Modified polyimide/polyimide-amide foams and methods of making same
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1984-12-06
•
Granted: 1985-09-03
•
Expires: 2004-12-06
Abstract
Abstract Methods of making modified polyimide/polyimide-amide foams having selected compressive resistance and density characteristics and the resulting compositions. A suitable aromatic dianhydride is mixed with a suitable oxoimine and alcohol, which initially is believed to form a monoimide which is substantially/simultaneously esterified by the alcohol. To this mixture is added a suitable diamine to produce a polyimide forming material. This material is dried to a powder or film. A foam is produced by heating the material to reaction temperature for a period sufficient to produce a stable foam. The material melts, then spontaneously expands into a foam which becomes self supporting and cures to a resilient flexible foam. Depending upon heating conditions, a polyimide, polyimide-amide or mixture thereof may be produced, resulting in foams having varying physical properties. Within the mole ratio range of oxoimine to dianhydride of about 1.5:1 to about 0.05:1 the compressive resistance of the final foam can be selected in accordance with the intended end use of the foam. Density and compressive resistance varies inversely with the oxoimine quantity in the ratio, being greatest with the 0.05:1 ratio and lowest with the 1.5:1 ratio.
Inventors
- 👤 John V. Long
- 👤 John Gagliani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:38
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08G73/1032; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
150 words
The method of making a resilient, flame resistant modified polyimide foam having a selected compressive resistance which comprises the steps of: providing an aromatic dianhydride; mixing these with an agent selected from oxoimines, amino acids and mixtures thereof; the mole ratio of said agent to dianhydride between about 1.5:1 and just above 0:1; mixing therewith a suitable quantity of an alcohol; heating the mixture to a temperature of about 60° C. to 120° C. for 30 to 90 minutes to produce an ester; adding thereto a diamine; drying the resulting solution; and heating the dry material to a selected foaming temperature of from about 120° C. to about 320° C. for a period of from about 10 to about 60 minutes; whereby a resilient foam having a selected compressive resistance in accordance with the selected oxoimine to dianhydride mole ratio, the compressive resistance being inversely proportional to the oxoimine quantity.
Claim 2
Independent Claim
150 words
The method of making a resilient, flame resistant modified polyimide foam having a selected compressive resistance which comprises the steps of: providing an aromatic dianhydride; mixing these with an agent selected from oxoimines, amino acids and mixtures thereof; the mole ratio of said agent to dianhydride between about 1.5:1 and just above 0:1; mixing therewith a suitable quantity of an alcohol; heating the mixture to a temperature of about 60° C. to 120° C. for 30 to 90 minutes to produce an ester; adding thereto a diamine; drying the resulting solution; and heating the dry material to a selected foaming temperature of from about 120° C. to about 320° C. for a period of from about 10 to about 60 minutes; whereby a resilient foam having a selected compressive resistance in accordance with the selected oxoimine to dianhydride mole ratio, the compressive resistance being inversely proportional to the oxoimine quantity.
Claim 3
Dependent Claim
29 words
A method according to claim 1 wherein the mole ratio of oxoimine to dianhydride is about 0.05:1, whereby the resulting foam has a high density and high compressive resistance.
Claim 4
Dependent Claim
29 words
The method according to claim 1 wherein the mole ratio of oxoimine to dianhydride is about 1.5:1, whereby the resulting foam has a low density and low compressive resistance.
Claim 5
Dependent Claim
31 words
The method according to claim 1 wherein said foaming temperature is in the range of from about 230° C. and about 320° C. and the resulting foam comprises primarily a polyimide.
Claim 6
Dependent Claim
31 words
The method according to claim 1 wherein said foaming temperature is in the range of from about 120° C. and about 220° C. and the resulting foam is primarily a polyimide-amide.
Claim 7
Dependent Claim
20 words
The method according to claim 1 wherein said aromatic dianhydride is pyromellitic dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride or mixtures thereof.
Claim 8
Dependent Claim
23 words
The method according to claim 1 wherein said oxoimine has the general formula: ##STR8## wherein "x" is an integer from 2 to 4.
Claim 9
Dependent Claim
31 words
The method according to claim 1 wherein said agent is selected from the group consisting of caprolactam, 2-piperidone, 2-pyrrolidone, 6-amino caproic acid, 5-amino valeric acid, 4-amino butyric acid and mixtures thereof.
Claim 10
Dependent Claim
11 words
The method according to claim 1 wherein said oxoimine is caprolactam.
Claim 11
Dependent Claim
12 words
The method according to claim 1 wherein said alcohol is methyl alcohol.
Claim 12
Dependent Claim
12 words
The method according to claim 1 wherein said diamine is 4,4'-diaminophenyl methane.
Claim 13
Dependent Claim
31 words
The method according to claim 1 wherein said diamine comprises at least two different diamines, at least one of which is an aromatic diamine and the other is an aliphatic diamine.
Claim 14
Dependent Claim
17 words
The method according to claim 12 wherein the mixed diamines are 4,4'-diamino diphenyl methane and 1,6-diamino hexane.
Claim 15
Dependent Claim
29 words
The method according to claim 1 further including the step of adding from about 0.01 to about 2 wt. % of a surfactant to the solution prior to drying.
Claim 16
Dependent Claim
22 words
The method according to claim 1 further including the step of adding fillers or reinforcing materials to the solution prior to drying.
Claim 17
Independent Claim
284 words
The method of making a modified polyimide foam having a selected compressive resistance comprising a mixture of polyimide and polyimide-amide resins with the polyimide-amide predominating which comprises the steps of: mixing together an aromatic dianhydride selected from pyromellitic dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and mixtures thereof and an oxoimine having the general formula: ##STR9## wherein "x" is an integer from 2 to 4, the mole ratio of oxoimine to dianhydride being selected within the range of from about 1.5:1 to about 1.05:1 in accordance with the final foam compressive resistance desired; mixing therewith an effective quantity of an alcohol; heating the mixture to a temperature of from about 60° to about 120° C. for from about 30 to about 90 minutes to react said dianhydride with said oxoimine to produce an N-substituted aliphatic imide and further to esterify said imide; cooling the mixture to a temperature of from about 40° C. to about 70° C.; adding thereto about 1.0M 4,4'-diaminodiphenyl methane per 1.0M of dianhydride; heating the resulting solution to reflux at a temperature of from about 70° C. to about 80° C. for a period of about 2 to about 30 minutes; drying the solution at a temperature of from about 60° C. to about 70° C. for a period of about 60 to about 240 minutes to produce a dry material; and foaming said dry material by heating to a temperature of about 120° C. to about 220° C. in a pre-heated oven for from about 10 to about 40 minutes; whereby a resilient foam is formed having a selected compressive resistance in accordance with the selected oxoimine to dianhydride mole ratio, the compressive resistance being inversely proportional to the oxoimine quantity.
Claim 18
Independent Claim
284 words
The method of making a modified polyimide foam having a selected compressive resistance comprising a mixture of polyimide and polyimide-amide resins with the polyimide-amide predominating which comprises the steps of: mixing together an aromatic dianhydride selected from pyromellitic dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and mixtures thereof and an oxoimine having the general formula: ##STR9## wherein "x" is an integer from 2 to 4, the mole ratio of oxoimine to dianhydride being selected within the range of from about 1.5:1 to about 1.05:1 in accordance with the final foam compressive resistance desired; mixing therewith an effective quantity of an alcohol; heating the mixture to a temperature of from about 60° to about 120° C. for from about 30 to about 90 minutes to react said dianhydride with said oxoimine to produce an N-substituted aliphatic imide and further to esterify said imide; cooling the mixture to a temperature of from about 40° C. to about 70° C.; adding thereto about 1.0M 4,4'-diaminodiphenyl methane per 1.0M of dianhydride; heating the resulting solution to reflux at a temperature of from about 70° C. to about 80° C. for a period of about 2 to about 30 minutes; drying the solution at a temperature of from about 60° C. to about 70° C. for a period of about 60 to about 240 minutes to produce a dry material; and foaming said dry material by heating to a temperature of about 120° C. to about 220° C. in a pre-heated oven for from about 10 to about 40 minutes; whereby a resilient foam is formed having a selected compressive resistance in accordance with the selected oxoimine to dianhydride mole ratio, the compressive resistance being inversely proportional to the oxoimine quantity.
Claim 19
Dependent Claim
29 words
The method according to claim 16 wherein the mole ratio of oxoimine to dianhydride is about 0.05:1, whereby the resulting foam has a high density and high compressive resistance.
Claim 20
Dependent Claim
29 words
The method according to claim 16 wherein the mole ratio of oxoimine to dianhydride is about 1.5:1, whereby the resulting foam has a low density and low compressive resistance.
Claim 21
Independent Claim
287 words
The method of making a modified polyimide foam having a selected compressive resistance comprising a mixture of polyimide and polyimide-amide with the polyimide predominating which comprises the steps of: mixing together an aromatic dianhydride selected from pyromellitic dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and mixtures thereof and an oxoimine having the general formula: ##STR10## wherein "x" is an integer from 2 to 4, the mole ratio of oxoimine to dianhydride being selected within the range of from about 1.5:1 to about 0.05:1 in accordance with the desired final foam compressive resistance, said compressive resistance being inversely proportional to the oxoimine quantity; mixing therewith from about 5 to 10 moles alcohol per 100 mole dianhydride, heating the mixture to a temperature of from about 60° to about 120° C. for from about 30 to about 90 minutes to react said dianhydride with said oxoimine to produce an N-substituted aliphatic imide and substantially simultaneously esterify said imide; cooling the mixture to a temperature of from about 40° C. to about 70° C.; adding thereto about 1.0M 4,4'-diaminodiphenyl methane per about 1.0M of dianhydride; heating the resulting solution to reflux at a temperature of from about 70° C. to about 80° C. for a period of about 2 to about 30 minutes; drying the solution at a temperature of from about 60° C. to about 70° C. for a period of about 60 to about 240 minutes to produce a dry material; and foaming said dry material by heating to a temperature of about 230° C. to about 320° C. in a pre-heated oven for about 30 to about 60 minutes; whereby a resilient flame resistant modified polyimide foam having selected compressive resistance characteristics is produced, consisting primarily of polyimide resin.
Claim 22
Independent Claim
287 words
The method of making a modified polyimide foam having a selected compressive resistance comprising a mixture of polyimide and polyimide-amide with the polyimide predominating which comprises the steps of: mixing together an aromatic dianhydride selected from pyromellitic dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and mixtures thereof and an oxoimine having the general formula: ##STR10## wherein "x" is an integer from 2 to 4, the mole ratio of oxoimine to dianhydride being selected within the range of from about 1.5:1 to about 0.05:1 in accordance with the desired final foam compressive resistance, said compressive resistance being inversely proportional to the oxoimine quantity; mixing therewith from about 5 to 10 moles alcohol per 100 mole dianhydride, heating the mixture to a temperature of from about 60° to about 120° C. for from about 30 to about 90 minutes to react said dianhydride with said oxoimine to produce an N-substituted aliphatic imide and substantially simultaneously esterify said imide; cooling the mixture to a temperature of from about 40° C. to about 70° C.; adding thereto about 1.0M 4,4'-diaminodiphenyl methane per about 1.0M of dianhydride; heating the resulting solution to reflux at a temperature of from about 70° C. to about 80° C. for a period of about 2 to about 30 minutes; drying the solution at a temperature of from about 60° C. to about 70° C. for a period of about 60 to about 240 minutes to produce a dry material; and foaming said dry material by heating to a temperature of about 230° C. to about 320° C. in a pre-heated oven for about 30 to about 60 minutes; whereby a resilient flame resistant modified polyimide foam having selected compressive resistance characteristics is produced, consisting primarily of polyimide resin.
Claim 23
Dependent Claim
29 words
The method according to claim 19 wherein the mole ratio of oxoimine to dianhydride is about 0.05:1, whereby the resulting foam has a high density and high compressive resistance.
Claim 24
Dependent Claim
29 words
The method according to claim 19 wherein the mole ratio of oxoimine to dianhydride is about 1.5:1, whereby the resulting foam has a low density and low compressive resistance.
Claim 25
Dependent Claim
25 words
The method according to claim 19 wherein the diamine added is a mixture of an aliphatic diamine and an aromatic diamine containing a methylene bridge.
Claim 26
Dependent Claim
19 words
The method according to claim 22 wherein the mixture of diamines is composed of 4,4'-diaminodiphenyl methane and 1,6-diamino hexane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-02 | 1989-03-04 | 1989-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-02 | 1993-03-04 | 1993-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-02 | 1997-03-04 | 1997-09-03 | $7700.00 | Window Closed / Lapsed |