Fluorinated cellulose acetate polymers
Assignee: APPLIED MEMBRANE TECHNOLOGY Inc A CORP OF MINNESOTA
•
Filing: 1984-08-13
•
Granted: 1985-10-22
•
Expires: 2004-08-13
Abstract
Abstract A new class of compounds, perfluoroacyl modified cellulose acetate polymers, has been synthesized. A novel method of preparation of these compounds is shown. It was discovered that these polymers can be used to form membranes having superior characteristics. The perfluoroacyl modification allows these polymers to be cast as ultrathin membranes resulting in improved gas flux rates while maintaining a high degree of selectivity, improved resistance to water, and the elimination of post treatment procedures. Furthermore these polymers can be spun as hollow fibers.
Inventors
- 👤 Ashok K. Sharma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:11
CPC Classifications
C; C08; C08B; C08B3/00; C08B3/14; B; B01; B01D; B01D71/00; B01D71/06; B01D71/08; B01D71/12; B01D71/14; B01D71/16; C08B3/22
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
62 words
A modified cellulose acetate polymer, which comprises, a cellulose acetate polymer in which substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general form --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10, and wherein the fluorine content of the polymer is at least about 15 percent by weight.
Claim 2
Dependent Claim
62 words
A modified cellulose acetate polymer, which comprises, a cellulose acetate polymer in which substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general form --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10, and wherein the fluorine content of the polymer is at least about 15 percent by weight.
Claim 3
Dependent Claim
91 words
A thin film composite membrane, which consists of, a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10, and wherein the fluorine content of said polymer is at least about 15 percent by weight, and said polymer laminated to microporous supports forming the thin film composite membrane, and said membrane having a thickness of from 0.5 to 2.5 microns.
Claim 4
Dependent Claim
91 words
A thin film composite membrane, which consists of, a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10, and wherein the fluorine content of said polymer is at least about 15 percent by weight, and said polymer laminated to microporous supports forming the thin film composite membrane, and said membrane having a thickness of from 0.5 to 2.5 microns.
Claim 5
Dependent Claim
85 words
A microporous hollow fiber membrane, which consists of, microporous hollow fibers spun from a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10 and wherein the fluorine content of said polymer is at least about 15 percent by by weight, said microporous hollow fibers having pore dimensions from about 50 angstroms to 1 micron.
Claim 6
Dependent Claim
85 words
A microporous hollow fiber membrane, which consists of, microporous hollow fibers spun from a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10 and wherein the fluorine content of said polymer is at least about 15 percent by by weight, said microporous hollow fibers having pore dimensions from about 50 angstroms to 1 micron.
Claim 7
Dependent Claim
75 words
A dense skinned asymetric hollow fiber membrane, which consists of, dense skinned assymetric hollow fibers spun from a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10 and wherein the fluorine content of said polymer is at least about 15 percent by weight.
Claim 8
Dependent Claim
75 words
A dense skinned asymetric hollow fiber membrane, which consists of, dense skinned assymetric hollow fibers spun from a modified cellulose acetate polymer, in which said polymer substantially all residual hydroxyl groups have been acylated to form perfluoroacyl ester groups having the general formula --OCO(CF 2 ) N CF 3 , wherein N is a number from 2 to 10 and wherein the fluorine content of said polymer is at least about 15 percent by weight.
Claim 9
Dependent Claim
87 words
A method of manufacturing the perfluoroacyl modified cellulose acetate as defined in claim 1, which comprises: dissolving cellulose acetate, adding pyridine to the dissolved cellulose acetate solution using an amount of pyridine that is approximately 50 to 100 percent in excess of the perfluoroacyl halide used, combining the perfluoroacyl halide with the pyridine and cellulose acetate solution using an amount of perfluoroacyl halide that is approximately a 100 to 200 percent stoichiometric excess, precipitating the mixture of perfluoroacyl halide pyridine and cellulose acetate, and filtering the precipitate.
References Cited (Backward Citations)
GB1120373A
Cited
US4008047A
Cited
US4035459A
Cited
US4318785A
Cited
US4214020A
Cited
US4305823A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |