US4563433A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ceramic material and method of manufacture
Assignee: Kennametal Inc
•
Filing: 1983-02-15
•
Granted: 1986-01-07
•
Expires: 2003-02-15
Abstract
Abstract A dual phase silicon aluminum oxynitride material comprising a first phase Si-Al-O-N, commonly referred to as β-Si-Al-O-N, and a second phase Si-Al-O-N referred to as α-Si-Al-O-N. In addition to the double phase Si-Al-O-Ns, there is included a glassy type material which can formulate up to ten percent by weight of the total composition. The material may be manufactured by forming a polytype material made from reacted alumina, aluminum nitride and silicon nitride. The polytype material may be mixed with further powders of silicon nitride and an oxide of yttrium, lithium or calcium and finally reacted to a double phase Si-Al-O-N material where hardness is increased as the additional α-Si-Al-O-N is increased without significantly affecting its strength. The material may be formed in situ by mixing aluminum nitride, alumina, silicon nitride, together with an oxide of yttrium, lithium or calcium. These materials can then be sintered to a final product containing a double phase Si-Al-O-N. Control of the alumina content in the polytype or in situ methods affects the percentage of α-Si-Al-O-N produced in the final product. The hardness of the material increases with the α-Si-Al-O-N content without significantly affecting its transverse rupture strength.
Inventors
- 👤 Russell L. Yeckley
- 👤 Bernard North
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:00
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
277 words
A method of producing a ceramic product, comprising the steps of forming a powder mixture consisting essentially of a first component consisting of compounds containing the elements of silicon, aluminum, oxygen and nitrogen in proportions such that the ratio of the total number of silicon and aluminum atoms to the total number of oxygen and nitrogen atoms lies in the range 0.735 to 0.77 and such that said compounds react together with the second component during the subsequent sintering process to produce a double phase ceramic material wherein a first phase obeys the general formula: Si 6-z Al z O z N 8-z where z is between 0.38 and 1.5; wherein a second phase obeys the general formula (Si, Al) 12 M x (O, N) 16 ; and wherein up to 10 percent by weight of a second component is in the form of an oxide of at least one of the further elements, yttrium, scandium, cerium, lanthanum and the metals of the lanthanide series; and wherein sintering said mixture in a non-reactive environment comprises placing said mixture in a graphite pot and covering with a mixture of boron nitride and silicon nitride powders while surrounding said graphite pot and said silicon nitride and boron nitride powders with a nitrogen gas, with or without the application of pressure, at a temperature between 1600 degrees Centigrade and 2000 degrees Centigrade and for a time, decreasing with increasing temperature, of at least ten minutes to at least five hours so as to produce a ceramic material containing said double phase ceramic material together with a second phase containing said at least one further element, which is a glassy phase.
Claim 2
Independent Claim
277 words
A method of producing a ceramic product, comprising the steps of forming a powder mixture consisting essentially of a first component consisting of compounds containing the elements of silicon, aluminum, oxygen and nitrogen in proportions such that the ratio of the total number of silicon and aluminum atoms to the total number of oxygen and nitrogen atoms lies in the range 0.735 to 0.77 and such that said compounds react together with the second component during the subsequent sintering process to produce a double phase ceramic material wherein a first phase obeys the general formula: Si 6-z Al z O z N 8-z where z is between 0.38 and 1.5; wherein a second phase obeys the general formula (Si, Al) 12 M x (O, N) 16 ; and wherein up to 10 percent by weight of a second component is in the form of an oxide of at least one of the further elements, yttrium, scandium, cerium, lanthanum and the metals of the lanthanide series; and wherein sintering said mixture in a non-reactive environment comprises placing said mixture in a graphite pot and covering with a mixture of boron nitride and silicon nitride powders while surrounding said graphite pot and said silicon nitride and boron nitride powders with a nitrogen gas, with or without the application of pressure, at a temperature between 1600 degrees Centigrade and 2000 degrees Centigrade and for a time, decreasing with increasing temperature, of at least ten minutes to at least five hours so as to produce a ceramic material containing said double phase ceramic material together with a second phase containing said at least one further element, which is a glassy phase.
Claim 3
Dependent Claim
37 words
The method according to claim 1 in which said non-reactive environment is created by placing said mixture in a graphite pot and covering with a 50/50 by weight percent mixture of boron nitride and silicon nitride powders.
Claim 4
Dependent Claim
71 words
A ceramic material of silicon aluminum oxynitride which is comprised of an α and β phase composite of the Si-Al-O-N material and a glassy phase wherein said α phase Si-Al-O-N ranges from 10 to 70 weight percent of said ceramic material, said β phase Si-Al-O-N ranges from 20 to 90 weight percent of said ceramic material and said glassy Phase ranges from 0.1 to 10 weight percent of said ceramic material.
Claim 5
Dependent Claim
71 words
A ceramic material of silicon aluminum oxynitride which is comprised of an α and β phase composite of the Si-Al-O-N material and a glassy phase wherein said α phase Si-Al-O-N ranges from 10 to 70 weight percent of said ceramic material, said β phase Si-Al-O-N ranges from 20 to 90 weight percent of said ceramic material and said glassy Phase ranges from 0.1 to 10 weight percent of said ceramic material.
Claim 6
Dependent Claim
27 words
A ceramic material of claim 3 which further comprises said ceramic material having a minimum hardness of 92.5 Rockwell "A" as measured with a 60 kilogram load.
Claim 7
Dependent Claim
29 words
A ceramic material according to claims 3 or 4 wherein said glassy phase may also comprise a crystalline phase from the group consisting of YAG, YAM, N-YAM and Y-N-α-Wollastonite.
Claim 8
Dependent Claim
71 words
A ceramic material of silicon aluminum oxynitride which consists essentially of an α and β phase composite of the Si-Al-O-N material and a glassy phase wherein said α phase Si-Al-O-N ranges from 10 to 70 weight percent of said ceramic material, said β phase Si-Al-O-N ranges from 20 to 90 weight percent of said ceramic material and said glassy phase ranges from 0.1 to 10 weight percent of said ceramic material.
Claim 9
Dependent Claim
71 words
A ceramic material of silicon aluminum oxynitride which consists essentially of an α and β phase composite of the Si-Al-O-N material and a glassy phase wherein said α phase Si-Al-O-N ranges from 10 to 70 weight percent of said ceramic material, said β phase Si-Al-O-N ranges from 20 to 90 weight percent of said ceramic material and said glassy phase ranges from 0.1 to 10 weight percent of said ceramic material.
Claim 10
Dependent Claim
28 words
A ceramic material of claim 6 which further consists of said ceramic material having a minimum hardness of 92.5 Rockwell "A" as measured with a 60 kilogram load.
Claim 11
Dependent Claim
29 words
A ceramic material according to claims 6 or 7 wherein said glassy phase may also contain a crystalline phase from the group consisting of YAG, YAM, N-YAM and Y-N-α-Wollastonite.
Claim 12
Dependent Claim
15 words
The method according to claim 1 wherein x ranges in value from 0.1 to 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-06 | 1989-07-08 | 1990-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-06 | 1993-07-08 | 1994-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-06 | 1997-07-08 | 1998-01-07 | $7700.00 | Window Closed / Lapsed |