Method of producing a container
Assignee: Rexam AB
•
Filing: 1982-11-23
•
Granted: 1986-01-14
•
Expires: 2002-11-23
Abstract
Abstract A method of producing a container of polyethylene terephthalate or similar thermoplastic material from a tubular blank of amorphous material. A mechanical forming element moves a transitional zone between amorphous (thicker) material and thinner oriented material stretched to flow during simultaneous elongation of the blank in the direction of movement of the transitional zone. The stretched and oriented material is heated to a temperature higher than the temperature of the material immediately before stretching. As a result, the internal stresses produced in the material during earlier stretching are relieved. Heating causes the length of the material in the direction of stretching also to be reduced. Each subsequent forming stage for shaping the container takes place at a temperature lower than the temperature at the immediately preceding forming stage.
Inventors
- 👤 Torsten Nilsson
- 👤 Kjell M. Jakobsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:23
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/42; B29C49/48; B29C49/4802; B29C49/071; B29C49/08; B29C49/10; B29C49/64; B29C49/6409; B29C55/00; B29C55/30; B29C67/00; B29C67/0014; B29C2049/4879; B29C2049/4881; B29C2949/00; B29C2949/07; B29C2949/072; B29C2949/0725; B29C2949/073; B29C2949/0731; B29C2949/0733; B29C2949/0734; B29C2949/076; B29C2949/0768; B29C2949/077; B29C2949/0771; B29C2949/078; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/26; B29C2949/28; B29K; B29K2067/00; B29L; B29L2031/00; B29L2031/712; B29L2031/7158; B29L2031/716
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
164 words
A method of producing a container of thermoplastic material, preferably of polyethylene terephthalate (PET) from a tubular blank of amorphous material, said container having a body and a mouth portion, said method comprising reducing the wall thickness of a tubular blank of amorphous material while concurrently elongating the blank at a temperature conducive to orientation to orient the material of the thus stretched blank by engaging a mechanical forming element with said blank to form a transition zone between amorphous, thicker material and oriented, thinner material and relatively moving said blank and forming element to move said transition zone axially of the blank while concurrently elongating the blank, heating the thus stretched blank to a temperature above the temperature of the blank immediately before stretching to relieve internal stresses produced in said material during stretching, forming the container from the stretched blank in successive forming stages, and maintaining the temperature in each forming stage lower than the temperature in the immediately preceding forming stage.
Claim 2
Independent Claim
164 words
A method of producing a container of thermoplastic material, preferably of polyethylene terephthalate (PET) from a tubular blank of amorphous material, said container having a body and a mouth portion, said method comprising reducing the wall thickness of a tubular blank of amorphous material while concurrently elongating the blank at a temperature conducive to orientation to orient the material of the thus stretched blank by engaging a mechanical forming element with said blank to form a transition zone between amorphous, thicker material and oriented, thinner material and relatively moving said blank and forming element to move said transition zone axially of the blank while concurrently elongating the blank, heating the thus stretched blank to a temperature above the temperature of the blank immediately before stretching to relieve internal stresses produced in said material during stretching, forming the container from the stretched blank in successive forming stages, and maintaining the temperature in each forming stage lower than the temperature in the immediately preceding forming stage.
Claim 3
Dependent Claim
36 words
A method as claimed in claim 1 wherein the temperature of the material in the last of said successive forming stages is higher than the highest temperature at which the formed container is to be used.
Claim 4
Dependent Claim
71 words
A method as claimed in claim 1 wherein the length of the amorphous blank and the length of the stretched blank are correlated with the highest temperature of the material during said forming of the blank into the container such that the length of the stretched material of the blank after heating to the highest temperature is substantially equal to the corresponding profile length of the material in the formed container.
Claim 5
Dependent Claim
66 words
A method as claimed in claim 1 wherein said material is polyethylene terephthalate (PET) and the highest temperature of the material during said forming of the blank to the container is a maximum of approximately 160° C. in the first forming stage, the material in each subsequent forming stage having a temperature lower than the temperature in the immediately preceding forming stage by approximately 5° C.
Claim 6
Dependent Claim
42 words
A method as claimed in claim 1 wherein the temperature of the material, when it passes the mechanical forming element to undergo flow, has a temperature in the range of or slightly higher than the glass transformation temperature (TG) of the material.
Claim 7
Dependent Claim
33 words
A method as claimed in claim 5 wherein said material is polyethylene terephthalate (PET), the material having a temperature of at least 70° C. when passing the mechanical forming element to undergo flow.
Claim 8
Dependent Claim
25 words
A method as claimed in claim 6 wherein the temperature of the material when passing the mechanical forming element is between 70° and 105° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-13 | 1989-07-15 | 1990-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-13 | 1993-07-15 | 1994-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-13 | 1997-07-15 | 1998-01-14 | $7700.00 | Window Closed / Lapsed |