Star-shaped polymers for improved tire treads
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1985-01-30
•
Granted: 1985-11-19
•
Expires: 2005-01-30
Abstract
Abstract A tire having a tread exhibiting substantial low rolling resistance, traction and wear comprises a cured compounded carbon black reinforced blend of (A) a star-shaped substantially random vinyl containing rubbery solution polymerized polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same and (B) at least one other rubbery diene polymer.
Inventors
- 👤 Francis J. Vitus
- 👤 Ivan G. Hargis
- 👤 Russell A. Livigni
- 👤 Sundar L. Aggarwal
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:00
CPC Classifications
C; C08; C08F; C08F236/00; C08F236/02; C08F236/04; C08F236/10; C08F297/00; C08F297/02; C08F297/04; C08F297/042; C08L; C08L21/00; C08L67/00; C08L67/06; Y; Y02; Y02T; Y02T10/00; Y02T10/80; Y02T10/86; Y10; Y10S; Y10S152/00; Y10S152/905; Y10S525/00; Y10S525/901; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31826; Y10T428/31855; Y10T428/31931
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
251 words
A tire having a tread of a compounded carbon black reinforced and vulcanized composition of a blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 2
Dependent Claim
251 words
A tire having a tread of a compounded carbon black reinforced and vulcanized composition of a blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 3
Dependent Claim
17 words
A tire according to claim 1 where (A) is a butadiene-styrene copolymer and (B) is natural rubber.
Claim 4
Dependent Claim
240 words
A vulcanizable composition comprising a blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 5
Dependent Claim
240 words
A vulcanizable composition comprising a blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 6
Dependent Claim
17 words
A composition according to claim 3 where (A) is a butadiene-styrene copolymer and (B) is natural rubber.
Claim 7
Dependent Claim
241 words
A vulcanized compounded carbon black reinforced blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 8
Dependent Claim
241 words
A vulcanized compounded carbon black reinforced blend of (A) from about 40 to 60% by weight of a solution polymerized rubbery substantially random star-shaped polymer and (B) from 60 to 40% by weight of at least one rubbery polymer selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene rubber, cis-1,4-polybutadiene rubber, high trans-1,4-polybutadiene rubber and high trans-1,4-butadiene-styrene rubbery copolymer, (A) being at least one polymer selected from the group consisting of polybutadienes, polyisoprenes, butadiene-styrene copolymers, butadiene-isoprene copolymers, isoprene-styrene copolymers, butadiene-isoprene-styrene copolymers and mixtures of the same, said styrene containing copolymers containing up to about 30 weight % of styrene, preferably from about 10 to 25 weight % of styrene, having a vinyl content for the diene segments of from about 12 to 60 weight %, having an average of from about 4 to 9 arms, having a Mn of from about 100,000 to 500,000, and having a nucleus from an initiator (1) having a VPO Mn of from about 750 to 4,000, (2) having an average of from about 4 to 9 C-Li sites and (3) being the adduct of an aromatic compound selected from the group consisting of divinyl benzene and diisopropenyl benzene and mixtures thereof and RLi where R is selected from the group consisting of normal, secondary and tertiary alkyl and cycloalkyl radicals of from 2 to 20, or from 2 to 10, carbon atoms, the mold ratio of RLi to said aromatic compound being about 1:0.83.
Claim 9
Dependent Claim
17 words
A blend according to claim 5 where (A) is a butadiene-styrene copolymer and (B) is natural rubber.
References Cited (Backward Citations)
US3644322A
Cited
US3652516A
Cited
US3763126A
Cited
US3734972A
Cited
US3734973A
Cited
US3903168A
Cited
DE2427955A1
Cited
CA1034133A
Cited
US3985830A
Cited
US3985830B1
Cited
US4116917A
Cited
US4397994A
Cited
US4417027A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-18 | 1989-05-20 | 1989-11-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-18 | 1993-05-20 | 1993-11-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-18 | 1997-05-20 | 1997-11-19 | $7700.00 | Window Closed / Lapsed |