Process for the polymerization of olefins
Assignee: Solvay SA
•
Filing: 1979-12-26
•
Granted: 1981-01-27
•
Expires: 1999-12-26
Abstract
Abstract Alumina-supported halogen-containing transition metal compounds prepared in such manner that (a) the transition metal compound is chemically bound to and supported by an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., (b) the concentration of the transition metal compound chemically bound to the support is greater than 10 grams of transition metal per kilogram of activated alumina, and (c) the atom ratio of halogen to transition metal on the support is higher than that of the halogen-containing transition metal compound which is used and preferably greater than 3:1, have been found to be unusually effective cocatalysts for the polymerization of ethylene and other α-olefins. These supported cocatalysts, which may be used to produce polyethylene as well as interpolymers of ethylene with other α-olefins and with diolefins, are prepared by heating an alumina hydrate (such as boehmite) to a temperature in the range from about 500° C. to 900° C. for a period of time sufficient to form an activated alumina having an internal pore volume greater than 0.8 cc/g., and then reacting the resultant activated alumina under substantially anhydrous conditions with a halogen-containing compound of a transition metal of Groups IV-A, V-A or VI-A of the Periodic Table. When ethylene is polymerized or copolymerized in the presence of a catalytic amount of the reaction product of an organometallic compound of a metal of Groups I-B, II-A, II-B, III-B or IV-B of the Periodic Table, and one of these supported cocatalysts, it is possible to produce normally solid, high molecular weight polyethylene or interpolymers of ethylene and other α-olefins at exceptionally high yields of polymer per gram of catalyst.
Inventors
- 👤 Luigi Reginato
- 👤 Charles Bienfait
- 👤 Jacques Stevens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:29
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
136 words
A process for the polymerization of ethylene which comprises contacting ethylene, at a temperature and at a pressure sufficient to initiate the polymerization reaction, with a catalytic amount of (a) a tri(C 4 -C 18 alkyl) aluminum compound; and (b) a supported cocatalyst prepared by reacting, under substantially anhydrous conditions, (1) titanium tetrachloride together with (2) an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., to form a supported cocatalyst in which (a) the TiCl 4 is chemically bound to and supported by the activated alumina, (b) the concentration of the titanium compound is greater than 10 grams of titanium metal per kilogram of activated alumina, and (c) the ratio of chlorine to titanium metal in the supported cocatalyst is higher than that of the TiCl 4 .
Claim 2
Dependent Claim
136 words
A process for the polymerization of ethylene which comprises contacting ethylene, at a temperature and at a pressure sufficient to initiate the polymerization reaction, with a catalytic amount of (a) a tri(C 4 -C 18 alkyl) aluminum compound; and (b) a supported cocatalyst prepared by reacting, under substantially anhydrous conditions, (1) titanium tetrachloride together with (2) an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., to form a supported cocatalyst in which (a) the TiCl 4 is chemically bound to and supported by the activated alumina, (b) the concentration of the titanium compound is greater than 10 grams of titanium metal per kilogram of activated alumina, and (c) the ratio of chlorine to titanium metal in the supported cocatalyst is higher than that of the TiCl 4 .
Claim 3
Dependent Claim
119 words
A process for the polymerization of ethylene according to claim 1 in which the supported cocatalyst is prepared by (1) heating an alumina hydrate to a temperature in the range from about 500° C. to 900° C. for a period of time sufficient to form an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., and (2) reacting the resultant activated alumina with TiCl 4 , to form a supported cocatalyst in which (a) the TiCl 4 metal compound is chemically bound to and supported by the activated alumina, and (b) the concentration of the titanium metal compound is greater than 10 grams of the titanium metal per kilogram of activated alumina.
Claim 4
Dependent Claim
119 words
A process for the polymerization of ethylene according to claim 1, in which the supported cocatalyst is prepared by (1) heating the α-monohydrate of alumina to a temperature in the range from about 700° C. to 800° C. for a period of time sufficient to form an activated alumina having a high surface area and an internal pore volume greater than 1 cc/g., and (2) reacting the resultant activated alumina with TiCl 4 , to form a supported cocatalyst in which (a) the titanium metal compound is chemically bound to and supported by the activated alumina, and (b) the concentration of the titanium metal compound is greater than 10 grams of the titanium metal per kilogram of activated alumina.
Claim 5
Dependent Claim
65 words
A process for the polymerization of ethylene according to claim 1, in which the supported cocatalyst is prepared by suspending the activated alumina in an excess amount of the titanium metal compound maintained as a liquid during such reaction while permitting the gaseous byproducts of the reaction between the activated alumina and the titanium metal compound to remain in the reaction mixture during each reaction.
Claim 6
Dependent Claim
155 words
A process for preparing catalysts for the low-pressure polymerization of ethylene which comprises preparing a supported cocatalyst by (1) heating an alumina hydrate to a temperature in the range from about 500° C. to 900° C. for a period of time sufficient to form an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., and (2) reacting the activated alumina under substantially anhydrous conditions with a titanium tetrachloride, to form a supported cocatalyst in which (a) the titanium tetrachloride compound is chemically bound to and supported by the activated alumina, (b) the concentration of the titanium metal compound is greater than 10 grams of the titanium metal per kilogram of activated alumina, and (c) the ratio of chlorine to titanium metal in the supported cocatalyst is higher than that of the titanium tetrachloride compound, and (3) reacting the resultant supported cocatalyst with a tri(C 4 -C 18 alkyl)aluminum.
Claim 7
Dependent Claim
155 words
A process for preparing catalysts for the low-pressure polymerization of ethylene which comprises preparing a supported cocatalyst by (1) heating an alumina hydrate to a temperature in the range from about 500° C. to 900° C. for a period of time sufficient to form an activated alumina having a high surface area and an internal pore volume greater than 0.8 cc/g., and (2) reacting the activated alumina under substantially anhydrous conditions with a titanium tetrachloride, to form a supported cocatalyst in which (a) the titanium tetrachloride compound is chemically bound to and supported by the activated alumina, (b) the concentration of the titanium metal compound is greater than 10 grams of the titanium metal per kilogram of activated alumina, and (c) the ratio of chlorine to titanium metal in the supported cocatalyst is higher than that of the titanium tetrachloride compound, and (3) reacting the resultant supported cocatalyst with a tri(C 4 -C 18 alkyl)aluminum.
Claim 8
Dependent Claim
61 words
A process for preparing polymerization catalysts according to claim 5, in which the activated alumina is prepared by heating an α-monohydrate of alumina to a temperature in the range from about 700° C. to 800° C. for a period of time sufficient to form an activated alumina having a high surface area and an internal pore volume greater than 1 cc/g.
Claim 9
Dependent Claim
63 words
A process for preparing catalysts according to claim 5, in which the supported cocatalyst is formed by suspending the activated alumina in an excess amount of the titanium metal compound maintained as a liquid during such reaction while permitting the gaseous byproducts of the reaction between the activated alumina and the titanium metal compound to remain in the reaction mixture during such reaction.
References Cited (Backward Citations)
US3166542A
Cited
US3325247A
Cited
US3526616A
Cited
US3513150A
Cited
US3506633A
Cited
GB1140649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-27 | 1984-07-28 | 1985-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-27 | 1988-07-28 | 1989-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-27 | 1992-07-28 | 1993-01-27 | $7700.00 | Window Closed / Lapsed |