Absorbing cover for wounds and the method for manufacturing thereof
Assignee: Czech Academy of Sciences
•
Filing: 1983-09-28
•
Granted: 1985-08-20
•
Expires: 2003-09-28
Abstract
Abstract The invention pertains to the absorbing dressing for wounds, which consists of spherical particles of regenerated cellulose of the size 0.05-0.5 mm (preferably 0.05-0.3 mm) and a macroporous structure characterized by the cyclohexane regain of the dry material at least 0.2 ml/g. The dressing is prepared from the regenerated cellulose swollen with water by replacement with organic solvents and the subsequent drying of the product swollen with the said solvent. The porous structure of the dressing warrants that it can absorb excretions of the wound in the amount 1.5 to 5 g water per g of solids; the grainy macrostructure remains preserved during the absorption so that the material applied on the wound in the form of a powder in the layer 2-5 mm thick, in particular 2-3 mm thick, can be without difficulties and almost without pain rinsed away with water.
Inventors
- 👤 Fritz Loth
- 👤 Horst Dautzenberg
- 👤 Jiri Stamberg
- 👤 Jan Peska
- 👤 Dieter Bertram
- 👤 Herbert Lettau
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:11
CPC Classifications
A; A61; A61L; A61L26/00; A61L26/0009; A61L26/0023
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
70 words
A powder dressing for wounds comprising spherical particles of water swollen regenerated cellulose beads wherein the water had first been replaced by an organic solvent, the solvent sequentially removed and the beads dried, said particles having a diameter of between 0.05 to 0.5 mm and a macroporous structure characterized by a porosity in the dry state corresponding to the cyclohexane regain of at least 0.2 ml/g of the dry material.
Claim 2
Dependent Claim
70 words
A powder dressing for wounds comprising spherical particles of water swollen regenerated cellulose beads wherein the water had first been replaced by an organic solvent, the solvent sequentially removed and the beads dried, said particles having a diameter of between 0.05 to 0.5 mm and a macroporous structure characterized by a porosity in the dry state corresponding to the cyclohexane regain of at least 0.2 ml/g of the dry material.
Claim 3
Dependent Claim
17 words
The dressing according to claim 1 wherein the particles have a diameter of 0.05 to 0.3 mm.
Claim 4
Independent Claim
158 words
A method for forming a powder dressing for wounds which consists of the sequence of steps of water swelling a mass of regenerated cellulose beads, contacting said water swollen beads with one of an organic solvent solution selected from the group consisting of (a) a water miscible, (b) a partly water miscible, or (c) a mixture of a water miscible and a water immisible organic solvent, and capable of absorbing at least 5% water to form a mixture of solvent and water, removing the water from said mixture until all the water in said mixture and said beads is replaced with solvent and said solvent maintains said beads swollen, removing said solvent and drying said beads, and separating from said dried beads those particles having a diameter of at least 0.05 mm and a macroporous structure characterized by a porosity in the dry state corresponding to the cyclohexane regain of at least 0.2 ml/g of the dry material.
Claim 5
Independent Claim
158 words
A method for forming a powder dressing for wounds which consists of the sequence of steps of water swelling a mass of regenerated cellulose beads, contacting said water swollen beads with one of an organic solvent solution selected from the group consisting of (a) a water miscible, (b) a partly water miscible, or (c) a mixture of a water miscible and a water immisible organic solvent, and capable of absorbing at least 5% water to form a mixture of solvent and water, removing the water from said mixture until all the water in said mixture and said beads is replaced with solvent and said solvent maintains said beads swollen, removing said solvent and drying said beads, and separating from said dried beads those particles having a diameter of at least 0.05 mm and a macroporous structure characterized by a porosity in the dry state corresponding to the cyclohexane regain of at least 0.2 ml/g of the dry material.
Claim 6
Dependent Claim
43 words
The method according to claim 3 wherein the water swollen beads is contacted with 2 to 20 volumes of said organic solvent per one volume of said swollen beads at a temperature between the ambient temperature and the boiling temperature of the solvent.
Claim 7
Dependent Claim
35 words
The method according to claim 3 wherein the step of removing the water from the solvent-water mixture is effected by distillation of said solvent and water and the separation of the water from said distillate.
Claim 8
Dependent Claim
33 words
The method according to claim 3 wherein the step of removing the water from the solvent-water mixture is effected by elution of said mixture and the separation of the water from the elute.
Claim 9
Dependent Claim
26 words
The method according to claim 5 wherein after removal of the water from the distillate, the solvent is reintroduced into contact with said water swollen beads.
Claim 10
Dependent Claim
26 words
The method according to claim 6 wherein after removal of the water from the elute, the solvent is reintroduced into contact with said water swollen beads.
Claim 11
Dependent Claim
34 words
The method according to claim 5 wherein after removal of the water from the distillate, the phase of the solvent immiscible with water is isolated and reintroduced into contact with said water swollen beads.
Claim 12
Dependent Claim
34 words
The method according to claim 6 wherein after removal of the water from the elute, the phase of the solvent immiscible with water is isolated and reintroduced into contact with said water swollen beads.
Claim 13
Dependent Claim
38 words
The method according to claim 3 wherein the water-miscible phase of said solvents is selected from the group comprising aliphatic alcohols and ketones with one to three carbon atoms in the molecule, advantageously from ethanol, 2-propanol, and acetone.
Claim 14
Dependent Claim
39 words
The method according to claim 3 wherein the said solvents limitedly miscible with water are selected from the group comprising aliphatic alcohols and ketones with four to five carbon atoms in the molecule, advantageously from 1-butanol, 2-butanol, and 2-butanone.
Claim 15
Dependent Claim
34 words
The method according to claim 3 wherein the said water-immiscible solvents are selected from the group comprising aromatic hydrocarbons and their derivatives and cycloaliphatic hydrocarbons, advantageously from benzene, toluene, xylene, chlorobenzene, cyclohexane, and methylcyclohexane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-19 | 1989-02-18 | 1989-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-19 | 1993-02-18 | 1993-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-19 | 1997-02-18 | 1997-08-20 | $7700.00 | Window Closed / Lapsed |