US4540437A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Tin alloy powder for sintering
Assignee: ACUPOWDER INTERNATIONAL LLC
•
Filing: 1984-09-25
•
Granted: 1985-09-10
•
Expires: 2004-09-25
Abstract
Abstract A tin alloy powder containing up to 5% P is disclosed. Reduced sensitivity to sintering conditions is achieved by use of present alloy powder in production of sintered bronze articles. Means for controlling the growth of the article during sintering are also disclosed.
Inventors
- 👤 Krishnakant B. Patel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:20
CPC Classifications
C; C22; C22C; C22C13/00; B; B22; B22F; B22F1/00; B22F1/09; B22F1/12; C22C1/00; C22C1/04; C22C1/05; C22C1/059
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
20 words
A tin alloy powder comprising a major proportion of tin, about 0.1 to 5.0 weight percent phosphorus and incidental impurities.
Claim 2
Dependent Claim
20 words
A tin alloy powder comprising a major proportion of tin, about 0.1 to 5.0 weight percent phosphorus and incidental impurities.
Claim 3
Dependent Claim
16 words
The tin alloy powder of claim 1 further comprising up to about 20 weight percent copper.
Claim 4
Dependent Claim
15 words
The tin alloy powder of claim 1 comprising about 0.1 to 1.5 weight percent phosphorus.
Claim 5
Dependent Claim
15 words
The tin alloy powder of claim 1 comprising about 0.3 to 1.0 weight percent phosphorus.
Claim 6
Dependent Claim
16 words
The tin alloy powder of claim 3 further comprising up to about 20 weight percent copper.
Claim 7
Dependent Claim
16 words
The tin alloy powder of claim 4 further comprising up to about 20 weight percent copper.
Claim 8
Dependent Claim
66 words
The tin alloy powder of claim 1 blended with a copper-based metal powder, comprising at least about 80 weight percent copper, said blend comprising about 4 to 30 parts by weight of said tin alloy powder, about 70 to 96 parts by weight of said copper-based metal powder and up to 20 parts by weight of a material selected from lubricant, graphite, binders and mixtures thereof.
Claim 9
Dependent Claim
30 words
The blend of claim 7 comprising about 4 to 15 parts by weight of said tin alloy and about 85 to 96 parts by weight of said copper-based metal powder.
Claim 10
Dependent Claim
67 words
The tin alloy powder of claim 4 blended with a copper-based metal powder comprising at least about 80 weight percent copper, said blend comprising about 4 to 15 parts by weight of said tin alloy powder, about 85 to about 96 parts by weight of said copper-based metal powder and up to 20 parts by weight of a material selected from lubricant, graphite, binders and mixtures thereof.
Claim 11
Dependent Claim
54 words
The blend of claim 7 diluted by further blending with iron powder to produce a diluted blend comprising 20 to 80 parts of the blend of claim 7 and 20 to 80 parts of iron powder, all powders in said diluted blend having a particle size disposed to pass through a 60 mesh screen.
Claim 12
Independent Claim
84 words
A method for producing a sinterable blend having a reduced sintering sensitivity comprising alloying tin with about 0.1 to about 5.0 weight percent phosphorous, atomizing said tin alloy to make a tin powder, and blending about 4 parts to about 30 parts by weight of said tin powder, about 70 parts to about 96 parts by weight of a copper powder and up to 20 parts by weight of a material selected from lubricant, graphite, binder and mixtures thereof to produce said sinterable blend.
Claim 13
Independent Claim
84 words
A method for producing a sinterable blend having a reduced sintering sensitivity comprising alloying tin with about 0.1 to about 5.0 weight percent phosphorous, atomizing said tin alloy to make a tin powder, and blending about 4 parts to about 30 parts by weight of said tin powder, about 70 parts to about 96 parts by weight of a copper powder and up to 20 parts by weight of a material selected from lubricant, graphite, binder and mixtures thereof to produce said sinterable blend.
Claim 14
Dependent Claim
49 words
The method of claim 11 wherein said sinterable blend comprises about 85 to about 96 parts by weight copper powder and about 4 to about 15 parts by weight tin powder and up to 20 parts by weight of a material selected from lubricant, graphite, binders, and mixtures thereof.
Claim 15
Dependent Claim
19 words
The method of claim 11 wherein said tin is alloyed with about 0.1 to about 1.5 weight percent phosphorous.
Claim 16
Dependent Claim
19 words
The method of claim 11 wherein said tin is alloyed with about 0.3 to about 1.0 weight percent phosphorous.
Claim 17
Independent Claim
104 words
A method of sintering comprising; preparing a blend comprising about 70 parts to about 96 parts by weight copper powder and about 4 parts to about 30 parts by weight tin powder and up to about 20 parts by weight of a material selected from lubricant, graphite, binders and mixtures thereof, compressing said blend to form a coherent compact, and sintering said compact in a non-oxidizing atmosphere at a temperature between about 1200° F. and 1700° F. wherein the improvement comprises preparing said blend with a tin powder comprising a major proportion of tin, about 0.1 to 5.0 weight percent phosphorous and incidental impurities.
Claim 18
Independent Claim
104 words
A method of sintering comprising; preparing a blend comprising about 70 parts to about 96 parts by weight copper powder and about 4 parts to about 30 parts by weight tin powder and up to about 20 parts by weight of a material selected from lubricant, graphite, binders and mixtures thereof, compressing said blend to form a coherent compact, and sintering said compact in a non-oxidizing atmosphere at a temperature between about 1200° F. and 1700° F. wherein the improvement comprises preparing said blend with a tin powder comprising a major proportion of tin, about 0.1 to 5.0 weight percent phosphorous and incidental impurities.
Claim 19
Dependent Claim
33 words
The method of claim 15 wherein said tin powder is prepared by melting tin to form a molten pool thereof, adding to said pool a predetermined proportion of phosphorous and atomizing said pool.
Claim 20
Dependent Claim
29 words
The method of claim 16 wherein said phosphorous is added to said pool in the form of a copper-phosphorous alloy containing up to about 15 percent by weight phosphorous.
Claim 21
Dependent Claim
9 words
The product produced by the method of claim 15.
Claim 22
Dependent Claim
9 words
The product produced by the method of claim 17.
Claim 23
Dependent Claim
9 words
The blend produced by the method of claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |