Vinylidene chloride type resin expandable particles, foam particles, in-mold foam molding by use thereof and process for producing them
Assignee: Asahi Kasei Corp
•
Filing: 1984-12-05
•
Granted: 1985-10-29
•
Expires: 2004-12-05
Abstract
Abstract This invention discloses a vinylidene chloride resin type in-mold foam molding having a broad cross-sectional area and a free shape, useful as thermal insulating plate materials or anti-shock molded vessels, and foam particles or expandable particles convenient for preparation thereof, and also a series of advantageous foaming techniques for completion of such a molding. The above foam molding can be prepared by bringing fine particles of a non-crystalline vinylidene chloride type resin obtained generally by suspension polymerization into contact with a volatile organic blowing agent thereby impregnating the resins with the blowing agent to form expandable resin particles, which are in turn subjected to expansion as such, or after forming into pre-expanded foam particles including expandable gas therein, by filling in a mold cavity which can be closed but not sealed, under heating to form a molding through fusion mutually between the expanded particles.
Inventors
- 👤 Norihiko Sakata
- 👤 Nobuo Miura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:53
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/16; C08J9/18; C08J9/04; C08J9/12; C08J9/14; C08J9/143; C08J2327/00; C08J2327/02; C08J2327/04; C08J2327/08; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/09; Y10S264/15; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
102 words
A process for producing expandable vinylidene chloride resin particles, which comprises bringing substantially non-crystalline vinylidene chloride resin particles with an average particle size within the range of from 0.05 to 5 mm, which are smooth on the surfaces without interstices into contact with a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, at a temperature of 50° to 120° C. thereby impregnating the particles with said blowing agent.
Claim 2
Dependent Claim
102 words
A process for producing expandable vinylidene chloride resin particles, which comprises bringing substantially non-crystalline vinylidene chloride resin particles with an average particle size within the range of from 0.05 to 5 mm, which are smooth on the surfaces without interstices into contact with a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, at a temperature of 50° to 120° C. thereby impregnating the particles with said blowing agent.
Claim 3
Dependent Claim
20 words
A process for producing expandable vinylidene chloride resin particles according to claim 1, wherein said vinylidene chloride resin is crosslinked.
Claim 4
Dependent Claim
140 words
A process for producing vinylidene chloride resin foam particles, which comprises bringing substantially non-crystalline vinylidene chloride resin particles with an average particle size within the range of from 0.05 to 5 mm, which are smooth on the surfaces without interstice into contact with a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, at a temperature of 50° to 120° C. thereby impregnating the particles with said blowing agent, and heating the impregnated resin particles to effect expansion thereof to an expansion ratio of 4 to 150-fold thereby forming multicellular particles with a closed cell percentage of 65% or more including a volatile organic blowing agent therein.
Claim 5
Dependent Claim
140 words
A process for producing vinylidene chloride resin foam particles, which comprises bringing substantially non-crystalline vinylidene chloride resin particles with an average particle size within the range of from 0.05 to 5 mm, which are smooth on the surfaces without interstice into contact with a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, at a temperature of 50° to 120° C. thereby impregnating the particles with said blowing agent, and heating the impregnated resin particles to effect expansion thereof to an expansion ratio of 4 to 150-fold thereby forming multicellular particles with a closed cell percentage of 65% or more including a volatile organic blowing agent therein.
Claim 6
Dependent Claim
20 words
A process for producing vinylidene chloride resin foam particles according to claim 3, wherein said vinylidene chloride resin is crosslinked.
Claim 7
Dependent Claim
67 words
A process for producing vinylidene chloride resin foam particles according to claim 3 or claim 4, wherein the vinylidene chloride resin is a copolymer of vinylidene chloride and methyl methacrylate, the content of methyl methacrylate units in the copolymer is within the range of from 30 to 90 wt. % and said resin has a Vicat softening point within the range of from 55° to 110° C.
Claim 8
Dependent Claim
76 words
A process for producing vinylidene chloride resin foam particles according to claim 3 or claim 4, wherein the volatile organic blowing agent impregnated is a single substance or a mixture of two or more compounds selected from aliphatic hydrocarbons having boiling points not higher than 60° C. and aliphatic halogenated hydrocarbons having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0.
Claim 9
Dependent Claim
43 words
A process for producing vinylidene chloride resin foam particles according to claim 6, wherein the volatile organic blowing agent impregnated is composed mainly of a mixed blowing agent of trichloromonofluoromethane and dichlorodifluoromethane, and its weight ratio is within the range of from 20-70:80-30.
Claim 10
Dependent Claim
43 words
A process for producing vinylidene chloride resin foam particles according to claim 6, wherein the volatile organic blowing agent impregnated is composed mainly of a mixed blowing agent of monochlorodifluoromethane and dichlorodifluoromethane, and its weight ratio is within the range of from 20-100:80-0.
Claim 11
Dependent Claim
142 words
A process for producing a vinylidiene chloride resin in-mold steam foam molding, which comprises incorporating a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, in substantially non-crystalline vinylidene chloride resin particles with an average particle size in the range of from 0.05 to 5 mm, which are smooth on the particle surfaces without insterstices, filling a mold cavity which can be closed but not sealed with these particles as such or after converting them to foam particles containing expandable gas therein by heating thereof, and effecting heating expansion of these particles to an expansion ratio of 4 to 150-fold thereby forming a molding through fusion mutually between particles.
Claim 12
Dependent Claim
142 words
A process for producing a vinylidiene chloride resin in-mold steam foam molding, which comprises incorporating a volatile organic blowing agent, which is a single substance or a mixture of two or more compounds having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0, in substantially non-crystalline vinylidene chloride resin particles with an average particle size in the range of from 0.05 to 5 mm, which are smooth on the particle surfaces without insterstices, filling a mold cavity which can be closed but not sealed with these particles as such or after converting them to foam particles containing expandable gas therein by heating thereof, and effecting heating expansion of these particles to an expansion ratio of 4 to 150-fold thereby forming a molding through fusion mutually between particles.
Claim 13
Dependent Claim
23 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 9, wherein said vinylidene chloride resin is crosslinked.
Claim 14
Dependent Claim
40 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 9 or claim 10, wherein the expandable gas included within the foam particles is composed mainly of a volatile blowing agent and an inorganic gas.
Claim 15
Dependent Claim
72 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 9 or claim 10, wherein the above vinylidene chloride resin is a copolymer of vinylidene chloride and methyl methacrylate, the content of methyl methacrylate units in the copolymer is within the range of from 30 to 90 wt. %, and the Vicat softening point of said resin is within the range of from 55° to 110° C.
Claim 16
Dependent Claim
78 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 9 or claim 10, wherein the volatile organic blowing agent is a single substance or a mixture of two or more compounds selected from aliphatic hydrocarbons having boiling points not higher than 60° C. and aliphatic halogenated hydrocarbons having boiling points not higher than 60° C. and its molar average solubility parameter (SP value) is within the range of from 5.7 to 7.0.
Claim 17
Dependent Claim
45 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 13, wherein the volatile organic blowing agent is composed mainly of a mixed blowing agent of trichloromorofluoromethane and dichlorodifluoromethane, and its weight ratio is within the range of from 20-70:80-30.
Claim 18
Dependent Claim
46 words
A process for producing a vinylidene chloride resin in-mold steam foam molding according to claim 13, wherein the volatile organic blowing agent included is composed mainly of a mixed blowing agent of monochlorodifluoromethane and dichlorodifluoromethane, and its weight ratio is within the range of from 20-100:80-0.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-28 | 1989-04-29 | 1989-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-28 | 1993-04-29 | 1993-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-28 | 1997-04-29 | 1997-10-29 | $7700.00 | Window Closed / Lapsed |