Synthetic resin

Claim 2

A powder finish applied to a substrate containing as essential binder a synthetic resin based on an acrylate copolymer containing epoxide groups and having a number average molecular weight of 1,000 to 30,000, said acrylate copolymer comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 18 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkyl acrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate and glycidyl methacrylate, the total amount of components (a), (b) and (c) being 100%; and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and, upon subsequent baking at an elevated temperature, isocyanate groups are liberated from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings.

Claim 3

A process for preparing a surface coating, which comprises applying a coating composition in the form of a film to a substrate, said coating composition containing as an essential binder a synthetic resin based on an acrylate copolymer containing epoxide groups, having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 8 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and subsequently baking said film at an elevated temperature to liberate isocyanate groups from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings and to give a firmly adhering surface coating.

Claim 4

A process for preparing a surface coating, which comprises applying a coating composition in the form of a film to a substrate, said coating composition containing as an essential binder a synthetic resin based on an acrylate copolymer containing epoxide groups, having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 8 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and subsequently baking said film at an elevated temperature to liberate isocyanate groups from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings and to give a firmly adhering surface coating.

Claim 5

A process for preparing a surface coating, which comprises applying to a substrate, by the electrostatic powder spray process, a powder finish which contains, as essential binder, a synthetic resin based on an acrylate polymer containing epoxide groups having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 18 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and subsequently baking the applied powder finish at an elevated temperature to liberate isocyanate groups from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings and to give a firmly adhering surface coating.

Claim 6

A process for preparing a surface coating, which comprises applying to a substrate, by the electrostatic powder spray process, a powder finish which contains, as essential binder, a synthetic resin based on an acrylate polymer containing epoxide groups having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 18 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and subsequently baking the applied powder finish at an elevated temperature to liberate isocyanate groups from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings and to give a firmly adhering surface coating.

Claim 7

An article coated with a surface coating, wherein the surface coating has been obtained by applying, and subsequently baking, a coating agent which contains, as essential binder, an acrylate copolymer having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 18 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and, upon said subsequent baking at an elevated temperature, isocyanate groups are liberated from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings.

Claim 8

An article coated with a surface coating, wherein the surface coating has been obtained by applying, and subsequently baking, a coating agent which contains, as essential binder, an acrylate copolymer having a number average molecular weight of 1,000 to 30,000 and comprising: (a) 20 to 90% by weight of a first acrylate selected from the group consisting of alkyl acrylate having 1 to 18 carbon atoms in the alkyl radical and alkyl methacrylate having 1 to 20 carbon atoms in the alkyl radical; (b) 5 to 40% by weight of a second acrylate having hydroxyl groups selected from the group consisting of hydroxyalkylacrylate and hydroxyalkylmethacrylate; and (c) 5 to 40% by weight of monomers containing epoxide groups selected from the group consisting of glycidyl acrylate, and glycidyl methacrylate, the total amount of components (a), (b), and (c) being 100%, and said hydroxyl groups of said second acrylate having been reacted in solution at 60°-100° C. with a partially blocked isocyanate selected from the group consisting of diisocyanate and polyisocyanate to a free isocyanate content of less than 1% and, upon said subsequent baking at an elevated temperature, isocyanate groups are liberated from said blocked isocyanate to react with said epoxide groups of component (c) to form oxazolidinone rings.

Claim 9

The powder finish of claim 1, further comprising component (d) comprising 0.1 to 35% by weight, relative to the total amount of components (a), (b), and (c), of a copolymerizable vinyl compound.

Claim 10

The process of claim 2, further comprising component (d) comprising 0.1 to 35% by weight, relative to the total amount of components (a), (b) and (c), of a copolymerizable vinyl compound.

Claim 11

The process of claim 3, further comprising component (d) comprising 0.1 to 35% by weight, relative to the total amount of components (a), (b) and (c), of a copolymerizable vinyl compound.

Claim 12

The article of claim 4, further comprising component (d) comprising 0.1 to 35% by weight, relative to the total amount of components (a), (b), and (c), of a copolymerizable vinyl compound.