahydroxylene glycol, said copolyester having a glass transition temperature (Tg) of -40° to 75° C.
Claim 2
Dependent Claim
138 words
A laminate structure comprising (1) a layer of a creep-resistant resin composed of ester recurring units selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate, polycarbonate and polyarylate and (2) a gas barrier layer containing an olefin-vinyl alcohol copolymer, said layers (1) and (2) being laminated through (3) a thermoplastic resin adhesive layer, wherein the adhesive resin is composed of a copolyester or copolyester composition comprising in the main chain at least two acid components selected from (i) an isophthalic acid component, (ii) a terephthalic acid component and (iii) a linear or cyclic aliphatic dibasic acid component, and at least one glycol component selected from the group consisting of ethylene glycol, propylene glycol, 1,4-butane diol, neopentyl glycol, cyclohexane diol, xylene glycol and hexahydroxylene glycol, said copolyester having a glass transition temperature (Tg) of -40° to 75° C.
Claim 3
Dependent Claim
18 words
A sealing and packaging multi-layer plastic vessel formed of a laminate structure as set forth in claim 1.
Claim 4
Dependent Claim
16 words
A vessel as set forth in claim 2, which is in the form of a cup.
Claim 5
Dependent Claim
16 words
A vessel as set forth in claim 2, which is in the form of a pouch.
Claim 6
Dependent Claim
16 words
A vessel as set forth in claim 2, which is in the form of a bottle.
Claim 7
Dependent Claim
20 words
A vessel as set forth in claim 5, wherein the vessel wall is molecularly oriented in at least one direction.
Claim 8
Dependent Claim
22 words
A laminate structure as set forth in claim 1, wherein the creep-resistant resin is a polyester composed mainly of ethylene terephthalate units.
Claim 9
Dependent Claim
22 words
A laminate structure as set forth in claim 1, wherein the creep-resistant resin is a polyester composed mainly of butylene terephthalate units.
Claim 10
Dependent Claim
16 words
A laminate structure as set forth in claim 1, wherein the creep-resistant resin is a polycarbonate.
Claim 11
Dependent Claim
16 words
A laminate structure as set forth in claim 1, wherein the creep-resistant resin is a polyarylate.
Claim 12
Dependent Claim
43 words
A laminate structure as set forth in claim 1, wherein the olefin-vinyl alcohol copolymer is a saponified copolymer obtained by saponifying an ethylene-vinyl acetate copolymer having an ethylene content of 20 to 60 mole % to a saponification degree of at least 95%.
Claim 13
Dependent Claim
49 words
A laminate structure as set forth in claim 1 wherein said at least one glycol component comprises 1,4-butane diol or a combination of 1,4-butane diol with at least one glycol component selected from the group consisting of ethylene glycol, propylene glycol, neopentylglycol, cyclohexane diol, xylene glycol and hexahydroxylene glycol.
Claim 14
Dependent Claim
46 words
A laminate structure as set forth in claim 1, wherein the adhesive resin is a copolyester or copolyester composition comprising at least 25 mole % of an aromatic dibasic acid component and 5 to 75 mole % of a linear or cyclic aliphatic dibasic acid component.
Claim 15
Dependent Claim
21 words
A laminate structure as set forth in claim 13, wherein the aliphatic dibasic acid component has 4 to 12 carbon atoms.
Claim 16
Dependent Claim
23 words
A laminate structure as set forth in claim 13, wherein the copolyester or copolyester composition comprises as the glycol component a 1,4-butane-diol component.
Claim 17
Dependent Claim
20 words
A laminate structure as set forth in claim 13, wherein the aromatic dibasic acid component is an isophthalic acid component.
Claim 18
Dependent Claim
38 words
A laminate structure as set forth in claim 1, wherein the adhesive resin is composed of a thermoplastic copolyester or copolyester composition containing in the main chain terephthalic acid and isophthalic acid components as the dibasic acid component.
Claim 19
Dependent Claim
36 words
A laminate structure as set forth in claim 17, wherein the copolyester or copolyester composition contains an isophthalic acid component in an amount of at least 5 mole % based on the total dibasic acid component.
Claim 20
Dependent Claim
16 words
A laminate structure as set forth in claim 17, wherein the thermoplastic copolyester is polybutylene terephthalate/isophthalate.
Claim 21
Dependent Claim
16 words
A laminate structure as set forth in claim 17, wherein the thermoplastic copolyester is polyethylene terephthalate/isophthalate.
Claim 22
Dependent Claim
23 words
A laminate structure as set forth in claim 17, wherein the thermoplastic copolyester composition is a mixture of polybutylene terephthalate/isophthalate and polyethylene terephthalate/isophthalate.
Claim 23
Dependent Claim
50 words
The laminate structure as set forth in claim 1 wherein the adhesive resin consists essentially of the copolyester or a mixture of two or more of said copolyesters or a mixture of said copolyester with up to 30% by weight, based on the total adhesive, of an olefinic thermoplastic resin.
Claim 24
Dependent Claim
51 words
The laminate structure as set forth in claim 22 wherein the olefinic thermoplastic resin is selected from the group consisting of polyethylene, polypropylene, an ethylene-propylene copolymer, an ethylene-butene-1 copolymer, an ion-crosslinked olefin copolymer (ionomer), an ethylene-vinyl acetate copolymer, an ethylene-acrylic acid copolymer, an ethylene-ethylacrylate copolymer, an acid-modified polyethylene and acid-modified polypropylene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-13 | 1989-07-15 | 1990-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-13 | 1993-07-15 | 1994-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-13 | 1997-07-15 | 1998-01-14 | $7700.00 | Window Closed / Lapsed |