Abstract
Abstract A method of preparing a foamable polyvinyl system resin composition which renders a non-flammable, high strength to weight ratio foam product comprises, reacting at least 0.05 parts by weight of an organic radical initiator per 1 part by weight of polyvinyl system resin with the components consisting essentially of (a) at least one polyvinyl system resin (b) 2-100 parts by weight of at least one inorganic filler per 1 part by weight of polyvinyl system resin (c) an effective amount of at least one blowing agent.
Inventors
- 👤 Takayuki Otsu
- 👤 Hirosuke Kojima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:14
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08J9/0066; C08J9/0014; C08J9/0028; C08J9/0033; C08K; C08K3/00; C08K5/00; C08K5/16; C08K5/22; C08K5/23; C08K5/36; C08K5/39; C08K5/40; C08K5/45; C08K5/46; C08K5/47; C08L; C08L27/00; C08L27/02; C08L27/04; C08J2357/00; C08J2357/06; C08J2357/08
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
126 words
A method of preparing a foamable polyvinyl resin composition suitable for forming nonflammable foamed products having compressive strengths greater than 10 kg/cm 2 and densities less than 100 kg/m 3 , said method comprising the step of reacting (a) polyvinyl chloride resin; (b) at least 0.05 parts by weight organic initiator per 1 part by weight of polyvinyl chloride resin, said organic initiator being selected from the group consisting of azobisalkylnitrile, azobiscyclohexylcarbonitrile, azobisester, phenylazotriphenylmethane, phenylazothiophenylether, phenylazophenylamine, azobisbenzoyl, tetraalkylterazane, 4,4'-azobis-4-cyano valeric acid, dibenzothiazoledisulfide, metal compound of 2-mercapto benzothiazole, N-cyclohexyl-2-benzothiazolysulphenamide, tetraalkylthiuramdisulfide, and metal derivatives of dialkyldithiocarbamic acid; (c) 2-100 parts by weight of at least one inorganic filler per 1 part by weight of polyvinyl chloride resin; and (d) an effective amount of at least one blowing agent.
Claim 2
Independent Claim
126 words
A method of preparing a foamable polyvinyl resin composition suitable for forming nonflammable foamed products having compressive strengths greater than 10 kg/cm 2 and densities less than 100 kg/m 3 , said method comprising the step of reacting (a) polyvinyl chloride resin; (b) at least 0.05 parts by weight organic initiator per 1 part by weight of polyvinyl chloride resin, said organic initiator being selected from the group consisting of azobisalkylnitrile, azobiscyclohexylcarbonitrile, azobisester, phenylazotriphenylmethane, phenylazothiophenylether, phenylazophenylamine, azobisbenzoyl, tetraalkylterazane, 4,4'-azobis-4-cyano valeric acid, dibenzothiazoledisulfide, metal compound of 2-mercapto benzothiazole, N-cyclohexyl-2-benzothiazolysulphenamide, tetraalkylthiuramdisulfide, and metal derivatives of dialkyldithiocarbamic acid; (c) 2-100 parts by weight of at least one inorganic filler per 1 part by weight of polyvinyl chloride resin; and (d) an effective amount of at least one blowing agent.
Claim 3
Dependent Claim
43 words
A method of preparing a foamable polyvinyl resin composition as claimed in claim 1, wherein said polyvinyl chloride resin includes at least one member selected from polyvinyl chloride, polyvinylidene chloride, copolymers of the polyvinyl chloride, copolymers of the polyvinylidene chloride, and chlorinated polyethylene.
Claim 4
Dependent Claim
154 words
A process for making a vinyl chloride polymer foam suitable for forming nonflammable foamed products having compressive strengths greater than 10 kg/cm 2 and densities less than 100 kg/cm 3 , said process comprising the steps of: (1) preparing a composition consisting of: (a) a vinyl chloride polymer selected from the group consisting of polyvinyl chloride, polyvinylidene chloride, copolymers of polyvinyl chloride, chlorinated polyethylene; (b) 2-100 parts per 1 part of vinyl chloride polymer of at least one inorganic filler; (c) a blowing agent; and (d) 0.05 parts per 1 part of polymer of an organic radical initiator selected from the group consisting of azobisalkylnitrile, azobiscyclohexylcarbonitrile, azobisester, phenylazotriphenylmethane, phenylazothiophenylether, phenylazophenylamine, azobisbenzoyl, tetraalkylterazane, 4,4'-azobis-4-cyano valeric acid, dibenzothiazoledisulfide, metal compound of 2-mercapto benzothiazole, N-cyclohexyl-2-benzothiazolysulphenamide, tetraalkylthiuramdisulfide, and metal derivatives of dialkyldithiocarbamic acid, and (2) blending the composition prepared according to step (1) at elevated temperatures until the temperature of the blend is raised to about 40°-60° C.
Claim 5
Dependent Claim
154 words
A process for making a vinyl chloride polymer foam suitable for forming nonflammable foamed products having compressive strengths greater than 10 kg/cm 2 and densities less than 100 kg/cm 3 , said process comprising the steps of: (1) preparing a composition consisting of: (a) a vinyl chloride polymer selected from the group consisting of polyvinyl chloride, polyvinylidene chloride, copolymers of polyvinyl chloride, chlorinated polyethylene; (b) 2-100 parts per 1 part of vinyl chloride polymer of at least one inorganic filler; (c) a blowing agent; and (d) 0.05 parts per 1 part of polymer of an organic radical initiator selected from the group consisting of azobisalkylnitrile, azobiscyclohexylcarbonitrile, azobisester, phenylazotriphenylmethane, phenylazothiophenylether, phenylazophenylamine, azobisbenzoyl, tetraalkylterazane, 4,4'-azobis-4-cyano valeric acid, dibenzothiazoledisulfide, metal compound of 2-mercapto benzothiazole, N-cyclohexyl-2-benzothiazolysulphenamide, tetraalkylthiuramdisulfide, and metal derivatives of dialkyldithiocarbamic acid, and (2) blending the composition prepared according to step (1) at elevated temperatures until the temperature of the blend is raised to about 40°-60° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-16 | 1988-04-16 | 1988-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-16 | 1992-04-16 | 1992-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-16 | 1996-04-16 | 1996-10-16 | $7700.00 | Window Closed / Lapsed |