Process of deburring moldings made from granular material

Claim 2

A process for deburring fragile moldings made of granular material comprising the steps of adding hard-foam bodies to abrasive bodies to form a mixture defining an abrasive body medium having a proportion of the hard-foam bodies in the abrasive body medium of more than 50%, deburring the moldings by abrasive action by vibration and circulation of the moldings with the abrasive body medium along a helical path within an abrasive finishing vibrator machine by vibrating the machine, said hard-foam bodies have a density substantially lower than that of the abrasive bodies, and have such a degree of hardness that an impression can be made on the hard-foam bodies by a person's fingernail, and wherein during the deburring step, the hard-foam bodies cushion the moldings.

Claim 3

The process according to claim 1, wherein said hard-foam bodies are small cylindrical rods.

Claim 4

The process according to claim 1, further comprising the step of adding coating material into the abrasive body medium, the moldings being completely coated with the coating material during the deburring step by the circulation and vibration.

Claim 5

The process according to claim 3, wherein said coating material is powdered to which a binder has been added.

Claim 6

The process according to claim 3, the abrasive body medium includes aluminum pins.

Claim 7

The process according to claim 5, wherein the portion of aluminum pins in said abrasive body medium is about 15%.

Claim 8

The process according to claim 13, wherein the dressing agent is selected from the group consisting of one of ground feldspar and mica.

Claim 9

The process according to claim 1, further comprising the step of adding moisture by continuous dosed addition to the abrasive body medium.

Claim 10

The process according to claim 1, wherein said moldings are selected from the group consisting of sand cores and bonded moldings.

Claim 11

The process according to claim 9, wherein said bonded moldings are made of porcelain.

Claim 12

The process according to claim 2, wherein the cylindrical rods have end surfaces extending obliquely to their longitudinal axes.

Claim 13

A process for deburring fragile moldings made of granular material comprising the steps of adding hard-foam bodies to abrasive bodies to form a mixture defining an abrasive body medium having a proportion of the hard-foam bodies in the abrasive body medium of more than 50%, deburring the moldings by abrasive action by vibration and circulation of the moldings with the abrasive body medium along a helical path within an abrasive finishing vibrator machine by vibrating the machine, adding coating material into the abrasive body medium, the moldings being completely coated with the coating material during the deburring steps by the circulation and vibration, the abrasive body medium includes the abrasive bodies, aluminum pins, and the hard-foam bodies, the latter being made of polyproplylene, said hard-foam bodies are small cylindrical rods and have a size which is comparable to that of the abrasive bodies, and the size of the aluminum pins is only a fraction of the size of said hard-foam bodies.

Claim 14

A process for deburring fragile moldings made of granular material comprising the steps of adding hard-foam bodies to abrasive bodies to form a mixture defining an abrasive body medium having a proportion of the hard-foam bodies in the abrasive body medium of more than 50%, deburring the moldings by abrasive action by vibration and circulation of the moldings with the abrasive body medium along a helical path within an abrasive finishing vibrator machine by vibrating the machine, adding coating material into the abrasive body medium, the moldings being completely coated with the coating material during the deburring steps by the circulation and vibration, the abrasive body medium includes the abrasive bodies, aluminum pins, and the hard-foam bodies, the latter being made of polyproplylene, said hard-foam bodies are small cylindrical rods and have a size which is comparable to that of the abrasive bodies, and the size of the aluminum pins is only a fraction of the size of said hard-foam bodies.

Claim 15

The process according to claim 12, wherein said abrasive bodies, said hard-foam bodies and said aluminum pins are in the respective proportions of 30%, 55% and 15%, and said coating material is a dressing agent constituting about 10% of the volume of the abrasive grinding medium.

Claim 16

The process according to claim 1, wherein the abrasive bodies are conical.

Claim 17

The process according to claim 13, wherein the dressing agent is powdered, and a binder is added.

Claim 18

The process according to claim 13, wherein the dressing agent is powdered, and a binder is added comprising a fat-containing material.

Claim 19

The process according to claim 16, wherein said powdered dressing agent is selected from the group consisting of one of graphite and talcum.

Claim 20

The process according to claim 16, wherein said moldings are castings and said powdered dressing agent is aluminum silicate admixed with about 10% pulverized stearate.

Claim 21

The process according to claim 16, wherein the binder of fat-containing material is added as a liquid to the dressing agent.

Claim 22

The process according to claim 19, wherein said liquid is oil.

Claim 23

The process according to claim 16, wherein the fat-containing material is added in the form of a pasty substance to the dressing agent.

Claim 24

The process according to claim 21, wherein said pasty substance is wax.

Claim 25

A composition abrasive body medium in an abrasive finishing vibrator machine, comprising polypropylene hard-foam bodies in an amount about 50% added to a vibrator abrasive body medium.

Claim 26

A composition abrasive body medium in an abrasive finishing vibrator machine, comprising polypropylene hard-foam bodies in an amount about 50% added to a vibrator abrasive body medium.