Abstract A method of making fluoride glasses produces fluoride glass having such low OH and low oxide content that the extrinsic optical absorbance caused by the OH vibration at 2.9μ is eliminated or substantially reduced. In the method, a glass charge is placed in a capped crucible and dry argon gas is caused to flow through the capped crucible while the temperature is raised to melt the charge. Thereafter, while the dry argon gas flow is continued, the temperature in the furnace is held constant for a time sufficient to obtain a homogenous melt in which all crystalline materials are dissolved. The temperature is then lowered to a value between the glass crystalization temperature and the sublimation temperature of ZrF 4 and then, at isothermal conditions, the flow of dry argon gas is replaced by a flow of SF 6 gas or by a flow of CF 4 gas. At the lowered temperature, the SF 6 or CF 4 gas flow is maintained for a time sufficient to eliminate or greatly reduce OH and oxides in the glass melt. Thereafter, the melt is allowed to cool in a still water-free environment.
A method of making fluoride glasses having low OH and low oxide content, comprising the steps of: (i) placing a fluoride glass charge containing ZrF 4 a crucible having a cap extending over the charge said cap providing a capped space above the charge and said cap being shaped such that gases can be fed into and out of the capped crucible, (ii) disposing the capped charged crucible in a heating chamber, (iii) causing dry argon gas to flow into through, and then out of the capped crucible while raising the temperature to thereby melt the charge in the crucible, (iv) continuing the flow of dry argon gas into through, and then out of the capped crucible while maintaining a constant temperature for a sufficient time to obtain a homogeneous melt in which all crystalline materials are dissolved, (v) while maintaining a water-free atmosphere over the melt, lowering the temperature in the heating chamber to a temperature between the glass crystallization temperature and a temperature near the sublimation temperature of ZrF 4 , (vi) maintaining said lowered temperature while causing a flow of a gas selected from the group of SF 6 and CF 4 to enter the capped space above the melt and flow therethrough for a time sufficiently long to substantially reduce OH and oxides in the glass melt, and (vii) cooling the crucible and its contents while maintaining them in a water-free environment.
Claim 2
Independent Claim
236 words
A method of making fluoride glasses having low OH and low oxide content, comprising the steps of: (i) placing a fluoride glass charge containing ZrF 4 a crucible having a cap extending over the charge said cap providing a capped space above the charge and said cap being shaped such that gases can be fed into and out of the capped crucible, (ii) disposing the capped charged crucible in a heating chamber, (iii) causing dry argon gas to flow into through, and then out of the capped crucible while raising the temperature to thereby melt the charge in the crucible, (iv) continuing the flow of dry argon gas into through, and then out of the capped crucible while maintaining a constant temperature for a sufficient time to obtain a homogeneous melt in which all crystalline materials are dissolved, (v) while maintaining a water-free atmosphere over the melt, lowering the temperature in the heating chamber to a temperature between the glass crystallization temperature and a temperature near the sublimation temperature of ZrF 4 , (vi) maintaining said lowered temperature while causing a flow of a gas selected from the group of SF 6 and CF 4 to enter the capped space above the melt and flow therethrough for a time sufficiently long to substantially reduce OH and oxides in the glass melt, and (vii) cooling the crucible and its contents while maintaining them in a water-free environment.
Claim 3
Dependent Claim
32 words
The method according to claim 1, further including the step of (viii) purging the heating chamber by causing dry argon gas to flow therethrough before raising the temperature to melt the charge.