Polyimide compositions and foams and methods of making same
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1985-02-25
•
Granted: 1985-10-08
•
Expires: 2005-02-25
Abstract
Abstract Methods of making modified polyimide compositions and the resulting compositions. A polyimide forming material is prepared by treating an aromatic dianhydride with an esterifying solvent, then adding a suitable diamine. In order to obtain a foam which is non-friable and resistant to repeated compressive forces, the selected diamine must contain an aliphatic moiety in the chain. This material is dried to a powder or film. A foam is produced by heating the material to reaction temperature for a period sufficient to produce a stable foam. The material melts, then spontaneously expands into a foam which becomes self supporting and cures to a resilient, flexible non-friable foam.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:13
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1025; C08G73/1028; C08G73/1032; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
116 words
In the method of making a polyimide precursor composition suitable for use in the manufacture of non-friable polyimide foams, which comprises the steps of esterifying an aromatic dianhydride with an esterifying solvent of produce a half-ester and reacting said half-ester with a diamine to produce a polyimide precursor composition; the improvement wherein: said diamine consists of a mixture of at least one aromatic-aliphatic diamine and from 0.1 to 50 mole % of at least one aliphatic diamine; said aromatic-aliphatic diamine having the general formula: ##STR2## wherein x is a positive integer from 1 to 20; and said aliphatic diamine has the general formula: H.sub.2 N═(CH.sub.2).sub.y ═NH.sub.2 wherein y is a positive integer from 2 to 12.
Claim 2
Dependent Claim
116 words
In the method of making a polyimide precursor composition suitable for use in the manufacture of non-friable polyimide foams, which comprises the steps of esterifying an aromatic dianhydride with an esterifying solvent of produce a half-ester and reacting said half-ester with a diamine to produce a polyimide precursor composition; the improvement wherein: said diamine consists of a mixture of at least one aromatic-aliphatic diamine and from 0.1 to 50 mole % of at least one aliphatic diamine; said aromatic-aliphatic diamine having the general formula: ##STR2## wherein x is a positive integer from 1 to 20; and said aliphatic diamine has the general formula: H.sub.2 N═(CH.sub.2).sub.y ═NH.sub.2 wherein y is a positive integer from 2 to 12.
Claim 3
Dependent Claim
25 words
The improvement according to claim 1 further including the steps of drying said polyimide precursor composition and pulverizing the resulting dry material to a powder.
Claim 4
Dependent Claim
36 words
The improvement according to claim 2 further including the step of heating said powder to cause melting and foaming of said powder as the polymerization reaction is completed whereby a resilient, non-friable, flame resistant foam results.
Claim 5
Dependent Claim
35 words
The improvement according to claim 3 wherein said heating is accomplished in an oven heated to a temperature of from about 120° to 320° C. for a period of from about 10 to 60 minutes.
Claim 6
Dependent Claim
18 words
The improvement according to claim 3 wherein said heating is accomplished by exposing the powder to microwave energy.
Claim 7
Dependent Claim
40 words
The improvement according to claim 1 wherein said solvent is either an aliphatic alcohol having up to 7 carbon atoms, or an aromatic alcohol, or either alcohol with either a halogen or amino substitution, or a mixture of such alcohols.
Claim 8
Dependent Claim
21 words
The improvement according to claim 6 wherein said aromatic-aliphatic diamine is 4,4'-diamino diphenyl methane and said aliphatic diamine is 1,6-diamino hexane.
Claim 9
Dependent Claim
19 words
The improvement according to claim 1 further including the step of drying said polyimide precursor composition by spray drying.
Claim 10
Dependent Claim
16 words
The improvement according to claim 1 wherein "x" is a positive integer from 1 to 3.
Claim 11
Dependent Claim
20 words
The improvement according to claim 1 wherein the NH 2 radicals are each in the meta rather than para position.
References Cited (Backward Citations)
US30213A
Cited
US3726834A
Cited
US3793281A
Cited
US3966652A
Cited
USRE30213E
Cited
US4070312A
Cited
US4315080A
Cited
US4315077A
Cited
US4346182A
Cited
US4426463A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-07 | 1989-04-08 | 1989-10-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-07 | 1993-04-08 | 1993-10-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-07 | 1997-04-08 | 1997-10-08 | $7700.00 | Window Closed / Lapsed |