Polyethylene composition
Assignee: Fidia SpA
•
Filing: 1984-04-12
•
Granted: 1985-08-20
•
Expires: 2004-04-12
Abstract
Abstract A polyethylene composition comprising three specific types of polyethylenes; polyethylene (A), polyethylene (B) and polyethylene (C) respectively. The polyethylene composition has a melt index not less than 0.001 g/10 min. and not more than 10 g/cm and exhibits excellent processability under variant molding techniques. Molded objects exhibit excellent physical properties such as impact strength environmental stress cracking resistance and uniform thickness distribution. Polyethylene (A) has a molecular weight of from 5,000 to 90,000 and polyethylene (C) has a molecular weight of from 100,000 to 1,500,000 and the ratio of the molecular weight of polyethylene (C)/the molecular weight of polyethylene (A) is from 4 to 200. Polyethylene (B) has a molecular weight of from 50,000 to 500,000, being prepared by a polymerization with use of a chromium compound-supported type catalyst capable of producing a specifically conditioned homopolyethylene with respect to the properties of the polymers in terms of flow ratio and die swell.
Inventors
- 👤 Kisoo Moriguchi
- 👤 Tadashi Ikegami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:52
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L23/08; C08L23/0807; C08L23/0815; C08L2205/00; C08L2205/02; C08L2205/025; C08L2205/03
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
231 words
A polyethylene composition comprising three types of polyethylene (A), (B) and (C) selected from the group consisting of homopolymers of ehtylene and copolymers of ethylene and an α-olefin, wherein (i) the polyethylene (A) has a molecular weight of from 5,000 to 90,000, the polyethylene (C) having a molecular weight of from 100,000 to 1,500,000 and the ratio of the molecular weight of the polyethylene (C)/ the molecular weight of polyethylene (A) being between 4 and 200, and the polyethylene (A) and the polyethylene (C) are produced by a polymerization using a magnesium-containing Ziegler type catalyst, (ii) the polyethylene (B) has a molecular weight of from 50,000 to 500,000 produced by a polymerization using a chromium compound supported type catalyst capable of producing a homopolymer of ethylene in a single stage polymerization having a flow ratio of from 40 to 150 and a die swell of from 40 to 100 g/20 cm measured at the condition in which the said homopolymer exhibits a melt index of 1 g/10 min., (iii) the ratio of the polyethylene (A) and the polyethylene (C) by weight is from 70 to 30 to 30 to 70, and the amount of the polyethylene (B) in the composition ranges from 10% by weight to 75% by weight, and (iv) the melt index of the composition is not less than 0.001 g/10 min., and not more than 10 g/100 min.
Claim 2
Dependent Claim
231 words
A polyethylene composition comprising three types of polyethylene (A), (B) and (C) selected from the group consisting of homopolymers of ehtylene and copolymers of ethylene and an α-olefin, wherein (i) the polyethylene (A) has a molecular weight of from 5,000 to 90,000, the polyethylene (C) having a molecular weight of from 100,000 to 1,500,000 and the ratio of the molecular weight of the polyethylene (C)/ the molecular weight of polyethylene (A) being between 4 and 200, and the polyethylene (A) and the polyethylene (C) are produced by a polymerization using a magnesium-containing Ziegler type catalyst, (ii) the polyethylene (B) has a molecular weight of from 50,000 to 500,000 produced by a polymerization using a chromium compound supported type catalyst capable of producing a homopolymer of ethylene in a single stage polymerization having a flow ratio of from 40 to 150 and a die swell of from 40 to 100 g/20 cm measured at the condition in which the said homopolymer exhibits a melt index of 1 g/10 min., (iii) the ratio of the polyethylene (A) and the polyethylene (C) by weight is from 70 to 30 to 30 to 70, and the amount of the polyethylene (B) in the composition ranges from 10% by weight to 75% by weight, and (iv) the melt index of the composition is not less than 0.001 g/10 min., and not more than 10 g/100 min.
Claim 3
Dependent Claim
22 words
A polyethylene composition according to claim 1, wherein the polyethylene (A) and the polyethylene (C) are prepared by a two stage polymerization.
Claim 4
Dependent Claim
78 words
A polyethylene composition according to claim 1, wherein the polyethylene (B) is produced by polymerization using a chromium compound supported type catalyst combined with an organometallic compound capable of producing a homopolymer of ethylene in a single stage polymerization having a flow ratio of from 50 to 120 and a die swell of from 50 g/20 cm to 80 g/20 cm measured at the condition in which the said polyethylene exhibits a melt index of 1 g/10 min.
Claim 5
Dependent Claim
87 words
A polyethylene composition according to claim 1, wherein the molecular weight of the polyethylene (B) is within a range from 70,000 to 400,000 and the ratio of the molecular weight of polyethylene (B)/the molecular weight of the polyethylene (A) is 1.2 or more, the ratio of the molecular weight of the polyethylene (B)/ the molecular weight of polyethylene (C) is 0.9 or less, and the molecular weight of the polyethylene consisting of the polyethylene (A) and the polyethylene (C) is higher than that of the polyethylene (B).
Claim 6
Dependent Claim
98 words
A polyethylene composition according to claim 1, wherein the polyethylene (A) has a molecular weight of from 10,000 to 70,000 and the polyethylene (C) has a molecular weight of from 200,000 to 1,000,000 produced by polymerization using a magnesium containing Ziegler type catalyst which is capable of producing a homopolymer of ethylene in a single stage polymerization having a flow ratio of 20 to less than 50 and a die swell of 20 g/20 cm to less than 50 g/20 cm measured at the condition in which the said homopolymer exhibits a melt index of 1 g/10 min.
Claim 7
Dependent Claim
28 words
A polyethylene composition according to claim 1, wherein the density of the polyethylene composition is in a range of from 0.935 g/cm 3 to 0.965 g/cm 3 .
Claim 8
Dependent Claim
193 words
A polyethylene composition according to claim 1, wherein the polyethylene (A) has a molecular weight of from 10,000 to 70,000 and the polyethylene (C) has a molecular weight of from 200,000 to 1,000,000 which are produced by a polymerization using a magnesium-containing Ziegler type catalyst which is capable of producing a homopolymer of ehtylene in a single stage polymerization having a flow ratio of from 20 to less than 50 and a die swell of from 20 g/20 cm to less than 50 g/20 cm measured at the condition in which the said homopolymer exhibits a melt index of 1 g/10 min. the polyethylene (B) is produced by a polymerization using a chromium compound supported type catalyst combined with an organometallic compound which is capable of producing in a single stage polymerization a homopolymer of ethylene having a flow ratio of from 50 to 120 and a die swell of from 20 g/20 cm to 80 g/20 measured at the condition in which the said homopolymer exhibits a melt index of l/g/10 min. and the amount of the polyethylene lene (B) in the composition ranges from 15% by weight to 60% by weight.
Claim 9
Dependent Claim
28 words
A polyethylene composition according to claim 7, wherein the density of the polyethylene composition is in a range of from 0.935 g/cm 3 to 0.965 g/cm 3 .
References Cited (Backward Citations)
US3127370A
Cited
JPS5197687A
Cited
JPS51107384A
Cited
JPS51148785A
Cited
JPS523677A
Cited
US4230831A
Cited
US4336352A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-19 | 1989-02-18 | 1989-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-19 | 1993-02-18 | 1993-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-19 | 1997-02-18 | 1997-08-20 | $7700.00 | Window Closed / Lapsed |