US4555437A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Transparent ink jet recording medium
Assignee: Xidex Corp
•
Filing: 1984-07-16
•
Granted: 1985-11-26
•
Expires: 2004-07-16
Abstract
Abstract A transparent recording medium comprised of a conventional transparency base material coated with hydroxyethylcellulose and optionally containing one or more additional polymers compatible therewith demonstrates unusually favorable properties for color ink jet recording by producing a clear transparent medium on which the ink dries rapidly to produce sharp images with minimal lateral bleed.
Inventors
- 👤 Elinor J. Tanck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:51
CPC Classifications
B; B41; B41M; B41M5/00; B41M5/50; B41M5/52; B41M5/5236; B41M5/5254; B41M5/529; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504; Y10T428/31786; Y10T428/3179; Y10T428/31855; Y10T428/3188; Y10T428/31884; Y10T428/31971
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
18 words
A transparent recording sheet comprising a transparent base support coated with a transparent ink-receiving layer comprising a hydroxyethylcellulose.
Claim 2
Dependent Claim
18 words
A transparent recording sheet comprising a transparent base support coated with a transparent ink-receiving layer comprising a hydroxyethylcellulose.
Claim 3
Dependent Claim
38 words
A transparent recording sheet according to claim 1 in which said hydroxyethylcellulose has a viscosity of from about 20 to about 2000 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer.
Claim 4
Dependent Claim
49 words
A transparent recording sheet according to claim 1 in which said hydroxyethylcellulose has a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0.
Claim 5
Dependent Claim
35 words
A transparent recording sheet according to claim 1 in which said base support is a heat-stable biaxially oriented polyethylene terephthalate and the thickness of said ink-receiving layer is from about 50 to about 1000 microinches.
Claim 6
Dependent Claim
30 words
A transparent recording sheet according to claim 1 in which said ink-receiving layer further comprises at least one member selected from the group consisting of a polyacrylamide and a polyvinylpyrrolidone.
Claim 7
Dependent Claim
43 words
A transparent recording sheet according to claim 1 in which said ink-receiving layer further comprises from about 1% to about 25% by weight of a polyacrylamide at most slightly anionic in character with an average molecular weight of less than about three million.
Claim 8
Dependent Claim
46 words
A transparent recording sheet according to claim 1 in which said ink-receiving layer further comprises from about 3% to about 15% by weight of a polyacrylamide ranging from substantially non-ionic to slightly anionic in character with an average molecular weight of less than about two million.
Claim 9
Dependent Claim
38 words
A transparent recording sheet according to claim 1 in which said ink-receiving layer further comprises from about 2% to about 70% by weight of a polyvinylpyrrolidone with an average molecular weight of from about 10,000 to about 700,000.
Claim 10
Dependent Claim
38 words
A transparent recording sheet according to claim 1 in which said ink-receiving layer further comprises from about 10% to about 50% by weight of a polyvinylpyrrolidone with an average molecular weight of from about 100,000 to about 500,000.
Claim 11
Dependent Claim
74 words
A transparent recording sheet comprising (a) a transparent base support comprising a heat-stable biaxially oriented polyethylene terephthalate and (b) a transparent ink-receiving layer having a thickness of from about 250 to about 750 microinches and comprising hydroxyethylcellulose having a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0.
Claim 12
Dependent Claim
74 words
A transparent recording sheet comprising (a) a transparent base support comprising a heat-stable biaxially oriented polyethylene terephthalate and (b) a transparent ink-receiving layer having a thickness of from about 250 to about 750 microinches and comprising hydroxyethylcellulose having a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0.
Claim 13
Dependent Claim
117 words
A transparent recording sheet comprising: (a) a transparent base support comprising a heat-stable biaxially oriented polyethylene terephthalate; and (b) a transparent ink-receiving layer adherent to said base support, said layer having a thickness of from about 250 to about 750 microinches and comprising (i) hydroxyethylcellulose having a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0, and (ii) from about 3% to about 15% by weight of said layer of a polyacrylamide which is at most slightly anionic in character with an average molecular weight of less than about two million.
Claim 14
Dependent Claim
117 words
A transparent recording sheet comprising: (a) a transparent base support comprising a heat-stable biaxially oriented polyethylene terephthalate; and (b) a transparent ink-receiving layer adherent to said base support, said layer having a thickness of from about 250 to about 750 microinches and comprising (i) hydroxyethylcellulose having a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0, and (ii) from about 3% to about 15% by weight of said layer of a polyacrylamide which is at most slightly anionic in character with an average molecular weight of less than about two million.
Claim 15
Independent Claim
44 words
A method for the preparation of a transparent recording sheet comprising: (a) applying to a transparent base support a layer of an aqueous solution of a hydroxyethylcellulose; and (b) evaporating water from said layer to provide a dry substantially uniform transparent layer of hydroxyethylcellulose.
Claim 16
Independent Claim
44 words
A method for the preparation of a transparent recording sheet comprising: (a) applying to a transparent base support a layer of an aqueous solution of a hydroxyethylcellulose; and (b) evaporating water from said layer to provide a dry substantially uniform transparent layer of hydroxyethylcellulose.
Claim 17
Dependent Claim
55 words
A method according to claim 12 in which the concentration of said hydroxyethylcellulose in said aqueous solution is from about 1% to about 30% by weight, and said hydroxyethylcellulose has a viscosity of from about 20 to about 2000 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer.
Claim 18
Dependent Claim
24 words
A method according to claim 12 in which the thickness of the layer of step (b) is from about 50 to about 1000 microinches.
Claim 19
Dependent Claim
82 words
A method according to claim 12 in which the concentration of said hydroxyethylcellulose in said aqueous solution is from about 5% to about 15% by weight, said hydroxyethylcellulose has a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0, and the thickness of the layer of step (b) is from about 250 to about 750 microinches.
Claim 20
Dependent Claim
31 words
A method according to claim 12 in which said aqeous solution of step (a) further contains at least one member selected from the group consisting of a polyacrylamide and a polyvinylpyrrolidone.
Claim 21
Dependent Claim
52 words
A method according to claim 12 in which said aqueous solution of step (a) further contains from about 1% to about 25% by weight, based on total dissolved solids, of a polyacrylamide ranging from substantially non-ionic to slightly anionic in character with an average molecular weight of less than about three million.
Claim 22
Dependent Claim
39 words
A method according to claim 12 in which said aqueous solution of step (a) further contains from about 2% to about 70% by weight of a polyvinylpyrrolidone with an average molecular weight of from about 10,000 to about 700,000.
Claim 23
Dependent Claim
116 words
A method according to claim 12 in which said base support of step (a) is a heat-stable biaxially oriented polyethylene terephthalate, said hydroxyethylcellulose has a viscosity of from about 50 to about 500 centipoise, measured as a 5 weight percent aqueous solution at 25° C. on a Brookfield viscometer, and a molar substitution of from about 1.5 to about 3.0, said aqueous solution further contains from about 3% to about 15%, based on total dissolved solids, of a polyacrylamide ranging from substantially non-ionic to slightly anionic in character with an average molecular weight of less than about two million, and the thickness of the layer of step (b) is from about 250 to about 750 microinches.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-25 | 1989-05-27 | 1989-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-25 | 1993-05-27 | 1993-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-25 | 1997-05-27 | 1997-11-26 | $7700.00 | Window Closed / Lapsed |