Patent US4548833A successfully refreshed from Google Patents.
US4548833A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing a magnetic recording medium
Assignee: Fujifilm Holdings Corp
•
Filing: 1983-01-28
•
Granted: 1985-10-22
•
Expires: 2003-01-28
Abstract
Abstract A method for preparing a magnetic recording medium is disclosed. The method includes providing a support base and a particular coating composition for the base. The composition is comprised of a ferromagnetic powder, a binder containing a compound capable of being polymerized with electron beam irradiation, and a solvent. The composition has apparent viscosity of about 1 to 150 centipoise at a shearing speed of 4000 sec -1 . After coating the composition on the support base, the coated layer is subjected to magnetic orientation. During orientation or shortly thereafter the coated layer is subjected to electrom beam irradiation and then dried in order to evaporate the solvent. The magnetic recording medium prepared has excellent dispersibility of the ferromagnetic fine powder within the binder, which further provides a smooth surface and excellent electrical properties as well as anti-abrasion properties.
Inventors
- 👤 Hiroshi Hashimoto
- 👤 Tsutomu Okita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 00:32
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/84; G11B5/842; G11B5/845; Y; Y10; Y10S; Y10S428/00; Y10S428/90
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
107 words
A method for preparing a magnetic recording medium, comprising the steps of: providing a support base; providing a coating composition comprising a ferromagnetic fine powder, a binder containing a compound capable of being polymerized with electron beam radiation, and a solvent, the composition having an apparent viscosity of 1 to 150 centipoise at a shearing speed of 4000 sec -1 ; coating the composition on a surface of the support base to form a coated layer; subjecting the coated layer to magnetic orientation while the coated layer is still wet; irradiating the coated layer with an electrom beam; and drying the coated layer to evaporate the solvent.
Claim 2
Independent Claim
107 words
A method for preparing a magnetic recording medium, comprising the steps of: providing a support base; providing a coating composition comprising a ferromagnetic fine powder, a binder containing a compound capable of being polymerized with electron beam radiation, and a solvent, the composition having an apparent viscosity of 1 to 150 centipoise at a shearing speed of 4000 sec -1 ; coating the composition on a surface of the support base to form a coated layer; subjecting the coated layer to magnetic orientation while the coated layer is still wet; irradiating the coated layer with an electrom beam; and drying the coated layer to evaporate the solvent.
Claim 3
Dependent Claim
35 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the coated layer is irradiated with the electron beam within 5 minutes or less after being subjected to the magnetic orientation.
Claim 4
Dependent Claim
38 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the coated layer is being subjected to the magnetic orientation at the same time it is being subjected to irradiation with the electron beam.
Claim 5
Dependent Claim
39 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the binder of the coating composition is comprised of 3% by weight or more of the compound capable of being polymerized with electron beam irradiation.
Claim 6
Dependent Claim
35 words
A method for preparing a magnetic recording medium as claimed in claim 4, wherein the binder is comprised of 5% by weight or more of the compound capable of being polymerized with electron beam irradiation.
Claim 7
Dependent Claim
35 words
A method for preparing a magnetic recording medium as claimed in claim 5, wherein the binder is comprised of 8% by weight or more of the compound capable of being polymerized with electron beam irradiation.
Claim 8
Dependent Claim
41 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the coating composition is comprised of the binder in an amount of 0.1 to 7 parts by weight per part by weight of the fine magnetic powder.
Claim 9
Dependent Claim
41 words
A method for preparing a magnetic recording medium as claimed in claim 7, wherein the coating composition is comprised of a binder in an amount of 0.2 to 0.5 parts by weight per part by weight of the fine magnetic powder.
Claim 10
Dependent Claim
35 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the apparent viscosity of the coating composition is 1 to 100 centipoise at a shearing speed of 4000 sec -1 .
Claim 11
Dependent Claim
35 words
A method for preparing a magnetic recording medium as claimed in claim 9, wherein the apparent viscosity of the coating composition is 1 to 50 centipoise at a shearing speed of 4000 sec -1 .
Claim 12
Dependent Claim
27 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the dried coated layer has a thickness of from 0.5 to 15 μm.
Claim 13
Dependent Claim
26 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the electron beam has an accelerating voltage of 100 to 1000 kV.
Claim 14
Dependent Claim
26 words
A method for preparing a magnetic recording medium as claimed in claim 12, wherein the electron beam has an accelerating voltage of 150 to 300 kV.
Claim 15
Dependent Claim
27 words
A method for preparing a magnetic recording medium as claimed in claim 1, wherein the drying is carried out at a temperature of 50° to 120° C.
Claim 16
Dependent Claim
27 words
A method for preparing a magnetic recording medium as claimed in claim 14, wherein the drying is carried out at a temperature of 70° to 100° C.
Claim 17
Dependent Claim
27 words
A method for preparing a magnetic recording medium as claimed in claim 15, wherein the drying is carried out at a temperature of 80° to 90° C.
Claim 18
Dependent Claim
26 words
A method for preparing a magnetic recording medium as claimed in claim 1, further comprising the step of: calendering the dried coated layer between calendering rollers.
Claim 19
Dependent Claim
38 words
A method for preparing a magnetic recording medium as claimed in claim 17, wherein the calendering is carried out by applying a pressure of 25 to 100 Kg/cm 2 at a temperature of about 10° to 100° C.
References Cited (Backward Citations)
US3104983A
Cited
US4058646A
Cited
US4049566A
Cited
US4180597A
Cited
US4394404A
Cited
US4443490A
Cited
US4415630A
Cited
US4448846A
Cited
JPS57111832A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |