Heat-hardenable reaction resin mixtures comprising polyfunctional epoxide, polyisocyanate prepolymer and a reaction accelerator which is either a tertiary amine or an imidazole
Assignee: Siemens AG
•
Filing: 1984-06-27
•
Granted: 1985-12-31
•
Expires: 2004-06-27
Abstract
Abstract The invention relates to heat-hardenable reaction resin mixtures which contain polyfunctional epoxides, polyfunctional isocyanates and a reaction accelerator as well as, optionally containing customary additives and/or fillers. The invention has the object of achieving reaction resin mixtures which are stable in storage, consist of individual components that are easy to mix, exhibit a prolonged prehardening period and permit at the same time the manufacture of materials which combine the good mechanical properties and the high temperature-cycle resistance of polyurethane structures with the good thermal properties of oxazolidinone and isocyanurate structures. According to the invention, the reaction resin mixtures contain as polyfunctional isocyanates, isocyanate prepolymerisates in the form of reaction products of diphenyl methanediisocyanate and a diol, or of an isocyanate mixture of diphenyl-methanediisocyanate and a polymethylenepolyphenylisocyanate (with a functionality greater than 2) and a diol. The prepolymerisates utilize 0.01 to 0.35 equivalents and preferably 0.05 to 0.2 equivalents of the diol per 1 equivalent of isocyanate; the mixture contains 0.2 to 5 equivalents isocyanate per 1 equivalent of epoxy. The reaction accelerator is a tertiary amine or an imidazole.
Inventors
- 👤 Wolfgang Rogler
- 👤 Helmut Markert
- 👤 Klaus Kretzschmar
- 👤 Gerhard Piecha
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:26
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/302; C; C08; C08G; C08G18/00; C08G18/003; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4028; H01B3/40
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
106 words
A heat-hardenable reaction resin mixture comprising: (a) a polyfunctional epoxide; (b) a polyfunctional isocyanate; and (c) a reaction accelerator selected from a tertiary amine or an imidazole, wherein; the polyfunctional isocyanate comprises an isocyanate prepolymerisate in the form of a reaction product of diphenylmethanediisocyanate and a diol or of a reaction product of a diol and an isocyanate mixture of diphenylmethanediisocyanate and a polymethylene polyphenylisocyanate having at least 2 isocyanate groups per molecule of monomer unit; the equivalent ratio of isocyanate to diol is from about 1:0.01 to about 1:0.35; and the equivalent ratio of epoxy to isocyanate to epoxy is from about 1:0.2 to 1:5.
Claim 2
Dependent Claim
106 words
A heat-hardenable reaction resin mixture comprising: (a) a polyfunctional epoxide; (b) a polyfunctional isocyanate; and (c) a reaction accelerator selected from a tertiary amine or an imidazole, wherein; the polyfunctional isocyanate comprises an isocyanate prepolymerisate in the form of a reaction product of diphenylmethanediisocyanate and a diol or of a reaction product of a diol and an isocyanate mixture of diphenylmethanediisocyanate and a polymethylene polyphenylisocyanate having at least 2 isocyanate groups per molecule of monomer unit; the equivalent ratio of isocyanate to diol is from about 1:0.01 to about 1:0.35; and the equivalent ratio of epoxy to isocyanate to epoxy is from about 1:0.2 to 1:5.
Claim 3
Dependent Claim
30 words
A reaction resin mixture according to claim 1 wherein the isocyanate prepolymerisate is a reaction product of an alkylene diol and an isocyanate mixture of diphenylmethane-diisocyanate and a polymethylene polyphenylisocyanate.
Claim 4
Dependent Claim
30 words
A reaction resin mixture according to claim 1 wherein the isocyanate prepolymerisate is a reaction product of a polyoxyalkylene glycol and a isocyanate mixture of diphenylmethanediisocyanate and a polymethylene polyphenylisocyanate.
Claim 5
Dependent Claim
21 words
A reaction resin mixture according to claim 3 wherein the polyoxyalkylene glycol has an average mol mass of 100 to 1000.
Claim 6
Dependent Claim
17 words
A reaction resin mixture according to claim 4 wherein the average mole mass is 200 to 800.
Claim 7
Dependent Claim
21 words
A reaction resin mixture according to claim 1 wherein the isocyanate mixture contains up to 35% by weight of a polymethylenepolyphenylisocyanate.
Claim 8
Dependent Claim
17 words
A reaction resin mixture according to claim 1 wherein the reaction accelerator is a latent reaction accelerator.
Claim 9
Dependent Claim
29 words
A reaction resin mixture according to claim 1 wherein the reaction accelerator content is 0.01 to 5% percent by weight relative to the weight of the reaction resin mixture.
Claim 10
Dependent Claim
19 words
A reaction resin mixture according to claim 8 wherein the reaction accelerator content is 0.25 to 2.5% by weight.
Claim 11
Dependent Claim
23 words
A reaction resin mixture according to claim 1 wherein the mixture contains quartz powder, fused silica, aluminum oxide or dolomite as a filler.
Claim 12
Dependent Claim
23 words
A reaction resin mixture according to claim 1 wherein the equivalent ratio of isocyanate to diol is from about 1:0.05 to about 1:0.2.
Claim 13
Dependent Claim
39 words
A thermal molded material suitable for embedding electric components, which comprises: the thermal reaction product produced from the reaction resin mixture of claim 1 by heating said mixture at a temperature from about room temperature to about 200° C.
Claim 14
Dependent Claim
50 words
A method of manufacturing a reaction resin molded material for an electrical component, which comprises the steps of: embedding the component with a reaction resin mixture according to claim 1, and hardening the mixture embedding the component by heating it at a temperature from room temperature to about 200° C.
Claim 15
Dependent Claim
50 words
A method of manufacturing a reaction resin molded material for an electrical winding, which comprises the steps of: impregnating the winding with a reaction resin mixture according to claim 1, and hardening the mixture impregnating the winding by heating it at a temperature from room temprature to about 200° C.
Claim 16
Dependent Claim
56 words
A method of manufacturing a reaction resin molded material insulating component, which comprises the steps of: injecting a reaction resin mixture according to claim 1 into a mold having the shape of the component and hardening the mixture contained in the mold by heating it to a temperature of from room temperature to about 200° C.
References Cited (Backward Citations)
US3198851A
Cited
US3394164A
Cited
US4070416A
Cited
US4100118A
Cited
US4055548A
Cited
US4220731A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-30 | 1989-07-01 | 1989-12-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-30 | 1993-07-01 | 1993-12-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-30 | 1997-07-01 | 1997-12-31 | $7700.00 | Window Closed / Lapsed |