Method for producing a tubular object of polyethylene terephthalate or similar thermoplastic material from a tubular blank of amorphous material
Assignee: Rexam AB
•
Filing: 1981-05-18
•
Granted: 1983-09-20
•
Expires: 2001-05-18
Abstract
Abstract An object is produced from a tubular blank (10,15,17) of thermoplastic material of polyester or polyamide, preferably of polyethylene terephthalate by reducing the thickness of amorphous material in one or several areas of the blank by means of one or several consecutive re-shaping operations. A mechanical shaping device (23,29,71,81) moves a transitional zone (13,14,113) situated between thicker and thinner material along the blank and simultaneously elongates the blank in the moving direction of the transitional zone while reducing the thickness. After the last re-shaping operation the thinner material preferably has an oriented state. During the re-shaping operation the temperature of the material in the transitional zone (13,14,113) is controlled at a level which, immediately before the re-shaping operation, is within or close to the range of the glass transition temperature (TG). In one embodiment the reduction of the wall thickness of the material is begun in a track (12) in the wall of the blank and continues symmetrically around the track. Clamping devices (41,51,61) are used to maintain the axial position of the blank. The blank is suitable for re-shaping, for instance, into a container in which the mouth also consists of oriented material.
Inventors
- 👤 Kjell M. Jakobsen
- 👤 Claes T. Nilsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:51
CPC Classifications
B; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B29; B29C; B29C31/00; B29C31/002; B29C49/00; B29C49/071; B29C49/08; B29C49/10; B29C49/14; B29C49/42; B29C49/48; B29C49/54; B29C49/541; B29C55/00; B29C55/22; B29C55/30; B29C59/00; B29C59/02; B29C59/04; B29C59/043; B29C67/00; B29C67/0003; B29C67/0014; B65D1/0223; B29C43/00; B29C43/32; B29C43/36; B29C43/361; B29C2043/3615; B29C2043/3631; B29C2793/00; B29C2793/009; B29C2949/00; B29C2949/07; B29C2949/072; B29C2949/0723; B29C2949/073; B29C2949/0732; B29C2949/076; B29C2949/0768; B29C2949/077; B29C2949/0772; B29C2949/0776; B29C2949/078; B29C2949/079; B29C2949/08; B29C2949/0861; B29C2949/0862; B29K; B29K2067/00; B29K2105/00; B29K2105/25; B29K2105/253; B29K2105/258; B29K2995/00; B29K2995/0037; B29K2995/004; Y; Y10; Y10S; Y10S425/00; Y10S425/218; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/139; Y10T428/1397
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
207 words
A method for producing an object of polyethylene terephthalate or similar thermoplastic material from a tubular blank with a wall of essentially amorphous material, said object being adapted to be reshaped into a container, said method comprising forming the wall of the tubular blank with a region of thinner material and a transitional zone between the thinner material and a remaining thicker portion of said wall, engaging a mechanical shaping device with said transitional zone, applying axial force to said transitional zone by relatively moving said shaping device and blank axially to move said transitional zone axially relative to said blank while simultaneously elongating the blank by increasing the length of the region of thinner material of the blank and reducing the length of said thicker portion of the blank and effecting an orientation of the thus elongated and reduced thickness of the blank in said region of thinner material corresponding to the orientation which would be obtained by monoaxially stretching to yielding a sheet of amorphous material of the same thickness of said wall of the tubular blank, the temperature of the material at the commencement of reduction of thickness being not higher than in the vicinity of the glass transition temperature (TG) of the material.
Claim 2
Independent Claim
207 words
A method for producing an object of polyethylene terephthalate or similar thermoplastic material from a tubular blank with a wall of essentially amorphous material, said object being adapted to be reshaped into a container, said method comprising forming the wall of the tubular blank with a region of thinner material and a transitional zone between the thinner material and a remaining thicker portion of said wall, engaging a mechanical shaping device with said transitional zone, applying axial force to said transitional zone by relatively moving said shaping device and blank axially to move said transitional zone axially relative to said blank while simultaneously elongating the blank by increasing the length of the region of thinner material of the blank and reducing the length of said thicker portion of the blank and effecting an orientation of the thus elongated and reduced thickness of the blank in said region of thinner material corresponding to the orientation which would be obtained by monoaxially stretching to yielding a sheet of amorphous material of the same thickness of said wall of the tubular blank, the temperature of the material at the commencement of reduction of thickness being not higher than in the vicinity of the glass transition temperature (TG) of the material.
Claim 3
Dependent Claim
35 words
A method as claimed in claim 1 wherein a plurality of regions of thinner material are provided and the blank is elongated and reduced in thickness and the material oriented in a plurality of locations.
Claim 4
Dependent Claim
29 words
A method as claimed in claim 1 wherein the reduction of thickness of the blank is effected in a plurality of consecutive elongations of the wall of the blank.
Claim 5
Dependent Claim
44 words
A method as claimed in claim 1 wherein immediately before reduction in thickness of the wall of the blank, the material which will undergo said reduction in thickness is maintained at a temperature not greater than the glass transition temperature (TG) of the material.
Claim 6
Dependent Claim
64 words
A method as claimed in claim 1 wherein said shaping device is in contact with and forms a bearing surface against the material in the transitional zone, said material in the transitional zone being maintained at a temperature in the vicinity of but not greater than the glass transition temperature (TG) by effecting transfer of heat to the material from the mechanical shaping device.
Claim 7
Dependent Claim
32 words
A method as claimed in claim 1 comprising cooling the material of the blank after it has assumed its reduced wall thickness immediately to a temperature below its glass transition temperature (TG).
Claim 8
Dependent Claim
38 words
A method as claimed in claim 1 wherein during the forming of the object, the external circumference of the cross-section of those sections of the material in which the thickness of the material is reduced will become smaller.
Claim 9
Dependent Claim
38 words
A method as claimed in claim 1 wherein during the forming of the object the internal circumference of the cross-section of those sections of the material in which the thickness of the material is reduced will become larger.
Claim 10
Dependent Claim
35 words
A method as claimed in claim 1 comprising separating the blank in the region in which the thickness has been reduced to obtain a plurality of objects each having an area of reduced wall thickness.
Claim 11
Dependent Claim
41 words
A method as claimed in claim 1 wherein said region of thinner material in the wall of the blank is an annular groove in the periphery of the blank, the reduction in thickness being effected in opposite directions from said groove.
Claim 12
Dependent Claim
73 words
A method as claimed in claim 10 comprising inserting as mandrel in said tubular blank prior to its reduction in thickness and holding the material of the blank against the mandrel as the wall of the blank is being elongated and reduced in thickness to secure the position of the blank relative to the mandrel, at least during an initial stage of reduction of thickness of said wall by said mechanical shaping device.
Claim 13
Dependent Claim
27 words
A method as claimed in claim 1 comprising sealing one end of the tubular blank by heating the material and press-moulding the end in a cup-shaped mould.
Claim 14
Dependent Claim
55 words
A method as claimed in claim 1 wherein said material is polyethylene terephthalate and the thickness of the reduced thickness is approximately 1/3 of the original thickness of the material, the temperature of said material, at least immediately before the final reduction in thickness takes place, being not greater than the glass transition temperature (TG).
Claim 15
Dependent Claim
22 words
A method as claimed in claim 13 wherein said temperature is between 3° and 15° C. less than said glass transition temperature.
Claim 16
Dependent Claim
30 words
A method as claimed in claim 1 wherein said forming of the wall of the tubular blank with the region of thinner material is effected by said mechanical shaping device.
Claim 17
Dependent Claim
26 words
A method as claimed in claim 1 wherein said region of thinner material in the wall of the blank is monaxially oriented as it is formed.
Claim 18
Dependent Claim
22 words
A method as claimed in claim 1 wherein said temperature of the material deviates from TG by no more than 15° C.
Claim 19
Dependent Claim
22 words
A method as claimed in claim 1 wherein said temperature of the material deviates from TG by no more than 3° C.
Claim 20
Dependent Claim
26 words
A method as claimed in claim 1 wherein the temperature of the material in the transitional zone exceeds the glass transition temperature (TG) of the material.
Claim 21
Dependent Claim
40 words
A method as claimed in claim 15 wherein the formation of the transitional zone and the elongation and orientation of the region of thinner material is effected by fixing the position of the blank and axially moving the shaping device.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-19 | 1987-03-21 | 1987-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-19 | 1991-03-21 | 1991-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-19 | 1995-03-21 | 1995-09-20 | $7700.00 | Window Closed / Lapsed |