Silicon nitride-cordierite ceramic article, and process of manufacture thereof
Assignee: Verizon Laboratories Inc
•
Filing: 1983-08-09
•
Granted: 1985-09-17
•
Expires: 2003-08-09
Abstract
Abstract A silicon nitride-cordierite article, and process for fabricating is described. The silicon nitride imparts a high mechanical strength, and the cordierite contributes to a lower thermal conductivity making the composition especially useful for internal parts of a diesel engine. The mechanical strength can be increased by crystallizing the continuous cordierite glassy phase of the article. Crystallization of the continuous cordierite glassy phase is accomplished by the addition of a nucleating agent such as zirconium dioxide in the formulation and a subsequent reheating step after densification.
Inventors
- 👤 Arvid E. Pasto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:17
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/01; C04B35/16; C04B35/18; C04B35/195; F; F02; F02B; F02B3/00; F02B3/06
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
44 words
A ceramic article consisting essentially of a first phase of silicon nitride, a second continuous phase of cordierite, and a nucleating agent, said ceramic article having a density greater than 95 percent of theoretical density, said second continuous phase of cordierite being essentially crystalline.
Claim 2
Dependent Claim
44 words
A ceramic article consisting essentially of a first phase of silicon nitride, a second continuous phase of cordierite, and a nucleating agent, said ceramic article having a density greater than 95 percent of theoretical density, said second continuous phase of cordierite being essentially crystalline.
Claim 3
Dependent Claim
28 words
A ceramic article in accordance with claim 1 wherein said ceramic article contains from about 5 to about 75 volume percent of said second continuous phase of cordierite.
Claim 4
Dependent Claim
32 words
A ceramic article in accordance with claim 1 wherein said nucleating agent consists essentially of zirconium dioxide in the amount from about 1 to about 5 weight percent of said ceramic article.
Claim 5
Dependent Claim
27 words
A ceramic article in accordance with claim 1 wherein said ceramic article has a modulus of rupture greater than 110 KSI at temperatures of about 900° C.
Claim 6
Dependent Claim
27 words
A ceramic article in accordance with claim 1 wherein said ceramic article has a modulus of rupture greater than 35 KSI at temperatures greater than 1000° C.
Claim 7
Dependent Claim
53 words
A ceramic article having a composition comprising of silicon nitride, and cordierite, said composition having an approximate formula (Si 3 N 4 ).sub.(1-x) (2MgO.2Al 2 O 3 .5SiO 2 ) x wherein x is from about 0.05 to about 0.75, said ceramic article having a density greater than 95 percent of theoretical density.
Claim 8
Dependent Claim
53 words
A ceramic article having a composition comprising of silicon nitride, and cordierite, said composition having an approximate formula (Si 3 N 4 ).sub.(1-x) (2MgO.2Al 2 O 3 .5SiO 2 ) x wherein x is from about 0.05 to about 0.75, said ceramic article having a density greater than 95 percent of theoretical density.
Claim 9
Dependent Claim
96 words
A process for fabricating a densified ceramic article comprising blending silicon nitride, magnesium oxide, silicon dioxide, aluminum sesquioxide, and a nucleating agent to form a powder mixture; pressing said powder mixture to form a ceramic article; sintering said ceramic article at an effective temperature in an inert atmosphere to form a densified ceramic article consisting essentially of a first phase of silicon nitride and a second continuous phase of cordierite and a nucleating agent; and reheating said densified ceramic article at an effective temperature for an effective time to crystallize said second continuous phase of cordierite.
Claim 10
Dependent Claim
96 words
A process for fabricating a densified ceramic article comprising blending silicon nitride, magnesium oxide, silicon dioxide, aluminum sesquioxide, and a nucleating agent to form a powder mixture; pressing said powder mixture to form a ceramic article; sintering said ceramic article at an effective temperature in an inert atmosphere to form a densified ceramic article consisting essentially of a first phase of silicon nitride and a second continuous phase of cordierite and a nucleating agent; and reheating said densified ceramic article at an effective temperature for an effective time to crystallize said second continuous phase of cordierite.
Claim 11
Dependent Claim
24 words
A process in accordance with claim 7 wherein the effective temperature of said sintering step is from about 1400° C. to about 1800° C.
Claim 12
Dependent Claim
24 words
A process in accordance with claim 7 wherein said densified ceramic article is sintered to a density greater than 95 percent of theoretical density.
Claim 13
Dependent Claim
24 words
A process in accordance with claim 7 wherein said powder mixture is pressed at a pressure of about 5,000 psig to about 20,000 psig.
Claim 14
Dependent Claim
32 words
A process in accordance with claim 7 wherein the silicon nitride, magnesium oxide, silicon dioxide, aluminum sesquioxide and a nucleating agent are blended in a non-metallic ball mill using non-contaminating milling media.
Claim 15
Dependent Claim
27 words
A process in accordance with claim 11 wherein said non-contaminating milling media is selected from the group consisting of silicon nitride, cordierite, zirconium dioxide, and mixtures thereof.
Claim 16
Dependent Claim
33 words
A process in accordance with claim 7 wherein the effective temperature and the effective time of said reheating step is from about 900° C. to about 1100° C. for at least 2 hours.
Claim 17
Dependent Claim
105 words
A process for fabricating a molded densified ceramic article comprising blending silicon nitride, magnesium oxide, silicon dioxide, aluminum sesquioxide and a nucleating agent to form a powder mixture; densifying said powder mixture to form a densified ceramic article having a crystalline silicon nitride first phase, a continuous glassy cordierite second phase and a nucleating agent; heating said densified ceramic article at a temperature sufficient to form a plastic densified ceramic article; molding said plastic densified ceramic article to form a molded densified ceramic article; crystallizing said continuous glassy cordierite second phase of said molded densified ceramic article to form a rigid, molded densified ceramic article.
Claim 18
Dependent Claim
105 words
A process for fabricating a molded densified ceramic article comprising blending silicon nitride, magnesium oxide, silicon dioxide, aluminum sesquioxide and a nucleating agent to form a powder mixture; densifying said powder mixture to form a densified ceramic article having a crystalline silicon nitride first phase, a continuous glassy cordierite second phase and a nucleating agent; heating said densified ceramic article at a temperature sufficient to form a plastic densified ceramic article; molding said plastic densified ceramic article to form a molded densified ceramic article; crystallizing said continuous glassy cordierite second phase of said molded densified ceramic article to form a rigid, molded densified ceramic article.
Claim 19
Dependent Claim
48 words
A process in accordance with claim 14 wherein the step of densifying comprises pressing said powder mixture to form a ceramic article; and sintering said ceramic article at a temperature from about 1400° C. to about 1800° C. in an inert atmoshere to form a densified ceramic article.
Claim 20
Dependent Claim
23 words
A process in accordance with claim 14 wherein said powder mixture is densified to a density greater than 95 percent of theoretical density.
Claim 21
Dependent Claim
20 words
A process in accordance with claim 15 wherein said powder mixture is pressed at a pressure of about 5,000 psig.
Claim 22
Dependent Claim
54 words
A process in accordance with claim 14 wherein said powder mixture has an approximate formulation (Si 3 N 4 ).sub.(1-x) (2MgO.2Al 2 O 3 .5SiO 2 ) x wherein x is from about 0.50 to about 0.75 and a nucleating agent being from about one to about 5 weight percent of said powder mixture.
Claim 23
Dependent Claim
14 words
A process in accordance with claim 18 wherein said nucleating agent is zirconium dioxide.
References Cited (Backward Citations)
DE2302438A1
Cited
DE2540015A1
Cited
US4143182A
Cited
DE2544437A1
Cited
US4104442A
Cited
US4070198A
Cited
US4283360A
Cited
JPS5647148A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-16 | 1989-03-18 | 1989-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-16 | 1993-03-18 | 1993-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-16 | 1997-03-18 | 1997-09-17 | $7700.00 | Window Closed / Lapsed |