Method for making composite material object by plastic processing
Assignee: Toyota Motor Corp
•
Filing: 1983-08-24
•
Granted: 1985-10-22
•
Expires: 2003-08-24
Abstract
Abstract First a reinforcing material mass is formed from a quantity of reinforcing material by binding it together with inorganic binder, and then this reinforcing material mass is compounded with matrix metal to form a composite material mass. Then the composite material mass is heated up so that the proportion of the matrix metal thereof which is in the liquid phase is at least 40%, and while still hot it is subjected to a plastic processing process to form the composite material object.
Inventors
- 👤 Kiyoshi Funatani
- 👤 Tadashi Donomoto
- 👤 Atsuo Tanaka
- 👤 Yoshiaki Tatematsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:31
CPC Classifications
B; B22; B22D; B22D19/00; B22D19/02; C; C22; C22C; C22C47/00; C22C47/02; C22C47/06; C22C47/08; F; F16; F16H; F16H63/00; F16H63/02; F16H63/30; F16H63/32; Y; Y10; Y10S; Y10S164/00; Y10S164/90
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
117 words
A method of forming an article of composite material of predetermined shape comprising the steps of: (a) forming a mass of reinforcing material bound with an inorganic binder; (b) compounding said reinforcing material mass in a matrix of metal by surrounding said bound reinforcing material with said metal in a molten state and applying pressure thereto, thereby forming a solid billet; (c) heating said billet to a degree sufficient to melt at least a portion of said matrix such that the percentage of matrix metal in the molten phase is at least 40 percent; (d) deforming said matrix billet by plastic processing under applied pressure to said predetermined shape; and (e) allowing said deformed billet to cool.
Claim 2
Independent Claim
117 words
A method of forming an article of composite material of predetermined shape comprising the steps of: (a) forming a mass of reinforcing material bound with an inorganic binder; (b) compounding said reinforcing material mass in a matrix of metal by surrounding said bound reinforcing material with said metal in a molten state and applying pressure thereto, thereby forming a solid billet; (c) heating said billet to a degree sufficient to melt at least a portion of said matrix such that the percentage of matrix metal in the molten phase is at least 40 percent; (d) deforming said matrix billet by plastic processing under applied pressure to said predetermined shape; and (e) allowing said deformed billet to cool.
Claim 3
Dependent Claim
37 words
A method for producing a composite material object according to claim 1, wherein the volume proportion of reinforcing material in said composite material mass, after step (b), is at least about 3% and less than about 60%.
Claim 4
Dependent Claim
32 words
A method for producing a composite material object according to claim 2, wherein the volume proportion of reinforcing material in said composite material mass, after step (b), is at least about 10%.
Claim 5
Dependent Claim
35 words
A method for producing a composite material object according to claim 2 or claim 3, wherein the volume proportion of reinforcing material in said composite material mass, after step (b), is less than about 40%.
Claim 6
Dependent Claim
18 words
A method for producing a composite material object according to claim 1, wherein the reinforcing material is fibrous.
Claim 7
Dependent Claim
39 words
A method for producing a composite material object according to claim 1, wherein the compression strength of the reinforcing material mass, after step (a), is greater than about 0.5 kg/cm 2 and is less than 20 kg/cm 2 .
Claim 8
Dependent Claim
32 words
A method for producing a composite material object according to claim 6, wherein the compression strength of the reinforcing material mass, after step (a), is greater than about 0.7 kg/cm 2 .
Claim 9
Dependent Claim
35 words
A method for producing a composite material object according to claim 6 or claim 7, wherein the compression strength of the reinforcing material mass, after step (a), is less than about 15 kg/cm 2 .
Claim 10
Dependent Claim
40 words
A method for producing a composite material object according to claim 1, wherein the inorganic binder used in step (a) is selected from the group consisting of silica, alumina, zirconia, chromia, ceria, zirconia silicate, ferric oxide, aluminum phosphate, and waterglass.
Claim 11
Dependent Claim
34 words
A method for producing a composite material object according to claim 1, wherein the method used in step (b) for compounding the reinforcing material and the matrix metal is the high pressure casting method.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |