US4548774A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing a SiC whisker-reinforced composite material
Assignee: TAKAI CARBON Co Ltd
•
Filing: 1983-07-19
•
Granted: 1985-10-22
•
Expires: 2003-07-19
Abstract
Abstract The invention provides a method for preparing a SiC whisker-reinforced composite material. A matrix material such as a metal, an alloy or a plastic is introduced into a fibrous base consisting of a SiC whisker sponge-like cake. The resultant structure is compressed into a desired shape as needed. The fibrous base is prepared by heating a mixture of silica gel or ashed rice hulls with a furnace carbon black and an additional amount of NaCl as a space forming agent for forming spaces conducive to whisker growth.
Inventors
- 👤 Masaru Akiyama
- 👤 Jotaro Yamada
- 👤 Masaya Takahata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:58
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/02; C; C04; C04B; C04B35/00; C04B35/622; C04B35/62204; C04B35/62213; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/12; B32B5/22; B32B5/24; B32B5/26; C04B35/62227; C04B35/62272; C04B35/62277; C04B35/62281; C04B35/626; C04B35/62605; C04B35/62645; C04B35/62675; C04B35/71; C04B35/78; C04B35/80; C04B38/00; C04B38/0067; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C22; C22C; C22C47/00; C22C47/08; B32B2305/00; B32B2305/08; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3217; C04B2235/3218; C04B2235/327; C04B2235/3272; C04B2235/3275; C04B2235/3279; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/524; C04B2235/5244; C04B2235/526; C04B2235/5264; C04B2235/5276; C04B2235/5296; C08K2201/00; C08K2201/016
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
173 words
A method for preparing a SiC whisker-reinforced composite material, comprising the steps of: preparing the fibrous base of a SiC whisker sponge-like cake by mixing a silica gel or ashed rice hulls, said silica gel or ashed rice hulls being a silicon source and containing 6.0 to 25.0% by weight of a water-soluble compound selected from the group consisting of Fe, Ni and Co, based on the Si content, with a furnace carbon black having an aggregated structure and a DBP absorption number of 50 ml/100 g or more as a carbonaceous material and with an additional amount of NaCl as a space forming agent, lightly packing the resultant mixture in a sealed reaction vessel, heating the mixture to a temperature of 1,300° to 1,700° C. in a nonoxidizing atmosphere, and burning away the residual carbonaceous material to obtain said fibrous base of said cake; and introducing a matrix material selected from the group consisting of a metal, an alloy and a plastic into the fibrous base of the SiC whisker sponge-like cake.
Claim 2
Independent Claim
173 words
A method for preparing a SiC whisker-reinforced composite material, comprising the steps of: preparing the fibrous base of a SiC whisker sponge-like cake by mixing a silica gel or ashed rice hulls, said silica gel or ashed rice hulls being a silicon source and containing 6.0 to 25.0% by weight of a water-soluble compound selected from the group consisting of Fe, Ni and Co, based on the Si content, with a furnace carbon black having an aggregated structure and a DBP absorption number of 50 ml/100 g or more as a carbonaceous material and with an additional amount of NaCl as a space forming agent, lightly packing the resultant mixture in a sealed reaction vessel, heating the mixture to a temperature of 1,300° to 1,700° C. in a nonoxidizing atmosphere, and burning away the residual carbonaceous material to obtain said fibrous base of said cake; and introducing a matrix material selected from the group consisting of a metal, an alloy and a plastic into the fibrous base of the SiC whisker sponge-like cake.
Claim 3
Dependent Claim
49 words
The method according to claim 1, wherein the fibrous base of the SiC whisker sponge-like cake comprises a cake wherein β-SiC single crystals each having a diameter of 0.2 to 1.0 μm and an aspect ratio of 100 or more are entangled with each other in a random manner.
Claim 4
Dependent Claim
29 words
The method according to claim 2, wherein the cake is compressed to have a bulk density of 0.03 to 1.9 g/cm 3 prior to introduction of said matrix material.
Claim 5
Dependent Claim
37 words
The method according to claim 1, wherein the mixing ratio of the silicon source to the carbonaceous material to the NaCl is within a range of 1 : 1.1 : 0.8 to 1 : 1.5 : 1.0.
Claim 6
Dependent Claim
38 words
The method according to claim 1, wherein the matrix material is at least one member selected from the group consisting of magnesium, aluminum, silicon, titanium, chromium, manganese, iron, cobalt, nickel, copper, zinc, silver, tantalum, tungsten, and alloys thereof.
Claim 7
Dependent Claim
37 words
The method according to claim 1, wherein the matrix material is at least one member selected from the group consisting of an epoxy resin, a polyester resin, a phenol resin, a polyimide resin, and a urea resin.
Claim 8
Dependent Claim
36 words
The method according to claim 1, wherein after the matrix material is introduced into the fibrous base of the SiC whisker sponge-like cake, the sponge-like cake is compressed to have a desired volume fraction and shape.
References Cited (Backward Citations)
GB796792A
Cited
GB791567A
Cited
GB916577A
Cited
US3653851A
Cited
GB1254732A
Cited
GB1475193A
Cited
US4279289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |