Abstract
Abstract A carbon resistive paste comprising an electrically conductive component, such as carbon; an inorganic filler, such as silica; a resin component, such as an epoxy resin; a solvent, such as ethanol and; if necessary, an organic filler, wherein the inorganic filler is treated with a silane coupling agent, such as γ-glycidoxypropyltrimethoxy silane. The carbon resistive paste provides a resistive film which has limited changes in resistance value in use and is superior in strength.
Inventors
- 👤 Tohru Kasanami
- 👤 Hirozi Tani
- 👤 Tsutomu Yokoi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 05:23
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/0652; H01C17/06573; H01C17/0658
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
53 words
In a carbon resistive paste for producing a carbon resistive film of high film strength upon application of said paste to a substrate and baking it, said paste containing an electrically conductive carbon component, an inorganic filler and a resin component, the improvement comprising an inorganic filler treated with a silane coupling agent.
Claim 2
Dependent Claim
53 words
In a carbon resistive paste for producing a carbon resistive film of high film strength upon application of said paste to a substrate and baking it, said paste containing an electrically conductive carbon component, an inorganic filler and a resin component, the improvement comprising an inorganic filler treated with a silane coupling agent.
Claim 3
Dependent Claim
54 words
A carbon resistive paste comprising carbon or a mixture of carbon and graphite as an electrically conductive component, a resin component, a solvent and an inorganic filler treated with a silane coupling agent wherein a resistive film of high film strength is obtained upon application of said paste to a substrate and baking it.
Claim 4
Dependent Claim
54 words
A carbon resistive paste comprising carbon or a mixture of carbon and graphite as an electrically conductive component, a resin component, a solvent and an inorganic filler treated with a silane coupling agent wherein a resistive film of high film strength is obtained upon application of said paste to a substrate and baking it.
Claim 5
Dependent Claim
29 words
The paste of claim 2, wherein the silane coupling agent is selected from the group consisting of β-(3,4-epoxycyclohexyl)ethyltrimethoxy silane, γ-glycidoxypropyltrimethoxy silane, N-β-(aminoethyl)-γ-aminopropyltrimethoxy silane, N-β-(aminoethyl)- γ-aminopropylmethyldimethoxy silane, and γ-mercaptopropyltrimethoxy silane.
Claim 6
Dependent Claim
35 words
The paste of claim 2, wherein the inorganic filler is selected from the group consisting of silica, alumina, glass, talc, clay, aluminum hydroxide, asbestos, titanium dioxide, zinc white, boron nitride, calcium carbonate, and calcium silicate.
Claim 7
Dependent Claim
19 words
The paste of claim 2, wherein the inorganic filler is talc and the silane coupling agent is γ-glycidoxypropyltrimethoxy silane.
Claim 8
Dependent Claim
41 words
The paste of claim 2, wherein the resin component is selected from the group consisting of an epoxy resin, a phenol resin, a urethane resin, a melamine resin, a polyimide resin, a diallyl phthalate resin, ethylenepropylene-diene terpolymer and styrene butadiene rubber.
Claim 9
Dependent Claim
41 words
The paste of claim 2, wherein the solvent is selected from the group consisting of ethanol, methanol, toluene, ethyl ether, terpineol, diethylene glycol monoethyl ether, ethylene glycol diacetate, benzyl alcohol, diacetone alcohol, m-cresol, methyl cellosolve, methyl cellosolve acetate and butyl cellosolve.
Claim 10
Dependent Claim
11 words
A carbon resistive film produced from the paste of claim 2.
Claim 11
Dependent Claim
68 words
A process for the preparation of a carbon resistive paste for use in the production of carbon resistive films comprising treating an inorganic filler with a solvent solution of a silane coupling agent, drying and heating the resulting mixture, and then mixing the dried and treated filler with carbon or carbon and graphite as an electrically conductive component, a resin component and a solvent to form a paste.
Claim 12
Dependent Claim
68 words
A process for the preparation of a carbon resistive paste for use in the production of carbon resistive films comprising treating an inorganic filler with a solvent solution of a silane coupling agent, drying and heating the resulting mixture, and then mixing the dried and treated filler with carbon or carbon and graphite as an electrically conductive component, a resin component and a solvent to form a paste.
Claim 13
Dependent Claim
22 words
The process of claim 9 wherein the ratio of inorganic filler to silane coupling agent-containing solution is from about 1/1 to 1/4.
References Cited (Backward Citations)
US3002862A
Cited
US2991257A
Cited
US3742423A
Cited
US3342752A
Cited
US3547834A
Cited
US3682839A
Cited
US3686139A
Cited
US3711428A
Cited
US4001128A
Cited
US4451537A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-14 | 1989-04-15 | 1989-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-14 | 1993-04-15 | 1993-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-14 | 1997-04-15 | 1997-10-15 | $7700.00 | Window Closed / Lapsed |