Closed cell polyimide foams and methods of making same
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1983-02-10
•
Granted: 1984-01-10
•
Expires: 2003-02-10
Abstract
Abstract A high temperature and flame resistant closed cell polyimide foam material and methods of making the foam. An aromatic tetracarboxylic acid dianhydride is reacted with an oxomine to produce an N-substituted imide, which is then esterified with a suitable alcohol. The resulting liquid is dried and the dry residue is reduced to a uniform powder having particles with diameters generally in the 0.5 to 10 mm. range. The powder is preferably further dried, either before or after final size reduction, in a moderate vacuum at moderate temperature to remove any excess residual alcohol. The powder spontaneously expands to form a closed cell foam when heated to a temperature in the range of about 90° to 150° C. for a suitable period. When the powder is expanded in a closed mold, a well consolidated, uniform, closed cell foam product results. When expanded in an unrestricted manner, closed cell "macroballoons" having average diameters between about 0.4 to 15 mm. result. The closed cell foam produced has excellent flexibility and resistance to heat and flame, and does not shrink appreciably when exposed to flame.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:04
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/22; C08J9/228; C08J9/236; B; B32; B32B; B32B5/00; B32B5/18; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08J9/02; C08J9/16; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
152 words
A process for producing high temperature and flame resistant closed cell foam structure formed by the following process steps: reacting an oxoimine having the general formula ##STR6## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio thereof between about 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles into a honeycomb structure; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a closed cell foam of substantial uniform density throughout the honeycomb structure forming a high strength structure with cell foam bonded to the honeycomb results.
Claim 2
Dependent Claim
152 words
A process for producing high temperature and flame resistant closed cell foam structure formed by the following process steps: reacting an oxoimine having the general formula ##STR6## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio thereof between about 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles into a honeycomb structure; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a closed cell foam of substantial uniform density throughout the honeycomb structure forming a high strength structure with cell foam bonded to the honeycomb results.
Claim 3
Dependent Claim
35 words
The process according to claim 1 including the further step of filling a honeycomb structure with said macroballoons, then heating said structure to a temperature sufficient to cause said macroballoons to bond to said honeycomb.
Claim 4
Dependent Claim
41 words
The process according to claim 1 including the further step of mixing said macroballoons with a portion of said liquid composition and heating the filled honeycomb to a temperature of about 90° to 150° C. to dry and cure said resin.
Claim 5
Dependent Claim
140 words
A process for producing high temperature and flame resistant closed cell foam structure formed by the following process steps: reacting an oximine having the general formula ##STR7## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio therof between 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles between spaced parallel sheets; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a composite closed cell foam layer of substantially uniform density bonded to said sheets.
Claim 6
Dependent Claim
140 words
A process for producing high temperature and flame resistant closed cell foam structure formed by the following process steps: reacting an oximine having the general formula ##STR7## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio therof between 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles between spaced parallel sheets; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a composite closed cell foam layer of substantially uniform density bonded to said sheets.
Claim 7
Dependent Claim
27 words
The process according to claim 4 further including the step of compressing the bonded composite at a temperature of about 150° to 200° C. to increase density.
Claim 8
Dependent Claim
105 words
High temperature and flame resistant macroballoons produced by the following process steps: reacting an oximine having the general formula ##STR8## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio therof between 0.05:1 and 1.5:1 to produce and N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; and foaming said particles by feeding them into a moving hot air stream, whereby discrete macroballoons are produced.
Claim 9
Dependent Claim
105 words
High temperature and flame resistant macroballoons produced by the following process steps: reacting an oximine having the general formula ##STR8## where "x" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio therof between 0.05:1 and 1.5:1 to produce and N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; and foaming said particles by feeding them into a moving hot air stream, whereby discrete macroballoons are produced.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-09 | 1987-07-11 | 1988-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-09 | 1991-07-11 | 1992-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-09 | 1995-07-11 | 1996-01-10 | $7700.00 | Window Closed / Lapsed |