Heat-shrinkable laminate film
Assignee: Kureha Corp
•
Filing: 1982-11-05
•
Granted: 1985-10-15
•
Expires: 2002-11-05
Abstract
Abstract Disclosed herein is a heat-shrinkable laminate film excellent in gas-barrier property and oil-resistance and heat-sealing resistance, comprising a core layer of a gas-barrier resin which is a copolymer of vinylidene chloride or a copolymer of ethylene and vinyl alcohol, the outer layer (A) of a resin which is a copolymer (I) of ethylene and alpha-olefine having specific gravity of 0.900 to 0.950 and of a crystal melting point of 110° to 130° C. or a mixture of more than 20% by weight of the copolymer (I) and less than 80% by weight of a copolymer (II) of ethylene and vinyl acetate having crystal melting point of 80° to 103° C., the other outer layers (B) of a resin which is a cross-linked material formed from a polymer selected from the group consisting of the copolymer (I), the copolymer (II) and mixture of the copolymer (I) and the copolymer (II) by exposing the polymer to an ionizing irradiation, and two adhesive layers disposed between the core layer and the outer layers (A) and (B).
Inventors
- 👤 Masaki Ohya
- 👤 Yoshiharu Nishimoto
- 👤 Kengo Yamazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:34
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B29; B29C; B29C61/00; B29C61/06; B29C61/0608; B29C61/0616; B32B27/30; B32B27/304; B32B27/306; B32B27/32; B32B38/00; B32B38/0008; C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815; C08L23/0846; C08L23/0853; C09; C09D; C09D123/00; C09D123/02; C09D123/04; C09D123/08; C09D123/0846; C09D123/0853; B29K; B29K2023/00; B29K2023/04; B29K2023/08; B29K2023/083; B29K2027/00; B29K2105/00; B29K2105/04; B29K2105/045; B29K2995/00; B29K2995/0037; B29K2995/0058; B29K2995/0065; B32B2250/00; B32B2250/24; B32B2307/00; B32B2307/70; B32B2307/724; B32B2307/7242; B32B2307/732; B32B2307/734; B32B2307/736; C08L2205/00; C08L2205/02; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10S428/913; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192; Y10T428/31928
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
185 words
A heat-shrinkable laminated film excellent in gas-barrier property and oil-resistance and heat-sealing resistance, comprising: a core layer of a gas-barrier resin which is a copolymer of vinylidene chloride or a copolymer of ethylene and vinyl alcohol, an outer layer (A) of a resin which is a copolymer (I) of ethylene and an alpha-olefin of 4 to 18 carbon atoms and having a specific gravity of 0.900 to 0.950 and a crystal melting point of 110° to 130° C. or a mixture of more than 20% by weight of the copolymer (I) and less than 80% by weight of a copolymer (II) of ethylene and vinyl acetate having a crystal melting point of 80° to 103° C., another outer layer (B) of a resin which is a cross-linked material formed from a polymer selected from the group consisting of the copolymer (I), the copolymer (II) and a mixture of the copolymer (I) and the copolymer (II) by exposing the polymer to an ionizing irradiation, and two adhesive layers each adhesive layer being disposed between the core layer and one of the outer layers (A) and (B).
Claim 2
Dependent Claim
185 words
A heat-shrinkable laminated film excellent in gas-barrier property and oil-resistance and heat-sealing resistance, comprising: a core layer of a gas-barrier resin which is a copolymer of vinylidene chloride or a copolymer of ethylene and vinyl alcohol, an outer layer (A) of a resin which is a copolymer (I) of ethylene and an alpha-olefin of 4 to 18 carbon atoms and having a specific gravity of 0.900 to 0.950 and a crystal melting point of 110° to 130° C. or a mixture of more than 20% by weight of the copolymer (I) and less than 80% by weight of a copolymer (II) of ethylene and vinyl acetate having a crystal melting point of 80° to 103° C., another outer layer (B) of a resin which is a cross-linked material formed from a polymer selected from the group consisting of the copolymer (I), the copolymer (II) and a mixture of the copolymer (I) and the copolymer (II) by exposing the polymer to an ionizing irradiation, and two adhesive layers each adhesive layer being disposed between the core layer and one of the outer layers (A) and (B).
Claim 3
Dependent Claim
33 words
A heat-shrinkable laminated film according to claim 1, wherein said outer layer (B) is made of a cross-linked material formed from the copolymer (II) by exposing the copolymer (II) to an ionizing irradiation.
Claim 4
Dependent Claim
34 words
A heat-shrinkable laminated film according to claim 1, wherein said outer layer (B) is made of a cross-linked material formed from the copolymer (I) by exposing the copolymer (I) to an ionizing irradiation thereof.
Claim 5
Dependent Claim
51 words
A heat-shrinkable laminated film according to claim 1, wherein said outer layer (B) is made of a cross-linked material formed from a mixture of 20 to 70% by weight of the copolymer (I) and 80 to 30% by weight of the copolymer (II) by exposing the mixture to an ionizing irradiation.
Claim 6
Dependent Claim
87 words
A heat-shrinkable laminated film according to claim 1, wherein said copolymer (II) forming the outer layer (B) is selected from the group having a relationship between the content (% by weight) of vinyl acetate units of the copolymer and the melt-index (g/10 min) thereof falling in the heptagonal range made of the seven points A(3, 0.2), B(12, 0.2), C(12, 0.5), D(9, 0.5), E(5, 2.0), F(5, 4.0) and G(3, 4.0) on a plane having said content of vinyl acetate as the abscissa and said melt-index as the ordinate.
Claim 7
Dependent Claim
30 words
A heat-shrinkable laminated film according to any one of claim 1 wherein said adhesive layer is selected from poly-olefin modified by carboxylic acid and copolymers of ethylene and vinyl acetate.
Claim 8
Dependent Claim
22 words
The heat-shrinkable laminate film according to claim 1 which has been biaxially stretched after layer (B) is laminated to the other layers.
References Cited (Backward Citations)
FR1548820A
Cited
US3617419A
Cited
US3741253A
Cited
CA982923A
Cited
US4044187B1
Cited
US4044187A
Cited
US4064296A
Cited
JPS5413582A
Cited
FR2450205A1
Cited
EP0022184A1
Cited
EP0032027A2
Cited
US4424243A
Cited
US4391862A
Cited
US4357376A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |