Insulation board and process of making

Claim 2

Insulation board having a density less than 30 pounds per cubic foot and capable of bearing a load, produced by a process comprising: (a) providing a stack of substantially binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 3

Insulation board having a density less than 30 pounds per cubic foot and capable of bearing a load, produced by a process comprising: (a) heating binder-containing glass fiber sheets at a temperature in the range of from equal to, to 400° F. below, the glass strain temperature for a time period sufficient to remove essentially all of the binder material in the glass fiber sheets and providing a stack of said binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 4

Insulation board having a density less than 30 pounds per cubic foot and capable of bearing a load, produced by a process comprising: (a) heating binder-containing glass fiber sheets at a temperature in the range of from equal to, to 400° F. below, the glass strain temperature for a time period sufficient to remove essentially all of the binder material in the glass fiber sheets and providing a stack of said binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 5

The insulation board of claims 1 or 2 having a density of from 14 to less than 30 pounds per cubic foot.

Claim 6

The insulation board of claims 1 or 2 wherein step (c) is accomplished by heating the stack and the press together.

Claim 7

The insulation board of claims 1 or 2 wherein a part of step (c) is accomplished by heating the stack and the press separately.

Claim 8

The insulation board of claims 1 or 2 wherein the temperature range of step (c) is from 100° F. greater than the strain temperature to 200° F. below the glass softening temperature.

Claim 9

The insulation board of claims 1 or 2 wherein the light vertically compressive force is from 0.5 to 1.5 pounds per square inch.

Claim 10

The insulation board of claims 1 or 2 wherein the time period of step (d) is from 2 to 16 hours.

Claim 11

The insulation board of claims 1 or 2 wherein the glass fiber sheets are comprised of glass fibers having a diameter of from 0.2 to 13 microns.

Claim 12

A process for producing insulation board having a density of less than 30 pounds per cubic foot and capable of bearing a load comprising: (a) providing a stack of substantially binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 13

A process for producing insulation board having a density of less than 30 pounds per cubic foot and capable of bearing a load comprising: (a) providing a stack of substantially binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 14

A process for producing insulation board having a density of less than 30 pounds per cubic foot and capable of bearing a load comprising: (a) heat binder-containing glass fiber sheets at a temperature in the range of from equal to, to 400° F. below, the glass strain temperature for a time period sufficient to remove essentially all of the binder material in the glass fiber sheets and providing a stack of said binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 15

A process for producing insulation board having a density of less than 30 pounds per cubic foot and capable of bearing a load comprising: (a) heat binder-containing glass fiber sheets at a temperature in the range of from equal to, to 400° F. below, the glass strain temperature for a time period sufficient to remove essentially all of the binder material in the glass fiber sheets and providing a stack of said binderless glass fiber sheets in an amount sufficient to achieve insulation board of desired density less than 30 pounds per cubic foot; (b) providing a press to compress the stack; (c) heating the stack and the press to a temperature in the range of from the glass strain temperature to less than the glass softening temperature for a time period sufficient to achieve thermal equilibration of the stack and the press surface; (d) thereafter compressing the stack by applying a light vertically compressive force of from 0.2 to 5.0 pounds per square inch to the stack with the press, at said thermal equilibrium for a time period sufficient to produce insulation board of desired density and to substantially relieve stress within the board; and (e) cooling the compressed glass fiber stack to ambient temperature.

Claim 16

The process of claims 10 or 11 wherein the density is from 14 to less than 30 pounds per cubic foot.

Claim 17

The process of claims 10 or 11 wherein step (c) is accomplished by heating the stack and the press together.

Claim 18

The process of claims 10 or 11 wherein a part of step (c) is accomplished by heating the stack and the press separately.

Claim 19

The process of claims 10 or 11 wherein the temperature range of step (c) is from 100° F. greater than the strain temperature to 200° F. below the glass softening temperature.

Claim 20

The process of claims 10 or 11 wherein the light vertically compressive force is from 0.5 to 1.5 pounds per square inch.

Claim 21

The process of claims 10 or 11 wherein the time period of step (d) is from 2 to 16 hours.

Claim 22

The process of claims 10 or 11 wherein the glass fiber sheets are comprised of glass fibers having a diameter of from 0.2 to 13 microns.

Claim 23

Insulation board essentially free of binder, capable of bearing a load and having a density less than 30 pounds per cubic foot comprised of compressed glass fibers oriented essentially in planes parallel to one another so as to have substantially only point contact between fibers.

Claim 24

Insulation board essentially free of binder, capable of bearing a load and having a density less than 30 pounds per cubic foot comprised of compressed glass fibers oriented essentially in planes parallel to one another so as to have substantially only point contact between fibers.