US4550093A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Alumina-based aerogel supported transition metal catalyst useful as a Ziegler-Natta olefin polymerization catalyst and process for preparing same
Assignee: Honeywell International Inc
•
Filing: 1984-08-06
•
Granted: 1985-10-29
•
Expires: 2004-08-06
Abstract
Abstract A new polymerization catalyst system comprising an aluminum compound and a transition metal compound on an alumina-based aerogel support, a process for preparing the polymerization catalyst system and use of the catalyst system for polymerization and copolymerization of alpha-olefins are disclosed. A heat-activated alumina-based aerogel useful as a catalyst support and having a morphology by transmission electron microcopy comprising extremely thin folded film-like ribbons or plates and having a high BET surface area, high pore volume, and low bulk density is also disclosed.
Inventors
- 👤 Anthony J. Fanelli
- 👤 Alson K. Price
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 12:21
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y10; Y10S; Y10S502/00; Y10S502/526
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
120 words
A catalyst system for the polymerization and the copolymerization of alpha-olefins comprising a di(C 1 -C 18 alkyl) chloroaluminum compound or tri(C 1 -C 18 alkyl) aluminum compound and a catalyst comprising the reaction product of a transition metal compound formed from a member selected from the group consisting of titanium, vanadium, hafnium and zirconium, and members selected from the group of chlorides, oxychlorides, alkoxychlorides, and oxyalkoxychlorides with a heat-activated alumina-based aerogel having a BET surface area greater than about 300 m 2 /g, a pore volume greater than about 3 cm 3 /g, a bulk density less than about 0.1 g/cm 3 , a morphology by transmission electron microscopy comprising thin film-like structures, and being substantially free of carbon.
Claim 2
Dependent Claim
120 words
A catalyst system for the polymerization and the copolymerization of alpha-olefins comprising a di(C 1 -C 18 alkyl) chloroaluminum compound or tri(C 1 -C 18 alkyl) aluminum compound and a catalyst comprising the reaction product of a transition metal compound formed from a member selected from the group consisting of titanium, vanadium, hafnium and zirconium, and members selected from the group of chlorides, oxychlorides, alkoxychlorides, and oxyalkoxychlorides with a heat-activated alumina-based aerogel having a BET surface area greater than about 300 m 2 /g, a pore volume greater than about 3 cm 3 /g, a bulk density less than about 0.1 g/cm 3 , a morphology by transmission electron microscopy comprising thin film-like structures, and being substantially free of carbon.
Claim 3
Dependent Claim
69 words
The catalyst system of claim 1 wherein the heat-activated alumina-based aerogel comprises mixed metal oxides of at least 65 weight percent of an aluminum oxide and up to about 35 weight percent of at least one of the oxides selected from the group consisting of calcium oxide, barium oxide, magnesium oxide, cerium oxide, lanthanum oxide, titanium dioxide, zirconium oxide, chromium oxide, zinc oxide, gallium oxide, silica and antimony oxide.
Claim 4
Dependent Claim
20 words
The catalyst system that is described in claim 2 wherein said heat-activated alumina-based aerogel is substantially free of fluorinated alumina.
Claim 5
Dependent Claim
37 words
The catalyst system of claim 3 wherein the morphology by transmission electron microscope comprises thin film-like ribbons and plates, said ribbons and plates being folded upon themselves and twisted around one another and rolled up into scrolls.
Claim 6
Dependent Claim
20 words
The catalyst system of claim 4 wherein the morphology of the heat-activated alumina-based aerogel is substantially free of spherical particles.
Claim 7
Independent Claim
228 words
A method of preparing a catalyst system for polymerization and copolymerization of alpha-olefins which comprises: (a) forming a solution or a suspension comprising an alcohol or mixture of alcohols selected from C 1 to C 5 alcohols and a hydrolyzable aluminum compound and at least about a stoichiometric amount of water required to hydrolyze said aluminum compound; (b) heating a suspension comprising the hydrolyzed and hydrolyzable aluminum compound in the presence of a solvent comprising methanol to a temperature above the critical temperature of the solvent comprising methanol; (c) removing the solvent comprising methanol under supercritical conditions to form an alumina-based aerogel having a carbon content; (d) heating said carbon-containing alumina-based aerogel in the presence of an oxygen-containing gas stream at a temperature of at least about 400° C. for a time sufficient to form a heat activated alumina-based aerogel substantially free of carbon; and (e) reacting said heat-activated aerogel under substantially anhydrous conditions with a transition metal compound formed from a member selected from the group consisting of titanium, vanadium, hafnium, and zirconium and members selected from the group consisting of chloride, oxychlorides, alkoxychlorides and oxyalkoxychlorides with said heat-activated aerogel to form a catalyst system having a BET surface area greater than about 300 m 2 /g, a pore volume greater than about 3 cm 3 /g, a bulk density less than about 0.1 g/cm 3 .
Claim 8
Independent Claim
228 words
A method of preparing a catalyst system for polymerization and copolymerization of alpha-olefins which comprises: (a) forming a solution or a suspension comprising an alcohol or mixture of alcohols selected from C 1 to C 5 alcohols and a hydrolyzable aluminum compound and at least about a stoichiometric amount of water required to hydrolyze said aluminum compound; (b) heating a suspension comprising the hydrolyzed and hydrolyzable aluminum compound in the presence of a solvent comprising methanol to a temperature above the critical temperature of the solvent comprising methanol; (c) removing the solvent comprising methanol under supercritical conditions to form an alumina-based aerogel having a carbon content; (d) heating said carbon-containing alumina-based aerogel in the presence of an oxygen-containing gas stream at a temperature of at least about 400° C. for a time sufficient to form a heat activated alumina-based aerogel substantially free of carbon; and (e) reacting said heat-activated aerogel under substantially anhydrous conditions with a transition metal compound formed from a member selected from the group consisting of titanium, vanadium, hafnium, and zirconium and members selected from the group consisting of chloride, oxychlorides, alkoxychlorides and oxyalkoxychlorides with said heat-activated aerogel to form a catalyst system having a BET surface area greater than about 300 m 2 /g, a pore volume greater than about 3 cm 3 /g, a bulk density less than about 0.1 g/cm 3 .
Claim 9
Dependent Claim
108 words
The method of claim 6 wherein the solution or suspension formed in step (a) comprises at least about 65 weight percent (basis Al 2 O 3 ) of a hydrolyzable aluminum compound and up to about 35 weight percent (basis metal oxide) of at least one member selected from the group consisting of hydrolyzable compounds of calcium, barium, magnesium, cerium, lanthanum, titanium, zirconium, chromium, zinc, gallium, silicon and antimony and wherein the alumina-based aerogel produced in step (c) has a carbon content of at least about 1-8 weight percent and wherein the catalyst system in step (e) has a Cl to Ti ratio of no more than 4:1.
Claim 10
Dependent Claim
21 words
The process of claim 6 wherein a solution of a hydrolyzable aluminum compound and an alcohol is formed in step (a).
Claim 11
Dependent Claim
32 words
The process of claim 8 wherein the solution in step (a) comprises aluminum isopropoxide in isopropanol and where the solute in steps (b) and (c) is a mixture of methanol and isopropanol.
Claim 12
Dependent Claim
19 words
The process of claim 6 wherein a suspension of an aluminum alkoxide in methanol is formed in step (a).
Claim 13
Dependent Claim
19 words
The process of claim 10 wherein the aluminum alkoxide is an aluminum secondary C 3 to C 5 alkoxide.
Claim 14
Dependent Claim
13 words
The process of claim 11 wherein the aluminum secondary alkoxide is aluminum isopropoxide.
Claim 15
Dependent Claim
84 words
A heat-activated alumina-based aerogel having a morphology by transmission electron microscopy comprising thin film-like ribbons and plates, said ribbons and plates being folded upon themselves and twisted around one another and rolled up into scrolls or mixtures of spherical particles and said thin film-like ribbons and plates, a BET surface area greater than about 300m 2 /g, a pore volume greater than about 3 cm 3 /g, and a bulk density less than about 0.1 g/cm 3 , and being substantially free of carbon.
Claim 16
Dependent Claim
84 words
A heat-activated alumina-based aerogel having a morphology by transmission electron microscopy comprising thin film-like ribbons and plates, said ribbons and plates being folded upon themselves and twisted around one another and rolled up into scrolls or mixtures of spherical particles and said thin film-like ribbons and plates, a BET surface area greater than about 300m 2 /g, a pore volume greater than about 3 cm 3 /g, and a bulk density less than about 0.1 g/cm 3 , and being substantially free of carbon.
Claim 17
Dependent Claim
139 words
A process for preparing a heat-activated alumina aerogel which comprises the steps of: (a) forming a solution or a suspension comprising an alcohol or mixture of alcohols selected from C 1 to C 5 alcohols and a hydrolyzable aluminum compound and at least about a stoichiometric amount of water required to hydrolyze said hydrolyzable aluminum compound; (b) heating a suspension comprising the hydrolyzed and hydrolyzable aluminum compound in the presence of a solvent comprising methanol to a temperature above the critical temperature of the solvent comprising methanol; (c) removing the solvent comprising methanol under supercritical conditions to form an alumina-based aerogel; and (d) heating the carbon-containing alumina-based aerogel in the presence of an oxygen-containing gas stream at a temperature of at least about 400° C. for a time sufficient to form a heat-activated alumina-based aerogel substantially free of carbon.
Claim 18
Dependent Claim
139 words
A process for preparing a heat-activated alumina aerogel which comprises the steps of: (a) forming a solution or a suspension comprising an alcohol or mixture of alcohols selected from C 1 to C 5 alcohols and a hydrolyzable aluminum compound and at least about a stoichiometric amount of water required to hydrolyze said hydrolyzable aluminum compound; (b) heating a suspension comprising the hydrolyzed and hydrolyzable aluminum compound in the presence of a solvent comprising methanol to a temperature above the critical temperature of the solvent comprising methanol; (c) removing the solvent comprising methanol under supercritical conditions to form an alumina-based aerogel; and (d) heating the carbon-containing alumina-based aerogel in the presence of an oxygen-containing gas stream at a temperature of at least about 400° C. for a time sufficient to form a heat-activated alumina-based aerogel substantially free of carbon.
Claim 19
Dependent Claim
56 words
The process of claim 14 wherein the morphology of the alumina-based aerogel by electron microscopy consists essentially of extremely thin film-like ribbons and plates, said ribbons and plates being folded upon themselves and twisted around one another and rolled up into scrolls and wherein a suspension of aluminum isopropoxide in methanol is formed in step (a).
Claim 20
Dependent Claim
67 words
The process of claim 14 wherein the suspension formed in step (a) comprises at least about 65 weight percent (basis Al 2 O 3 ) of a hydrolyzable aluminum compound and up to about 35 weight percent (basis metal oxide) of at least one member selected from the group consisting of hydrolyzable compounds of calcium, barium, magnesium, cerium, lanthanum, titanium, zirconium, chromium, zinc, gallium, silicon and antimony.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |