Catalysis over activated zeolites

Claim 2

A process for converting a feedstock comprising an alcohol, ether or mixture thereof to conversion products comprising hydrocarbons which comprises contacting said feedstock at conversion conditions with a catalyst composition comprising a supported crystalline zeolite, said zeolite having an initial silica-to-alumina mole ratio greater than about 100, prepared by a method which comprises compositing said crystalline zeolite with alumina, reacting the composite with a dilute aqueous solution of hydrogen fluoride of from about 0.1 to about 5 Normal at a temperature of from about 0° C. to about 30° C. for a time of less than about 60 minutes, drying the hydrogen fluoride reacted composite, treating the dried hydrogen fluoride reacted composite by contact with an ammonium salt solution, by hydrolysis or ammonolysis, and calcining the resulting material at a temperature of from about 200° C. to about 600° C.

Claim 3

The process of claim 1 wherein said zeolite has a silica-to-alumina mole ratio greater than about 500.

Claim 4

The process of claim 1 wherein said dried hydrogen fluoride reacted composite is treated by contact with an ammonium salt solution.

Claim 5

The process of claim 3 wherein the ammonium salt is selected from the group consisting of ammonium nitrate, ammonium sulfate and ammonium chloride.

Claim 6

The process of claim 4 wherein said ammonium salt is ammonium nitrate.

Claim 7

The process of claim 1 wherein said composite is formed as an extrudate prior to said reacting with a dilute aqueous solution of hydrogen fluoride.

Claim 8

The process of claim 6 wherein said zeolite has a silica-to-alumina mole ratio greater than about 500.

Claim 9

The process of claim 6 wherein said dried hydrogen fluoride reacted extrudate is treated by contact with an ammonium salt solution.

Claim 10

The process of claim 1 wherein said dried hydrogen fluoride reacted composite is treated by hydrolysis.

Claim 11

The process of claim 1 wherein said dried hydrogen fluoride reacted composite is treated by ammonolysis.

Claim 12

The process of claim 6 wherein said dried hydrogen fluoride reacted extrudate is treated by hydrolysis.

Claim 13

The process of claim 6 wherein said dried hydrogen fluoride reacted extrudate is treated by ammonolysis.

Claim 14

The process of claim 1 wherein said zeolite has the structure of ZSM-5, ZSM-11, ZSM-5/ZSM-11 intermediate, ZSM-12, ZSM-23, ZSM-35, ZSM-38 or ZSM-48.

Claim 15

The process of claim 13 wherein said zeolite has the structure of ZSM-5 or ZSM-11.

Claim 16

The process of claim 6 wherein said zeolite has the structure of ZSM-5, ZSM-11, ZSM-5/ZSM-11 intermediate, ZSM-12, ZSM-23, ZSM-35, ZSM-38 or ZSM-48.

Claim 17

The process of claim 15 wherein said zeolite has the structure of ZSM-5 or ZSM-11.

Claim 18

The process of claim 1 wherein said conversion conditions include a temperature of from about 100° C. to about 800° C., a pressure of from about 0.1 atmosphere to about 200 atmospheres, a weight hourly space velocity of from about 0.08 hr -1 to about 2000 hr -1 and a hydrogen/feedstock organic compound mole ratio of from 0 to about 100.

Claim 19

The process of claim 1 wherein said conversion conditions include a temperature of from about 275° C. to about 600° C., a pressure of from about 0.5 atmosphere to about 50 atmospheres and a liquid hourly space velocity of from about 0.5 to about 100.

Claim 20

The process of claim 6 wherein said conversion conditions include a temperature of from about 100° C. to about 800° C., a pressure of from about 0.1 atmosphere to about 200 atmospheres, a weight hourly space velocity of from about 0.08 hr -1 to about 2000 hr -1 and a hydrogen/feedstock organic compound mole ratio of from 0 to about 100.

Claim 21

The process of claim 6 wherein said conversion conditions include a temperature of from about 275° C. to about 600° C., a pressure of from about 0.5 atmosphere to about 50 atmospheres and a liquid hourly space velocity of from about 0.5 to about 100.

Claim 22

A process for converting a feedstock comprising an alcohol, ether or mixture thereof to conversion products comprising hydrocarbons which comprises contacting said feedstock at conversion conditions with a catalyst composition comprising a supported crystalline zeolite, said zeolite having an initial silica-to-alumina mole ratio greater than 100 and the structure of zeolite ZSM-5, said catalyst composition being prepared by a method which comprises compositing said crystalline zeolite with alumina, reacting the composite with a dilute aqueous solution of hydrogen fluoride of from about 0.1 to about 5 Normal at a temperature of from about 0° C. to about 30° C. for a time of less than about 60 minutes, drying the hydrogen fluoride reacted composite, treating the dried hydrogen fluoride reacted composite by contact with an ammonium salt solution, by hydrolysis or ammonolysis, and calcining the resulting material at a temperature of from about 200° C. to about 600° C.

Claim 23

A process for converting a feedstock comprising an alcohol, ether or mixture thereof to conversion products comprising hydrocarbons which comprises contacting said feedstock at conversion conditions with a catalyst composition comprising a supported crystalline zeolite, said zeolite having an initial silica-to-alumina mole ratio greater than 100 and the structure of zeolite ZSM-5, said catalyst composition being prepared by a method which comprises compositing said crystalline zeolite with alumina, reacting the composite with a dilute aqueous solution of hydrogen fluoride of from about 0.1 to about 5 Normal at a temperature of from about 0° C. to about 30° C. for a time of less than about 60 minutes, drying the hydrogen fluoride reacted composite, treating the dried hydrogen fluoride reacted composite by contact with an ammonium salt solution, by hydrolysis or ammonolysis, and calcining the resulting material at a temperature of from about 200° C. to about 600° C.