Abstract
Abstract A process for metal plating filled thermoplastic resins such as nylon-6. The filled resin surface to be plated is cleaned and rendered hydrophillic and preferably deglazed by a suitable solvent or acid. At least a portion of the filler in the surface is removed, preferably by a suitable acid. The treated surface is electroless plated to provide an electrically conductive metal deposit. Thereafter, the electroless plated surface is cleaned and thoroughly dried. The cleaned and dried electroless plated surface is then electroplated with at least one metallic layer to provide a desired wear resistant and/or decorative metallic surface.
Inventors
- 👤 Richard M. Stevenson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:34
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C25; C25D; C25D5/00; C25D5/54; C25D5/56; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381; H05K2203/00; H05K2203/07; H05K2203/0756; H05K2203/0773; Y; Y10; Y10S; Y10S205/00; Y10S205/917; Y10S205/924; Y10S205/926
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
253 words
A method of metal plating a surface of an article of a thermoplastic resin with a filler therein comprising the steps of; providing an article of at least one of a polyester and polyamide resin with a weight average molecular weight of at least about 10,000 and filled with about 5 to 60% by weight of at least one of metal, metal salt and mineral fillers, cleaning and making hydrophillic a surface of said article by contacting said surface with an alkaline cleaning solution and a surfactant prior to removing filler from said surface, removing at least a portion of the filler from said surface by contacting said surface with an organic or mineral acid having a normality of not greater than about 4.0 and which will dissolve at least a portion of said filler, after removing said filler electroless plating said surface from which filler has been removed to deposit thereon and adhere thereto an electrically conductive metallic layer of at least one of cobalt, nickel and copper, driving said electroless plated surface to remove essentially all moisture therefrom by heating to an elevated temperature of not more than about 190° F. for not more than 30 minutes, after drying said electroless plated surface electroplating such surface to deposit thereon and adhere thereto at least one metallic layer of at least one of copper and nickel, and thereafter electroplating such electroplated surface to deposit on and adhere to said layer at least one layer of at least one of nickel and chromium.
Claim 2
Independent Claim
253 words
A method of metal plating a surface of an article of a thermoplastic resin with a filler therein comprising the steps of; providing an article of at least one of a polyester and polyamide resin with a weight average molecular weight of at least about 10,000 and filled with about 5 to 60% by weight of at least one of metal, metal salt and mineral fillers, cleaning and making hydrophillic a surface of said article by contacting said surface with an alkaline cleaning solution and a surfactant prior to removing filler from said surface, removing at least a portion of the filler from said surface by contacting said surface with an organic or mineral acid having a normality of not greater than about 4.0 and which will dissolve at least a portion of said filler, after removing said filler electroless plating said surface from which filler has been removed to deposit thereon and adhere thereto an electrically conductive metallic layer of at least one of cobalt, nickel and copper, driving said electroless plated surface to remove essentially all moisture therefrom by heating to an elevated temperature of not more than about 190° F. for not more than 30 minutes, after drying said electroless plated surface electroplating such surface to deposit thereon and adhere thereto at least one metallic layer of at least one of copper and nickel, and thereafter electroplating such electroplated surface to deposit on and adhere to said layer at least one layer of at least one of nickel and chromium.
Claim 3
Dependent Claim
59 words
The method of claim 1 which also comprises the step of deglazing said surface after making it hydrophillic and before electroless plating thereof by contacting said surface with a diluted solution of at least one organic solvent of the group consisting essentially of acetone, butyrolactone, diacetylmethane, furfuryl alcohol, methyl ethylketone, n methyl pyrrolidone, 1,3 dioxolane, p-dioxane, and propylene carbonate.
Claim 4
Dependent Claim
38 words
The method of claim 2 which also comprises carrying out said deglazing step and said filler removal step at the same time by contacting said surface with said filler removal acid and said solvent at the same time.
Claim 5
Dependent Claim
52 words
The method of claim 1 which also comprises the step of deglazing said surface after marking it hydrophillic and before electroless plating thereof by contacting said surface with a diluted solution of at least one organic solvent of the group consisting essentially of chloroform, ethyl acetate, methylene chloride, methyl acetate and m-cresol.
Claim 6
Dependent Claim
48 words
The method of claim 1 which also comprises the step of deglazing said surface after making it hydrophillic and before electroless plating thereof by contacting said surface with at least one deglazing acid of the group consisting essentially of acetic, acetic anhydride, formic, propionic, and p-toluene sulfonic acids.
Claim 7
Dependent Claim
15 words
The method of claim 5 wherein said deglazing acid consists essentially of p-toluene sulfonic acid.
Claim 8
Dependent Claim
39 words
The method of claim 5 which also comprises carrying out the filler removal step and the deglazing step at the same time by contacting said surface with said filler removal acid and said deglazing acid at the same time.
Claim 9
Dependent Claim
15 words
The method of claim 7 wherein said deglazing acid consists essentially of p-toluene sulfonic acid.
Claim 10
Dependent Claim
20 words
The method of claim 8 wherein said filler comprises a siliceous composition and said filler removal acid comprises hydrofluoric acid.
Claim 11
Dependent Claim
36 words
The method of claim 1 wherein said filler removal acid is at least one of the group consisting essentially of acetic, chromic, citric, hydrobromic, hydrochloric, hydrofluoric, nitric, phenyl sulfonic, phosphoric, sulfuric, tartaric, and toluene sulfonic acids.
Claim 12
Dependent Claim
20 words
The method of claim 1 wherein said filler comprises a siliceous composition and said filler removal acid comprises hydrofluoric acid.
Claim 13
Dependent Claim
39 words
The method of claim 1 wherein said step of removing essentially all moisture from said surface before electroplating thereof comprises contacting said surface with forced hot air at a temperature in the range of about 130° to 190° F.
Claim 14
Dependent Claim
47 words
The method of claim 1 which also comprises the step of removing essentially all moisture from said surface after removing filler therefrom and before electroless plating thereof by heating to an elevated temperature of not more than about 190° F. for not more than about 30 minutes.
Claim 15
Dependent Claim
40 words
The method of claim 13 wherein said step of removing essentially all moisture from said surface after removing filler therefrom comprises contacting said surface with forced hot air at a temperature in the range of about 130° to 190° F.
Claim 16
Dependent Claim
59 words
The method of claim 1 which also comprises the steps of cleaning said surface after removing filler therefrom and before electroless plating thereof, and removing essentially all moisture from said surface after cleaning thereof and before electroless plating thereof by heating to an elevated temperature of not more than about 190° F. for not more than about 30 minutes.
Claim 17
Dependent Claim
39 words
The method of claim 15 wherein said step of removing essentially all moisture from said surface after cleaning thereof comprises contacting said surface with forced hot air at a temperature in the range of about 130° to 190° F.
References Cited (Backward Citations)
US3466232A
Cited
US3579428A
Cited
US3544432A
Cited
US3767538A
Cited
US3793159A
Cited
US4298424A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |