High strength glass-ceramic containing apatite and alkaline earth metal silicate crystals and process for producing the same

Claim 2

A high strength glass-ceramic having a bending strength from at least 1500 kg/cm 2 and containing apatite crystals and at least one alkaline earth metal silicate crystal selected from the group consisting of diopside, forsterite and akermanite and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 , 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0 to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 .

Claim 3

A process for producing a high strength glass-ceramic containing apatite crystals and at least one alkaline earth metal silicate crystal, which process comprises molding glass powders having a particle size of 200 mesh or less and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 , 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 , heat treating the resulting molding in a sintering temperature range of the glass powders, and heat treating the molding in the temperature range where alkaline earth metal silicate crystals selected from the group consisting of diopside, forsterite and akermanite are formed.

Claim 4

A process for producing a high strength glass-ceramic containing apatite crystals and at least one alkaline earth metal silicate crystal, which process comprises molding glass powders having a particle size of 200 mesh or less and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 , 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 , heat treating the resulting molding in a sintering temperature range of the glass powders, and heat treating the molding in the temperature range where alkaline earth metal silicate crystals selected from the group consisting of diopside, forsterite and akermanite are formed.

Claim 5

A high strength glass-ceramic having a bending strength from at least 1500 kg/cm 2 and containing apatite crystals and at least one alkaline earth metal silicate crystal selected from the group consisting of diopside, forsterite and akermanite and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; 1 to 10% Al 2 O 3 , ZrO 2 or both with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 +(Al 2 O 3 +ZrO 2 ), 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0 to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 .

Claim 6

A high strength glass-ceramic having a bending strength from at least 1500 kg/cm 2 and containing apatite crystals and at least one alkaline earth metal silicate crystal selected from the group consisting of diopside, forsterite and akermanite and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; 1 to 10% Al 2 O 3 , ZrO 2 or both with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 +(Al 2 O 3 +ZrO 2 ), 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0 to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 .

Claim 7

A process for producing a high strength glass-ceramic containing apatite crystals and at least one alkaline earth metal silicate crystal, which process comprises (1) molding glass powders having a particle size of 200 mesh or less and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; 1 to 10% Al 2 O 3 , ZrO 2 or both with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 +(Al 2 O 3 +ZrO 2 ), 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0 to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 , (2) heat treating the resulting molding in a sintering temperature range of the glass powders, and (3) heat treating the molding in the temperature range where alkaline earth metal silicate crystals selected from the group consisting of diopside, forsterite and akermanite are formed.

Claim 8

A process for producing a high strength glass-ceramic containing apatite crystals and at least one alkaline earth metal silicate crystal, which process comprises (1) molding glass powders having a particle size of 200 mesh or less and having a composition consisting essentially of, in % by weight, 8 to 34% MgO; 12 to 43% CaO; 25 to 40% SiO 2 ; 10 to 25% P 2 O 5 ; 1 to 10% Al 2 O 3 , ZrO 2 or both with proviso of 90% or more MgO+CaO+SiO+P 2 O 5 +(Al 2 O 3 +ZrO 2 ), 0 to 10% Li 2 O; 0 to 5% Na 2 O; 0 to 10% K 2 O; 0 to 10% SrO; 0 to 10% B 2 O 3 ; 0 to 10% TiO 2 ; 0 to 10% Nb 2 O 5 ; 0 to 10% Ta 2 O 5 ; and 0 to 3% F 2 , with proviso of 10% or less Li 2 O+Na 2 O+K 2 O+SrO+B 2 O 3 +TiO 2 +Nb 2 O 5 +Ta 2 O 5 +F 2 , (2) heat treating the resulting molding in a sintering temperature range of the glass powders, and (3) heat treating the molding in the temperature range where alkaline earth metal silicate crystals selected from the group consisting of diopside, forsterite and akermanite are formed.