Low temperature fired dielectric ceramic composition with flat TC characteristic and method of making
Assignee: Tam Ceramics LLC
•
Filing: 1984-05-23
•
Granted: 1985-09-10
•
Expires: 2004-05-23
Abstract
Abstract A low temperature fired ceramic dielectric composition in which the dielectric constant does not vary from its base value of over 2400 by more than 15 percent over a wide temperature range. A base ceramic preparation (a) and a ceramic flux (b), each consisting essentially of metal oxides or precursors thereof to provide in oxide form (a) 98.0 to 99 weight percent barium titanate, from about 0.97 to about 1.54 weight percent niobium pentoxide and from about 0.19 to about 0.32 weight percent cobalt oxide; (b) from about 16 to about 60 weight percent bismuth titanate, about 8 to about 52 weight percent lead titanate, about 18 to about 35 weight percent zinc oxide and about 5 to about 11 weight percent boron oxide. Manganese dioxide or precursor thereof in amount of from about 0 to 0.114 percent of the combined weight of the base ceramic preparation and ceramic flux is added to the metal oxides or precursors of the base ceramic preparation and ceramic flux and the mixture is fired at a temperature less than about 1150° C.
Inventors
- 👤 Mike S. H. Chu
- 👤 Charles E. Hodgkins
- 👤 Daniel C. Rose
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:08
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B35/4684
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
97 words
A dielectric ceramic composition consisting essentially of from about 91.6 to about 95.5 weight percent barium titanate, from about 0.91 to about 1.49 weight percent niobium pentoxide, from about 0.18 to about 0.31 weight percent cobalt oxide, from about 1.04 to about 1.87 weight percent bismuth trioxide, from about 0.68 to about 1.23 weight percent titanium dioxide, from about 0.67 to about 1.20 weight percent lead oxide, from about 0.26 to about 0.46 weight percent boron oxide, from about 0.82 to about 1.49 weight percent zinc oxide, and from 0 to about 0.11 weight percent manganese dioxide.
Claim 2
Dependent Claim
97 words
A dielectric ceramic composition consisting essentially of from about 91.6 to about 95.5 weight percent barium titanate, from about 0.91 to about 1.49 weight percent niobium pentoxide, from about 0.18 to about 0.31 weight percent cobalt oxide, from about 1.04 to about 1.87 weight percent bismuth trioxide, from about 0.68 to about 1.23 weight percent titanium dioxide, from about 0.67 to about 1.20 weight percent lead oxide, from about 0.26 to about 0.46 weight percent boron oxide, from about 0.82 to about 1.49 weight percent zinc oxide, and from 0 to about 0.11 weight percent manganese dioxide.
Claim 3
Dependent Claim
182 words
A dielectric ceramic composition formed by firing a mixture comprising (a) from about 93.5 to about 96.5 percent by weight of a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 98.0 to about 99 weight percent barium titanate, from about 0.97 to about 1.54 weight percent niobium pentoxide, and from about 0.19 to about 0.32 weight percent cobalt oxide; (b) from about 3.5 to about 6.5 percent by weight of a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 16 to about 60 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 8 to about 52 weight percent lead titanate, about 18 to about 35 weight percent zinc oxide, and about 5 to about 11 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of from about 0 to 0.114 percent of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 4
Dependent Claim
182 words
A dielectric ceramic composition formed by firing a mixture comprising (a) from about 93.5 to about 96.5 percent by weight of a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 98.0 to about 99 weight percent barium titanate, from about 0.97 to about 1.54 weight percent niobium pentoxide, and from about 0.19 to about 0.32 weight percent cobalt oxide; (b) from about 3.5 to about 6.5 percent by weight of a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 16 to about 60 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 8 to about 52 weight percent lead titanate, about 18 to about 35 weight percent zinc oxide, and about 5 to about 11 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of from about 0 to 0.114 percent of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 5
Dependent Claim
31 words
A dielectric ceramic composition in accordance with claim 2 wherein said mixture comprises about 95 weight percent of said base ceramic preparation and about 5 weight percent of said ceramic flux.
Claim 6
Dependent Claim
33 words
A dielectric ceramic composition in accordance with claim 2 wherein the ratio of the weight of said bismuth titanate to the weight of said lead titanate is between about 7.33:1 and about 0.33:1.
Claim 7
Dependent Claim
41 words
A dielectric ceramic composition in accordance with claim 2 wherein the ratio of the combined weight of said bismuth titanate and said lead titanate to the combined weight of said zinc oxide and said boron oxide is between 3.20:1 and 1.24:1.
Claim 8
Dependent Claim
34 words
A dielectric ceramic composition in accordance with claim 2 wherein said zinc oxide is from about 1.22 to about 1.60 percent of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 9
Dependent Claim
34 words
A dielectric ceramic composition in accordance with claim 2 wherein said boron oxide is from about 0.38 to about 0.50 percent of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 10
Dependent Claim
17 words
A dielectric ceramic composition in accordance with claim 2 wherein the dielectric constant is greater than 2400.
Claim 11
Dependent Claim
41 words
A dielectric ceramic composition in accordance with claim 2 wherein said composition is formed by sintering said base ceramic preparation, said ceramic flux and said manganese dioxide or oxide precursors thereof at a temperature between about 1100° C. and 1140° C.
Claim 12
Dependent Claim
39 words
A dielectric ceramic composition in accordance with claim 2 wherein the capacitance of said composition varies with temperature from the capacitance at 25° C. about 15 percent or less at temperatures between about -55° C. and about 125° C.
Claim 13
Dependent Claim
136 words
A dielectric ceramic composition having a dielectric constant greater than 2400, said composition consisting essentially of from about 91.6 to about 95.5 weight percent barium titanate, from about 0.91 to about 1.49 weight percent niobium pentoxide, from about 0.18 to about 0.31 weight percent cobalt oxide, from about 1.04 to about 1.87 weight percent bismuth trioxide, from about 0.68 to about 1.23 weight percent titanium dioxide, from about 0.67 to about 1.20 weight percent lead oxide, from about 0.26 to about 0.46 weight percent boron oxide, from about 0.82 to about 1.49 weight percent zinc oxide, and from 0 to about 0.11 weight percent manganese dioxide, wherein the capacitance of said composition varies with temperature about 15 percent or less from the capacitance at 25° C. at temperatures between about -55° C. and about 125° C.
Claim 14
Dependent Claim
136 words
A dielectric ceramic composition having a dielectric constant greater than 2400, said composition consisting essentially of from about 91.6 to about 95.5 weight percent barium titanate, from about 0.91 to about 1.49 weight percent niobium pentoxide, from about 0.18 to about 0.31 weight percent cobalt oxide, from about 1.04 to about 1.87 weight percent bismuth trioxide, from about 0.68 to about 1.23 weight percent titanium dioxide, from about 0.67 to about 1.20 weight percent lead oxide, from about 0.26 to about 0.46 weight percent boron oxide, from about 0.82 to about 1.49 weight percent zinc oxide, and from 0 to about 0.11 weight percent manganese dioxide, wherein the capacitance of said composition varies with temperature about 15 percent or less from the capacitance at 25° C. at temperatures between about -55° C. and about 125° C.
Claim 15
Dependent Claim
144 words
A dielectric ceramic composition formed from (a) about 95.24 percent by weight of a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 98.31 weight percent barium titanate, about 1.40 weight percent niobium pentoxide, and 0.29 weight percent cobalt oxide; (b) about 4.76 percent by weight of a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 27.99 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 40.02 weight percent lead titanate, about 24.4 weight percent zinc oxide and 7.6 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of about 0.05 percent of the combined of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 16
Dependent Claim
144 words
A dielectric ceramic composition formed from (a) about 95.24 percent by weight of a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 98.31 weight percent barium titanate, about 1.40 weight percent niobium pentoxide, and 0.29 weight percent cobalt oxide; (b) about 4.76 percent by weight of a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, about 27.99 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 40.02 weight percent lead titanate, about 24.4 weight percent zinc oxide and 7.6 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of about 0.05 percent of the combined of the combined weight of said base ceramic preparation and said ceramic flux.
Claim 17
Independent Claim
181 words
A method of making dielectric ceramic composition which comprises: (1) mixing (a) a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 98.0 to about 99 weight percent barium titanate, from about 0.97 to about 1.54 weight percent niobium pentoxide, and from about 0.19 to about 0.32 weight percent cobalt oxide; (b) a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 16 to about 60 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 8 to about 52 weight percent lead titanate, about 18 to about 35 weight percent zinc oxide, and about 5 to about 11 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of from about 0 to about 0.114 percent of the combined weight of said base ceramic preparation and said ceramic flux; (2) firing the resulting mixture at a temperature between about 1100° C. and about 1140° C.
Claim 18
Independent Claim
181 words
A method of making dielectric ceramic composition which comprises: (1) mixing (a) a base ceramic preparation consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 98.0 to about 99 weight percent barium titanate, from about 0.97 to about 1.54 weight percent niobium pentoxide, and from about 0.19 to about 0.32 weight percent cobalt oxide; (b) a ceramic flux consisting essentially of metal oxides or precursors thereof in proportions to provide, in the oxide form, from about 16 to about 60 weight percent bismuth titanate (Bi 2 Ti 2 O 7 ), about 8 to about 52 weight percent lead titanate, about 18 to about 35 weight percent zinc oxide, and about 5 to about 11 weight percent boron oxide; and (c) manganese dioxide or precursors thereof in proportions to provide manganese dioxide in an amount of from about 0 to about 0.114 percent of the combined weight of said base ceramic preparation and said ceramic flux; (2) firing the resulting mixture at a temperature between about 1100° C. and about 1140° C.
Claim 19
Dependent Claim
49 words
A method in accordance with claim 13 wherein said mixture of said base ceramic preparation and said ceramic flux consists essentially of from about 3.5 to about 6.5 weight percent of said ceramic flux and of from about 96.5 to about 93.5 weight percent of said base ceramic preparation.
Claim 20
Dependent Claim
39 words
A method in accordance with claim 13 wherein said mixture of said base ceramic preparation and said ceramic flux consists essentially of about 95 weight percent of said base ceramic preparation and 5 weight percent of said ceramic flux.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |