Sodium higher fatty alkyl sulfate detergent laundry bars and process for manufacture thereof
Assignee: Colgate Palmolive Co
•
Filing: 1983-08-17
•
Granted: 1985-09-24
•
Expires: 2003-08-17
Abstract
Abstract A detergent laundry bar, based on sodium higher fatty alcohol sulfate, which is resistant to breakage on handling, includes sodium higher fatty alcohol sulfate in which the higher fatty alcohol is of about 10 to 18 carbon atoms, water soluble builder salt for the sodium higher fatty alcohol sulfate, water insoluble particulate material which may also possess building properties, water and a higher fatty acid of 10 to 18 carbon atoms, with the proportion of higher fatty acid being such as to aid in overcoming the tendency of such laundry bars to crack, chip and break on handling. The water soluble builder salt will normally include an inorganic phosphate builder salt, such as sodium tripolyphosphate, and the water insoluble particulate material will normally include calcium carbonate and/or bentonite, and/or talc, usually being constituted of two or three of such materials. Preferably a higher fatty acid alkanolamide and a higher fatty alcohol will also be present. Also described is a process for manufacturing such detergent laundry bars, which process includes milling and plodding operations.
Inventors
- 👤 Gregorio C. Gervasio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:41
CPC Classifications
C; C11; C11D; C11D3/00; C11D3/16; C11D3/20; C11D3/2003; C11D3/2006; C11D3/201; C11D3/2013; C11D1/00; C11D1/02; C11D1/12; C11D1/14; C11D1/146; C11D17/00; C11D17/0047; C11D17/0065; C11D17/0069; C11D3/02; C11D3/04; C11D3/06; C11D3/2075; C11D3/2079
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
110 words
A detergent laundry bar which is based on sodium higher fatty alcohol sulfate and which is resistant to breaking on storage and handling which comprises from 10 to 35% of sodium higher fatty alcohol sulfate having about 10 and 18 carbon atoms, 2 to 30% of water soluble inorganic phosphate builder salt for the sodium higher fatty alcohol sulfate, 20 to 60% of finely divided, water insoluble, inorganic, particulate material, 0 to 15% of non-phosphate water soluble salt selected from the group consisting of builder salt, filler salt and mixtures thereof, 7 to 16% of moisture and 1 and 10% of higher fatty acid of 10 to 18 carbon atoms.
Claim 2
Dependent Claim
110 words
A detergent laundry bar which is based on sodium higher fatty alcohol sulfate and which is resistant to breaking on storage and handling which comprises from 10 to 35% of sodium higher fatty alcohol sulfate having about 10 and 18 carbon atoms, 2 to 30% of water soluble inorganic phosphate builder salt for the sodium higher fatty alcohol sulfate, 20 to 60% of finely divided, water insoluble, inorganic, particulate material, 0 to 15% of non-phosphate water soluble salt selected from the group consisting of builder salt, filler salt and mixtures thereof, 7 to 16% of moisture and 1 and 10% of higher fatty acid of 10 to 18 carbon atoms.
Claim 3
Dependent Claim
114 words
A detergent laundry bar which is based on sodium higher fatty alcohol sulfate and which is resistant to breakage on storage and handling which comprises from 10 to 35% of sodium higher fatty alcohol sulfate of about 10 to 18 carbon atoms, 2 to 30% of sodium tripolyphosphate, 20 to 60% of finely divided, water insoluble, inorganic, particulate material selected from the group consisting of calcium carbonate, bentonite, talc, and mixtures thereof, 0 to 15% of non-phosphate water soluble salt selected from the group consisting of sodium carbonate, sodium silicate, sodium sulfate and mixtures thereof, 7 to 16% of moisture and 1 to 10% of higher fatty acid of 12 to 14 carbon atoms.
Claim 4
Dependent Claim
114 words
A detergent laundry bar which is based on sodium higher fatty alcohol sulfate and which is resistant to breakage on storage and handling which comprises from 10 to 35% of sodium higher fatty alcohol sulfate of about 10 to 18 carbon atoms, 2 to 30% of sodium tripolyphosphate, 20 to 60% of finely divided, water insoluble, inorganic, particulate material selected from the group consisting of calcium carbonate, bentonite, talc, and mixtures thereof, 0 to 15% of non-phosphate water soluble salt selected from the group consisting of sodium carbonate, sodium silicate, sodium sulfate and mixtures thereof, 7 to 16% of moisture and 1 to 10% of higher fatty acid of 12 to 14 carbon atoms.
Claim 5
Dependent Claim
61 words
A laundry bar according to claim 2 which comprises from 2 to 10% of higher fatty acid alkanolamide of higher fatty acid of 10 to 18 carbon atoms and of alkanol of 2 to 3 carbon atoms, and wherein the finely divided water insoluble, inorganic particulate material includes from 10 to 40% of calcium carbonate and 2 to 10% of talc.
Claim 6
Dependent Claim
79 words
A laundry bar according to claim 3 which comprises from 20 to 30% of sodium lauryl sulfate, 5 to 15% of sodium tripolyphosphate, 10 to 30% of calcium carbonate, 5 to 20% of bentonite, 3 to 8% of higher fatty acid, 3 to 8% of higher fatty acid alkanolamide, 2 to 8% of sodium silicate of Na 2 O:SiO 2 ratio in the range of 1:1.6 to 1:3, 3 to 8% of talc, and 9 to 14% of moisture.
Claim 7
Dependent Claim
85 words
A laundry bar according to claim 4 which comprises about 25% of sodium lauryl sulfate, about 9% of high phase I content sodium tripolyphosphate, about 19% of calcium carbonate, about 12% of bentonite, about 5% of talc, about 5% of coco fatty acids and/or palm kernel fatty acids, about 5% of cocomonoethanolamide, about 4% of sodium silicate of Na 2 O:SiO 2 ratio of about 1:2, about 1% of lauryl alcohol, about 2% of sodium sulfate, about 12% of moisture and about 1% of adjuvants.
Claim 8
Dependent Claim
88 words
A process for manufacturing a detergent laundry bar based on sodium higher fatty alcohol sulfate so as to make it resistant to breakage on storage and handling which comprises adding a higher fatty acid of 10 to 18 carbon atoms to a mixture of sodium higher fatty alcohol sulfate in which the higher fatty alcohol is of about 10 to 18 carbon atoms, water soluble builder salt for the sodium higher fatty alcohol sulfate, water insoluble, inorganic particulate material and water, milling, plodding, extruding and cutting the mixture.
Claim 9
Dependent Claim
88 words
A process for manufacturing a detergent laundry bar based on sodium higher fatty alcohol sulfate so as to make it resistant to breakage on storage and handling which comprises adding a higher fatty acid of 10 to 18 carbon atoms to a mixture of sodium higher fatty alcohol sulfate in which the higher fatty alcohol is of about 10 to 18 carbon atoms, water soluble builder salt for the sodium higher fatty alcohol sulfate, water insoluble, inorganic particulate material and water, milling, plodding, extruding and cutting the mixture.
Claim 10
Dependent Claim
133 words
A process according to claim 6 which comprises adding 1 to 10 parts of the higher fatty acid to a mixture of 10 to 35 parts of sodium higher fatty alcohol sulfate wherein the higher fatty alcohol is of about 10 to 18 carbon atoms, 2 to 30 parts of water soluble inorganic phosphate builder salt for the sodium higher fatty alcohol sulfate, 20 to 60 parts of finely divided, water insoluble, inorganic particulate material, 0 to 15 parts of non-phosphate water soluble builder and/or filler salt, and enough water so that the laundry bar will contain from 7 to 16% of moisture, mixing such materials, milling the mixture to ribbon or chip form, plodding the ribbons or chips resulting, extruding the plodded material into bar form and cutting the bar to lengths.
Claim 11
Dependent Claim
176 words
A process for manufacturing a detergent laundry bar based on sodium higher fatty alcohol sulfate so as to make it resistant to breakage on storage and handling, which comprises adding 1 to 10 parts of a higher fatty acid of 10 to 14 carbon atoms to a mixture of 10 to 35 parts of sodium higher fatty alcohol sulfate wherein the higher fatty alcohol is of about 10 to 18 carbon atoms, 2 to 30 parts of sodium tripolyphosphate, 20 to 60 parts of finely divided, inorganic, water insoluble particulate material which is selected from the group consisting of calcium carbonate, bentonite, talc and mixtures thereof, 0 to 15 parts of non-phosphate water soluble salt selected from the group consisting of sodium carbonate, sodium silicate, sodium sulfate and mixtures thereof, and enough water so that the laundry bar will contain from 7 to 16% of moisture, mixing such materials, milling the mixture to ribbon or chip form, plodding the ribbons or chips resulting, extruding the plodded material into bar form and cutting the bar to lengths.
Claim 12
Dependent Claim
176 words
A process for manufacturing a detergent laundry bar based on sodium higher fatty alcohol sulfate so as to make it resistant to breakage on storage and handling, which comprises adding 1 to 10 parts of a higher fatty acid of 10 to 14 carbon atoms to a mixture of 10 to 35 parts of sodium higher fatty alcohol sulfate wherein the higher fatty alcohol is of about 10 to 18 carbon atoms, 2 to 30 parts of sodium tripolyphosphate, 20 to 60 parts of finely divided, inorganic, water insoluble particulate material which is selected from the group consisting of calcium carbonate, bentonite, talc and mixtures thereof, 0 to 15 parts of non-phosphate water soluble salt selected from the group consisting of sodium carbonate, sodium silicate, sodium sulfate and mixtures thereof, and enough water so that the laundry bar will contain from 7 to 16% of moisture, mixing such materials, milling the mixture to ribbon or chip form, plodding the ribbons or chips resulting, extruding the plodded material into bar form and cutting the bar to lengths.
Claim 13
Dependent Claim
66 words
A process according to claim 8 wherein the mixture comprises from 2 to 10 parts of higher fatty acid alkanolamide of higher fatty acid of 10 to 14 carbon atoms and alkanol of 2 to 3 carbon atoms and wherein the finely divided water insoluble, inorganic particulate material in the mixture includes 10 to 40 parts of calcium carbonate and 2 to 10 parts of talc.
Claim 14
Dependent Claim
98 words
A process according to claim 9 wherein the milling is by a multi-rolled mill and the plodding is by a vacuum plodder and the laundry bar made comprises from 20 to 30% of sodium lauryl sulfate, 5 to 15% of sodium tripolyphosphate, 10 to 30% of calcium carbonate, 5 to 20% of bentonite, 3 to 8% of higher fatty acid, 3 to 8% of higher fatty acid alkanolamide, 2 to 8% of sodium silicate of Na 2 O:SiO 2 ratio in the range of 1:1.6 to 1:3, 3 to 8% of talc and 9 to 14% of moisture.
Claim 15
Dependent Claim
78 words
A process according to claim 10 wherein the higher fatty acid is a mixture of coco fatty acids and palm kernel fatty acids, the higher fatty acid alkanolamide is cocomonoethanolamide, the sodium silicate is of Na 2 O:SiO 2 ratio of about 1:2, and about 1 part of lauryl alcohol is present in the mix before milling and plodding, and after milling and plodding the plodder bar is cut to blank lengths and is pressed to final form.
Claim 16
Dependent Claim
19 words
A process according to claim 6 wherein the milled, plodded, extruded and cut material is pressed to bar shape.
Claim 17
Dependent Claim
17 words
A process according to claim 7 wherein the cut bar lengths are pressed to final bar form.
References Cited (Backward Citations)
US2845391A
Cited
GB557593A
Cited
US2982735A
Cited
US2941948A
Cited
GB945062A
Cited
US3434974A
Cited
US3442812A
Cited
US3798181A
Cited
US4219436A
Cited
GB2048931A
Cited
GB2096163A
Cited
GB2099013A
Cited
GB2127426A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-23 | 1989-03-25 | 1989-09-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-23 | 1993-03-25 | 1993-09-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-23 | 1997-03-25 | 1997-09-24 | $7700.00 | Window Closed / Lapsed |