Curable epoxy resins
Assignee: Cytec Technology Corp
•
Filing: 1984-07-31
•
Granted: 1985-12-17
•
Expires: 2004-07-31
Abstract
Abstract A curable composition consisting of A. 100 parts by weight of an epoxy resin, B. from 4 to 100 parts by weight of a conventional curing agent for epoxy resins, and C. from 0.1 to 5 parts by weight of an N-acylimidazole which possesses an aromatic acyl component which is substituted at the two positions ortho to the carbonyl group can be used to produce moldings, coatings, finishes, adhesives and composite fiber materials.
Inventors
- 👤 Helmut Tesch
- 👤 Andreas Henne
- 👤 Manfred Heym
- 👤 Herbert Stutz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:17
CPC Classifications
C; C07; C07D; C07D231/00; C07D231/02; C07D231/10; C07D231/12; C07D233/00; C07D233/54; C07D233/56; C07D249/00; C07D249/02; C07D249/08; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08G59/686; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3442; C08K5/3445
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
190 words
A curable resin composition containing A. 100 parts by weight of an epoxy resin, B. from 4 to 100 parts by weight of a conventional curing agent for epoxy resins, and C. from 0.1 to 5 parts by weight of a N-acylimidazole as an accelerator, wherein component C is an N-acylimidazole of the formula ##STR1## where R 1 , R 2 and R 3 can be identical or different and are each hydrogen, branched or straight-chain alkyl of 1 to 17 carbon atoms, chlorine, or phenyl which is unsubstituted or substituted by alkyl, alkoxy or chlorine, or are each haloalkyl, hydroxyalkyl, a carboxylic ester group or a carboxamide group, R 4 and R 5 can be identical or different and are each a branched or straight-chain alkyl, alkoxy or alkylthio group of 1 to 4 carbon atoms, R 6 is hydrogen, an alkoxy or alkylthio group of 1 to 6 carbon atoms, dialkylamino where alkyl is of 1 to 6 carbon atoms or branched or straight-chain alkyl of 1 to 12 carbon atoms, n is 1, 2 or 3 and R 7 is alkyl of 1 to 4 carbon atoms.
Claim 2
Dependent Claim
190 words
A curable resin composition containing A. 100 parts by weight of an epoxy resin, B. from 4 to 100 parts by weight of a conventional curing agent for epoxy resins, and C. from 0.1 to 5 parts by weight of a N-acylimidazole as an accelerator, wherein component C is an N-acylimidazole of the formula ##STR1## where R 1 , R 2 and R 3 can be identical or different and are each hydrogen, branched or straight-chain alkyl of 1 to 17 carbon atoms, chlorine, or phenyl which is unsubstituted or substituted by alkyl, alkoxy or chlorine, or are each haloalkyl, hydroxyalkyl, a carboxylic ester group or a carboxamide group, R 4 and R 5 can be identical or different and are each a branched or straight-chain alkyl, alkoxy or alkylthio group of 1 to 4 carbon atoms, R 6 is hydrogen, an alkoxy or alkylthio group of 1 to 6 carbon atoms, dialkylamino where alkyl is of 1 to 6 carbon atoms or branched or straight-chain alkyl of 1 to 12 carbon atoms, n is 1, 2 or 3 and R 7 is alkyl of 1 to 4 carbon atoms.
Claim 3
Dependent Claim
54 words
A curable composition as claimed in claim 1, which contains A. 100 parts by weight of bisphenol A diglycidyl ether as an epoxy resin B. from 4 to 10 parts by weight of dicyanodiamide as a curing agent for the epoxy resin, and C. from 0.2 to 2 parts by weight of an N-acylimidazole.
Claim 4
Dependent Claim
31 words
A process for the production of a molding by introducing a curable composition as claimed in claim 1 into a mold, and carrying out curing at from 50° to 300° C.
Claim 5
Dependent Claim
36 words
A process for the production of a finish, a coating or an adhesive by applying a curable composition as claimed in claim 1 onto a substrate, and carrying out curing at from 50° to 300° C.
Claim 6
Dependent Claim
47 words
A process for the production of a composite fiber material by impregnating from 30 to 70 vol. % of reinforcing fibers with from 70 to 30 vol. % of a curable composition as claimed in claim 1, and carrying out curing at from 50° to 300° C.
Claim 7
Dependent Claim
25 words
A curable resin composition as set forth in claim 1, wherein R 4 and R 5 are each alkyl of 1 to 4 carbon atoms.
Claim 8
Dependent Claim
19 words
A curable resin composition as set forth in claim 1, wherein R 4 and R 5 are each methyl.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-16 | 1989-06-17 | 1989-12-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-16 | 1993-06-17 | 1993-12-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-16 | 1997-06-17 | 1997-12-17 | $7700.00 | Window Closed / Lapsed |