Conductive elastomers from electrically conductive fibers in silicone emulsion

Claim 2

A silicone composition which provides an elastomeric electrically conductive product upon removal of the water under ambient conditions comprising (A) an emulsion of a dispersed phase of silicone elastomer, and a continuous phase of water containing a material selected from the group comprising colloidal silica, alkali metal silicates, and organosilicates, said emulsion being an aqueous oil-in-water emulsion, having at least 20 percent by weight water, that cures upon drying at ambient temperature to an elastomeric film, and (B) from 10 to 25 parts by weight of electrically conductive particles in the form of fibers having a diameter of less than 25 micrometers and a length of less than 10 millimeters with the ratio of length to diameter of greater than 10:1, said particles being selected from the group consisting of graphite, stainless steel, and metal-coated graphite fibers where the metal coating is silver, gold, or nickel, based upon 100 parts by weight of non-volatile material in (A), the composition yielding an elastic product, obtained by drying the composition at room temperature, comprising dispersed particles of elastomer and electrically conducting fibers in a solid polar continuous phase, and having a surface resistivity of less than 2 ohms per square on at least one surface.

Claim 3

The composition of claim 1 in which the electrically conductive particles are present in an amount of from 10 to 25 parts by weight and are nickel-coated graphite fibers having an average diameter of from about 5 to 15 micrometers and a length of from about 1 to 5 mm.

Claim 4

The composition of claim 2 in which the nickel-coated graphite fibers have a silane coating.

Claim 5

The composition of claim 1 in which the emulsion (A) is a silicone emulsion suitable to provide an elastomeric product upon removal of the water under ambient conditions comprising a continuous aqueous phase and a dispersed phase, the dispersed phase consisting essentially of an anionically stabilized hydroxylated polydiorganosiloxane which contains about 2 silicon-bonded hydroxyl radicals per molecule, an organic tin compound, and a colloidal silica, said silicone emulsion having a pH in a range of 9 to 11.5 inclusive.

Claim 6

The composition of claim 4 in which the polydiorganosiloxane is a polydimethylsiloxane having a weight average molecular weight in a range of 200,000 to 700,000, the colloidal silica is present in a amount of from 1 to 25 parts by weight for each 100 parts by weight of polydimethylsiloxane, and the organic tin compound is a diorganotindicarboxylate present in an amount of from 0.1 to 2 parts by weight for each 100 parts by weight of the polydimethylsiloxane.

Claim 7

The composition of claim 1 in which the elastomer of emulsion (A) comprises a graft copolymer of hydroxyl endblocked polydiorganosiloxane and an alkali metal silicate, the silicone emulsion having a pH within the range from 8.5 to 12 inclusive.

Claim 8

The composition of claim 6 in which the hydroxyl endblocked polydiorganosiloxane is a polydimethylsiloxane having an average molecular weight in a range of 200,000 to 700,000, the alkali metal silicate is a sodium silicate employed in an amount of from 0.3 to 30 parts by weight for each 100 parts by weight of polydimethylsiloxane, and there is also present an organic tin salt.

Claim 9

The composition of claim 7 in which the organic tin salt is a diorganotindicarboxylate present in an amount of from 0.1 to 2 parts by weight for each 100 parts by weight of polydimethylsiloxane.

Claim 10

The composition of claim 1 in which the emulsion (A) comprises the emulsion produced by a process comprising emulsifying (C) a vinyl endblocked polydiorganosiloxane and (D) an organosilicon compound having silicon-bonded hydrogen atoms using water and surfactant to form an emulsion, adding a platinum catalyst and heating the emulsion to form a dispersed phase of cross-linked silicone elastomer, then adding colloidal silica.

Claim 11

The composition of claim 9 in which the vinyl endblocked polydiorganosiloxane (C) is a polydiorganosiloxane terminated by triorganosiloxy groups and having two vinyl radicals per molecule, no silicon atom having more than one vinyl radical bonded thereto, the remaining organic radicals being selected from the group consisting of methyl, ethyl, phenyl, and 3,3,3-trifluoropropyl radicals, at least 50 percent of the organic radicals being methyl radicals, and said polydiorganosiloxane having a viscosity of from 0.1 to 100 Pa's at 25° C., and the organosilicon compound (D) is a mixture of silicon compounds providing from 0.75 to 1.50 silicon-bonded hydrogen atoms per vinyl radical of (C), said mixture (D) consisting essentially of (1) an organosiloxane compound containing two silicon-bonded hydrogen atoms per molecule and the organic radicals being selected from the group consisting of alkyl radicals having from 1 to 12 carbon atoms inclusive, phenyl and 3,3,3-trifluoropropyl, no silicon atom having bonded thereto more than one silicon-bonded hydrogen atom, and said organosiloxane compound (1) having no more than 500 silicon atoms per molecule, and (2) an organosiloxane compound containing at least 3 silicon-bonded hydrogen atoms per molecule, the organic radicals being selected from the group consisting of alkyl radicals having from 1 to 12 carbon atoms inclusive, phenyl and 3,3,3-trifluoropropyl radicals, no silicon atom having bonded thereto more than one silicon-bonded hydrogen atom, and said organosiloxane compound (2) having no more than 75 silicone atoms per molecule, said mixture (D) being such that at least 10 percent of the silicon-bonded hydrogen atoms are derived from (1) and at least 10 percent of the silicon-bonded hydrogen atoms are derived from (2), (1) and (2) composing 100 weight percent of mixture (D).

Claim 12

The composition of claim 1 in which the emulsion (A) comprises an emulsion prepared by (E) first forming a stabilized dispersion of hydroxyl endblocked polydiorganosiloxane containing sufficient vinyl substituted siloxane units to facilitate the crosslinking of the polydiorganosiloxane and having a weight average molecular weight of at least 5000 and then, (F) treating the dispersion to provide a crosslinking action by forming radicals within the dispersed polydiorganosiloxane, then adding colloidal silica.

Claim 13

The composition of claim 10 in which the radicals are formed within the dispersed polydiorganosiloxane by exposing the dispersion to high energy radiation.

Claim 14

The composition of claim 11 in which the radicals are formed within the dispersed polydiorganosiloxane by the combined action of heat and a radical-producing agent.

Claim 15

The composition of claim 11 in which the polydiorganosiloxane is a copolymer containing dimethylsiloxane units and methylvinylsiloxane units, the copolymer having a weight average molecular weight of 200,000 to 700,000.

Claim 16

The elastomeric, electrically conductive product produced by drying the composition of claim 1.

Claim 17

The elastomeric, electrically conductive product produced by drying the composition of claim 4.

Claim 18

The elastomeric, electrically conductive product produced by drying the composition of claim 6.

Claim 19

The elastomeric, electrically conductive product produced by drying the composition of claim 9.

Claim 20

The elastomeric, electrically conductive product produced by drying the composition of claim 11.