Method for making polyetherimide

Claim 2

A process for the continuous polymerization of polyetherimide which comprises (1) dry-blending aromatic bis(ether anhydride) and organic diamine, (2) feeding the resulting solids into an extruder, (3) conveying the solids to a melting stage in the extruder, where they are kneaded and melted via viscous heating at a temperature in the range of from about 50° C. to about 300° C. resulting in the production of a liquid pool, (4) conveying the liquid of (3) to a mass transfer stage where water of reaction is vented to the atmosphere at temperatures of from 200° C. to 350° C., (5) conveying the resulting melt from the mass transfer stage of (4) to an advanced polymerization stage where the melt is further subjected to higher shear and intensive mixing at a temperature in the range of from 300° C. to 400° C. while being subjected to pressures of 1 atmospheres to 25 atmospheres, and (6) and thereafter separating from the extruder polyetherimide and additional water of reaction.

Claim 3

A process in accordance with claim 1, where the polyetherimide has an intrinsic viscosity in chloroform of at least 0.4.

Claim 4

A process in accordance with claim 1, where the polyetherimide consists essentially of chemically combined units of the formula ##STR11## where R is a member selected from ##STR12## and divalent organic radicals of the general formula, ##STR13## X is a member selected from the class consisting of divalent radicals of the formula, ##STR14## y is an integer from 1 to 5; and R 1 is a divalent organic radical selected from the class consisting of aromatic hydrocarbon radicals having from 6 to about 20 carbon atoms and halogenated derivatives thereof, alkylene radicals having from 2 to about 20 carbon atoms, cycloalkylene radicals having from 3 to about 20 carbon atoms, from C 2 to about C 8 alkylene terminated polydiorganosiloxanes and divalent radicals of the general formula, ##STR15## Q is a member selected from the class consisting of --O--, --S--, C.sub.x H.sub.2 x, x is an integer from 1 to 5 and n is 0 or 1.

Claim 5

A method in accordance with claim 1, where the aromatic bis(ether anhydride) has the formula, ##STR16## where R is a member selected from ##STR17## and divalent organic radicals of the general formula, ##STR18## X is a member selected from the class consisting of divalent radicals of the formula, ##STR19## and y is an integer from 1 to 5.

Claim 6

A method in accordance with claim 1, where the aromatic bis(ether anhydride) is a mixture of ##STR20## and up to 30 mole percent of benzophenone dianhydride, where R is a member selected from ##STR21## and divalent organic radicals of the general formula, ##STR22## X is a member selected from the class consisting of divalent radicals of the formula, ##STR23## and y is an integer from 1 to 5.

Claim 7

A method in accordance with claim 1, where the organic diamine has the formula, H.sub.2 N--R.sup.1 --NH.sub.2, where R 1 is a divalent organic radical selected from the class consisting of aromtic hydrocarbon radicals haviang from 6 to about 20 carbon atoms and halogenated derivatives thereof, alkylene radicals having from 2 to about 20 carbon atoms, cycloalkylene radicals having from 3 to about 20 carbon atoms, from C 2 to about C 8 alkylene terminated polydiorganosiloxanes and divalent radicals of the general formula, ##STR24## Q is a member selected from the class consisting of --O--, --S--, C.sub.x H.sub.2 x, x is an integer from 1 to 5 and n is 0 or 1.

Claim 8

A method in accordance with claim 1, where there is utilized an effective amount of a chain stopper.

Claim 9

A process for the continuous, steady state polymerization of polyetherimides consisting essentially of chemically combined units of the formula, ##STR25## (1) dry-blending aromatic bis(ether anhydride) of the formula, ##STR26## and the organic diamine has the formula, H.sub.2 N--R.sup.1 --NH.sub.2, (2) continuously introducing the dry-blended solids of (1) to an extruder, (3) continuously conveying the blended solids to a melting stage in the extruder, where they are rapidly converted to a liquid as a result of being subjected to kneading conditions at a temperature in the range of from about 50° C. to about 300° C., (4) continuously conveying the liquid of (3) to a first extruder mass transfer stage to effect separation of water of reaction resulting in polyetherimide formation based on the intercondensation of the aromatic bis(ether anhydride) and organic diamine, (5) continuously conveying the viscous polyetherimide product of reaction from the first mass transfer stage of (4) to a mixing stage where the intercondensation product of reaction is subjected to high shear at a temperature in the range of from about 250° C. to 350° C. and elevated pressures to further polymerize the polyetherimide, (6) conveying said further polymerized polyetherimide to a second mass transfer stage where further melt pool acceleration, polymerization, and evacuation of water of reaction are accomplished, (7) conveying said further polymerized polyetherimide from said second mass transfer stage to an advanced polymerization stage where complete polymerization of said polyetherimide is accomplished with extended residence time, and (8) removing a high polymer polyetherimide from said advanced polymerization stage with removal of final water of reaction, where R is a member selected from ##STR27## and divalent organic radicals of the general formula, ##STR28## X is a member selected from the class consisting of divalent radicals of the formula, ##STR29## y is an integer from 1 to 5; and R 1 is a divalent organic radical selected from the class consisting of aromatic hydrocarbon radicals having from 6 to about 20 carbon atoms and halogenated derivatives thereof, alkylene radicals having from 2 to about 20 carbon atoms, cycloalkylene radicals having from 3 to about 20 carbon atoms, from C 2 to about C 8 alkylene terminated polydiorganosiloxanes and divalent radicals of the general formula, ##STR30## Q is a member selected from the class consisting of --O--, --S--, C.sub.x H.sub.2 x, x is an integer from 1 to 5 and n is 0 or 1.

Claim 10

A process for the continuous, steady state polymerization of polyetherimides consisting essentially of chemically combined units of the formula, ##STR25## (1) dry-blending aromatic bis(ether anhydride) of the formula, ##STR26## and the organic diamine has the formula, H.sub.2 N--R.sup.1 --NH.sub.2, (2) continuously introducing the dry-blended solids of (1) to an extruder, (3) continuously conveying the blended solids to a melting stage in the extruder, where they are rapidly converted to a liquid as a result of being subjected to kneading conditions at a temperature in the range of from about 50° C. to about 300° C., (4) continuously conveying the liquid of (3) to a first extruder mass transfer stage to effect separation of water of reaction resulting in polyetherimide formation based on the intercondensation of the aromatic bis(ether anhydride) and organic diamine, (5) continuously conveying the viscous polyetherimide product of reaction from the first mass transfer stage of (4) to a mixing stage where the intercondensation product of reaction is subjected to high shear at a temperature in the range of from about 250° C. to 350° C. and elevated pressures to further polymerize the polyetherimide, (6) conveying said further polymerized polyetherimide to a second mass transfer stage where further melt pool acceleration, polymerization, and evacuation of water of reaction are accomplished, (7) conveying said further polymerized polyetherimide from said second mass transfer stage to an advanced polymerization stage where complete polymerization of said polyetherimide is accomplished with extended residence time, and (8) removing a high polymer polyetherimide from said advanced polymerization stage with removal of final water of reaction, where R is a member selected from ##STR27## and divalent organic radicals of the general formula, ##STR28## X is a member selected from the class consisting of divalent radicals of the formula, ##STR29## y is an integer from 1 to 5; and R 1 is a divalent organic radical selected from the class consisting of aromatic hydrocarbon radicals having from 6 to about 20 carbon atoms and halogenated derivatives thereof, alkylene radicals having from 2 to about 20 carbon atoms, cycloalkylene radicals having from 3 to about 20 carbon atoms, from C 2 to about C 8 alkylene terminated polydiorganosiloxanes and divalent radicals of the general formula, ##STR30## Q is a member selected from the class consisting of --O--, --S--, C.sub.x H.sub.2 x, x is an integer from 1 to 5 and n is 0 or 1.

Claim 11

The process of claim 7 wherein from 40 to 60% of the water of reaction is removed in said first mass transfer stage, from 30 to 45% of said water of reaction is removed in said second mass transfer stage, and from 10 to 15% of said water of reaction is removed upon removal of the high polymer from said advanced polymerization stage.

Claim 12

The process of claim 7 wherein the elements in said melting stage of said extruder are kneading blocks and zero pumping blocks.

Claim 13

The process of claim 9 wherein the solids in said melting stage are raised to a temperature of from 50° to 100° C., melting of said solids is accomplished at from 200° to 300° C., and the liquid temperature is maintained at from 180° to 300° C., at a pressure of 1 to 5 atmospheres.

Claim 14

The process of claim 10 wherein the liquid temperature is maintained at from 225° to 275° C. and the pressure is maintained at from 1 to 2 atmospheres.

Claim 15

The process of claim 7 wherein the elements in said first mass transfer stage are open pitch, forward conveying elements.

Claim 16

The process of claim 13 wherein the temperature in said first mass transfer stage is maintained at from 180° to 400° C. at atmospheric pressure.

Claim 17

The process of claim 14 wherein the temperature is maintained at from 200° to 350° C.

Claim 18

The process of claim 8 wherein the elements in said mixing stage are zero and forward conveying kneadiang blocks.

Claim 19

The process of claim 16 wherein the temperature in said mixing stage is maintained at from 200° to 400° C. and the pressure is maintained at from 1 to 6 atmospheres.

Claim 20

The process of claim 17 wherein the temperature is maintained at from 200° to 350° C. and the pressure is maintained at from 1 to 3 atmospheres.

Claim 21

The process of claim 8 wherein the elements in said second mass transfer stage of said extruder are medium pitch, forward conveying elements.

Claim 22

The process of claim 19 wherein the temperature in said second mass transfer stage is maintained at from 250° to 400° C. and the pressure is essentially atmospheric.

Claim 23

The process of claim 20 wherein the temperature is frotm 300° to 350° C. and the pressure is maintained at from 1 to 6 atmospheres.

Claim 24

The process of claim 8 wherein the elements in said advanced polymerization stage of said extruder are tight pitch, forward conveying elements and said stage is provided with a restricted exit.

Claim 25

The process of claim 22 wherein the temperature in said advanced polymerization stage is maintained at from 300° to 400° C. and the pressure is maintained at from 1 to 50 atmospheres.

Claim 26

The process of claim 23 wherein the temperature is from 325° to 400° C. and the pressure is from 1 to 25 atmospheres.

Claim 27

The process of claim 1 wherein said extruder has two screws, said screws being co-rotating and intermeshing.