Melt fed blending process
Assignee: General Electric Co
•
Filing: 1983-09-01
•
Granted: 1985-10-15
•
Expires: 2003-09-01
Abstract
Abstract A method is provided for producing thermoplastic polymer blends with the exposure of blend constituents to extreme blending conditions minimized by melting the thermoplastic polymers and adjusting their viscosity and elasticity values, through control of their melt temperatures, prior to blending. Where the viscosity and elasticity values are adjusted properly, the desired thermoplastic polymer blend can be produced with a minimum effort.
Inventors
- 👤 Joseph C. Golba, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:40
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/54; B; B29; B29C; B29C48/00; B29C48/25; B29C48/36; B29C48/375; B29C48/38; C08J; C08J3/00; C08J3/005; B29C48/03
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
79 words
A process for producing thermoplastic polymer blends comprising: a. separately melting two or more compositions, each containing a major portion of one of said thermoplastic polymers to form a uniform melt thereof; and b. subsequently blending the resulting melts to form a uniform admixture of melts under conditions where the viscosity and elasticity values of the compositions are in a ratio within the range of about 1:1 to about 1:3 during initial blending of the admixture of the melts.
Claim 2
Dependent Claim
79 words
A process for producing thermoplastic polymer blends comprising: a. separately melting two or more compositions, each containing a major portion of one of said thermoplastic polymers to form a uniform melt thereof; and b. subsequently blending the resulting melts to form a uniform admixture of melts under conditions where the viscosity and elasticity values of the compositions are in a ratio within the range of about 1:1 to about 1:3 during initial blending of the admixture of the melts.
Claim 3
Dependent Claim
41 words
A process as in claim 1 wherein the viscosity values and elasticity values for the compositions are in ratios within the range of 1:1 to 1:3 during the initial blending, by adjusting the melt temperatures of said composition prior to blending.
Claim 4
Dependent Claim
30 words
A process as in claim 2 wherein the melt temperatures are adjusted to provide viscosity values for the compositions as measured in a shear deformational mode that are about equal.
Claim 5
Dependent Claim
30 words
A process as in claim 2 wherein the melt temperatures are adjusted to provide viscosity values for the compositions as measured in an extensional deformational mode that are about equal.
Claim 6
Dependent Claim
30 words
A process as in claim 2 wherein the melt temperatures are adjusted to provide elasticity values for the compositions as measured in a shear deformational mode that are about equal.
Claim 7
Dependent Claim
30 words
A process as in claim 2 wherein the melt temperatures are adjusted to provide elasticity values for the compositions as measured in an extensional deformational mode that are about equal.
Claim 8
Dependent Claim
30 words
A process as in claim 1 comprising the additional step of separately pre-blending one or more of the melted compositions prior to blending said compositions to form a uniform admixture.
Claim 9
Dependent Claim
90 words
A process for producing polyolefin/poly(2,6-dimethyl 1,4-phenylene oxide) blends which comprises: a. melting a primary composition comprising poly(2,6-dimethyl 1,4-phenylene oxide) to form a uniform melt thereof; b. melting a secondary composition comprising at least one polyolefin to form a uniform melt thereof; c. blending said molten primary composition and said molten secondary composition under conditions wherein the viscosity values and elasticity values of said primary and secondary composition are in a ratio in the range of about 1:1 to about 1:3 during initial blending of the molten primary and secondary compositions.
Claim 10
Dependent Claim
90 words
A process for producing polyolefin/poly(2,6-dimethyl 1,4-phenylene oxide) blends which comprises: a. melting a primary composition comprising poly(2,6-dimethyl 1,4-phenylene oxide) to form a uniform melt thereof; b. melting a secondary composition comprising at least one polyolefin to form a uniform melt thereof; c. blending said molten primary composition and said molten secondary composition under conditions wherein the viscosity values and elasticity values of said primary and secondary composition are in a ratio in the range of about 1:1 to about 1:3 during initial blending of the molten primary and secondary compositions.
Claim 11
Dependent Claim
55 words
A process as in claim 8 wherein the viscosity values and elasticity values of said molten primary composition and said molten secondary composition are in a ratio within the range of about 1:1 to about 1:3 by independently adjusting the melt temperature of said molten primary composition and said molten secondary composition prior to blending.
Claim 12
Dependent Claim
44 words
A process as in claim 9 wherein the melt temperature of said molten primary composition and the melt temperature of said molten secondary composition are maintained at values wherein elasticity values as measured in a shear deformational mode form a ratio of about 1:1.
Claim 13
Dependent Claim
45 words
A process as in claim 10 wherein the melt temperature of said molten primary composition and the melt temperature of said molten secondary composition are maintained at values wherein viscosity values as measured in a shear deformational mode are in a ratio of about 1:1.
Claim 14
Dependent Claim
32 words
A process as in claim 8 wherein said molten primary composition comprises poly(2,6-dimethyl-1,4phenylene oxide), styrene-ethylene-butylene triblock copolymer thermoplastic elastomers, and aryl phosphate esters and said secondary composition comprises a low density polyethylene.
Claim 15
Dependent Claim
34 words
A process as in claim 8 wherein said molten primary composition comprises poly(2,6-dimethyl-1,4phenylene oxide) and aryl phosphate esters and said molten secondary composition comprises a low density polyethylene and styrene-ethylene-butylene triblock copolymer thermoplastic elastomers.
Claim 16
Dependent Claim
47 words
A process as in claim 9 wherein the melt temperature of said molten secondary composition is adjusted to a value within the range of about 270°-400° F. and the melt temperature of said molten primary composition is adjusted to a value within the range of 500°-550° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |