Process of end-capping a polyimide system

Assignee: National Aeronautics and Space Administration
•
Filing: 1984-09-11
•
Granted: 1985-11-12
•
Expires: 2004-09-11
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process of endcapping a polyimide system with an endcapping agent in order to achieve a controlled decrease in molecular weight and melt viscosity along with predictable fracture resistance of the molded products is disclosed. The uncapped system is formed by combining an equimolar ratio of 4,4'-bis(3,4-dicarboxyphenoxy) diphenylsulfide dianhydride (BDSDA) and 1,3-bis(aminophenoxy)benzene (APB) dissolved in bis(2-methoxyethyl)ether. The endcapped system is formed by dissolving APB in bis-(2-methoxyethyl)ether, adding the endcapping agent, and then adding the BDSDA. By varying the amount of endcapping from 0 to 4%, molecular weight is decreased from 13,900 to 8660. At a processing temperature of 250 DEG C., there is a linear relationship between molecular weight and viscosity, with the viscosity decreasing by two orders of magnitude as the molecular weight decreased from 13,900 to 8660. A greater drop in viscosity is noted at higher temperatures. Apparent viscosity as a function of molecular weight at 250 DEG C. and at 280 DEG C. is depicted in FIG. 2. Reducing the molecular weight also results in a linear decrease in the fracture resistance from 4100 J/m2 to 296 J/m2, as shown in FIG. 1.

Inventors

  • 👤 Terry L. St. Clair
  • 👤 Harold D. Burks

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-05 17:47
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1057; C08G73/1064; C08G73/1003; C08G73/1007; C08G73/101; C08G73/1014; C08G73/1017; C08G73/1067; C08G73/1071

Claims Analysis

Total Claims: 8
Claim 1
Independent Claim 82 words
A process of endcapping a polyimide system having the uncapped chemical structure of ##STR5## where n=5-100 comprising reacting an endcapping agent with the uncapped polyimide system for a controlled period of time and wherein the endcapping agent is selected from the group consisting of: ##STR6## where R is any alkyl moiety, ##STR7## where Ar is any aryl moiety, a monofunctional amine of the general type R--NH 2 where R is any alkyl moiety, and Ar--NH 2 where Ar is any aryl moiety.
Claim 2
Dependent Claim 82 words
A process of endcapping a polyimide system having the uncapped chemical structure of ##STR5## where n=5-100 comprising reacting an endcapping agent with the uncapped polyimide system for a controlled period of time and wherein the endcapping agent is selected from the group consisting of: ##STR6## where R is any alkyl moiety, ##STR7## where Ar is any aryl moiety, a monofunctional amine of the general type R--NH 2 where R is any alkyl moiety, and Ar--NH 2 where Ar is any aryl moiety.
Claim 3
Dependent Claim 13 words
The process of claim 1 wherein the specific endcapping agent is phthalic anhydride.
Claim 4
Dependent Claim 49 words
The process of claim 1 wherein the endcapped system is formed by dissolving 1,3-bis-(aminophenoxy)benzene (APB) in bis(2-methoxyethyl)ether, adding the endcapping agent, stirring for 15 minutes, and then adding 4,4'-bis-(3,4 dicarboxyphenoxy)diphenylsulfide (BDSDA) and stirring for one hour to yield a resultant endcapped system having the formula of: ##STR8## where n=5-100.
Claim 5
Dependent Claim 34 words
The process of claim 1 wherein the molecular weight is lowered from 13,900 to 8660, with a concomitant decrease in melt viscosity, by endcapping the system with varying amounts of phthalic anhydride from 1-4%.
Claim 6
Dependent Claim 49 words
The process of claim 4 wherein there is a linear relationship between molecular weight and apparent viscosity with the 13,900 system having a viscosity of about 10 6 Pa-sec and the 8660 system with a viscosity of less than 10 4 Pa-sec at a processing temperature of 250° C.
Claim 7
Dependent Claim 30 words
The process of claim 5 wherein there is a greater drop in viscosity at temperatures above 250° C.; at 280° C., the loss is more than three orders of magnitude.
Claim 8
Dependent Claim 53 words
The process of claim 4 wherein an increase in endcapping from 1-4%, while decreasing molecular weight from 13,900 to 8660, also results in a linear decrease in fracture resistance from 4100 J/m 2 to 296 J/m 2 thus permitting maximization of flow characteristics for a molecular weight material with the desired fracture resistance.

References Cited (Backward Citations)

US3234181A Cited
US3179632A Cited
US3179630A Cited
US3998786A Cited
US3943107A Cited
US4417044A Cited
US4429102A Cited
US4443591A Cited
US4444979A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1988-11-11 1989-05-13 1989-11-12 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1992-11-11 1993-05-13 1993-11-12 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1996-11-11 1997-05-13 1997-11-12 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag