Abstract The invention provides a method for providing a highly protective coating layer of silicon carbide on to the surface of a substrate. The method comprises pyrolyzing the vapor of an organosilicon compound having at least one hydrogen atom directly bonded to the silicon atom in a molecule but having no halogen or oxygen atom directly bonded to the silicon atom at a temperature of 700° to 1400° C. in contact with the substrate surface to deposit silicon carbide thereon. In particular, the method is useful to form a sheath-and-core structure composed of the core of carbon filament and the coating layer of silicon carbide so that the carbon fibers are imparted with greatly improved resistance against oxidation and chemicals including molten metals when the carbon fibers are used as a reinforcing material of a fiber-reinforced metal composite as well as with improved affinity with molten resins and metals which is also an advantageous property as a reinforcing material for such matrix materials.
A method for providing a coating layer of silicon carbide on the surface of a filament of carbon in a sheath-and-core manner which comprises pyrolyzing the vapor of a vaporizable organosilicon compound having at least one hydrogen atom directly bonded to the silicon atom in a molecule but having no halogen atom or oxygen atom directly bonded to the silicon atom at a temperature in the range from 700° to 1400° C. in contact with the surface of the carbon filament to deposit silicon carbide thereon, wherein the organosilicon compound is a silane or polysilane compound represented by the general formula R 2n+2 Si n , in which R is a hydrogen atom or a monovalent hydrocarbon group, at least one but not all of the groups denoted by R in a molecule being a hydrogen atom, and n is a positive integer of 1 to 4 inclusive.
Claim 2
Independent Claim
148 words
A method for providing a coating layer of silicon carbide on the surface of a filament of carbon in a sheath-and-core manner which comprises pyrolyzing the vapor of a vaporizable organosilicon compound having at least one hydrogen atom directly bonded to the silicon atom in a molecule but having no halogen atom or oxygen atom directly bonded to the silicon atom at a temperature in the range from 700° to 1400° C. in contact with the surface of the carbon filament to deposit silicon carbide thereon, wherein the organosilicon compound is a silane or polysilane compound represented by the general formula R 2n+2 Si n , in which R is a hydrogen atom or a monovalent hydrocarbon group, at least one but not all of the groups denoted by R in a molecule being a hydrogen atom, and n is a positive integer of 1 to 4 inclusive.
Claim 3
Dependent Claim
28 words
The method as claimed in claim 1 wherein the temperature at which pyrolysis of the organosilicon compound is performed is in the range from 900° to 1200° C.
Claim 4
Dependent Claim
58 words
The method as claimed in claim 1 wherein the vapor of the organosilicon compound is admixed with the vapor of a hydrocarbon compound in such an amount that the product of the pyrolysis of the mixed vapor is composed of silicon carbide and carbon, the amount of carbon being not exceeding equimolar to that of the silicon carbide.