Cement for the manufacture of cores and moulds and method for preparing same

Assignee: VSESOJUZNY NAUCHNO-ISSLEDOVATELSKY I PROEKTNY INSTITUT ALJUMINIEVOI MAGNIEVOI I ELEKTRODNOI PROMYSHLENNOSTI
•
Filing: 1983-05-05
•
Granted: 1985-08-20
•
Expires: 2003-05-05
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract The cement of the invention comprises chemically combined oxides, percent by mass: CaO, 50 to 60; Al2O3, 28 to 37; Fe2O3, 0.01 to 1; SiO2, 0.1 to 8; Na2O, 0.1 to 1; K2O, 0.1 to 0.5; H2O, 3 to 12; and incorporates 85 to 99% by mass of a fraction with a particle size of below 80 mu m and 1 to 15% by mass of a fraction with a particle size of from 80 to 200 mu m. The cement can also contain one or more additives: calcium oxide or calcium hydroxide, calcium carbonate, calcium carboaluminate. The method according to the invention for preparing said cement comprises a heat-treatment of calcium hydroalumosilicate containing SiO2 in an amount of not more than 8% by mass at a temperature of from 250 DEG to 600 DEG C. The heat-treated product is disintegrated to produce 85 to 99% by mass of a fraction with a particle size of below 80 mu m and 1 to 15% of a fraction with a particle size of from 80 to 200 mu m. During the heat-treatment of the hydroalumosilicate at least one component can be added calcium oxide or calcium hydroxide, calcium carbonate, calcium carboaluminate. The cement is useful in foundry engineering for the manufacture of articles from ferrous and non-ferrous metals.

Inventors

  • 👤 Nikolai A. Kaluzhsky
  • 👤 Khoren A. Badaliants
  • 👤 Ivan M. Kostin
  • 👤 Isaak A. Zatulovsky
  • 👤 Valentin I. Korneev
  • 👤 Vladimir V. Andreev
  • 👤 Boris A. Kuzmin
  • 👤 Viktor M. Sizyakov
  • 👤 Nikolai S. Shmorgunenko
  • 👤 Vladislav A. Krochevsky
  • 👤 Alexei I. Alexeev

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-07 13:32
CPC Classifications
C; C04; C04B; C04B7/00; C04B7/32; B; B22; B22C; B22C1/00; B22C1/16; B22C1/18; B22C1/181

Claims Analysis

Total Claims: 5
Claim 1
Independent Claim 103 words
A cement for the manufacture of cores and moulds containing chemically combined oxides, with the following percent by weight: CaO, 50 to 60; Al 2 O 3 , 28 to 37; Fe 2 O 3 , 0.01 to 1; SiO 2 , 0.1 to 8; Na 2 O, 0.1 to 1; K 2 O, 0.1 to 0.5; H 2 O, 3 to 12; and having the following grain-size distribution: 85 to 99% by weight of a fraction with a particle size below 80 μm and 1 to 15% by weight of a fraction with a particle size of from 80 to 200 μm.
Claim 2
Dependent Claim 103 words
A cement for the manufacture of cores and moulds containing chemically combined oxides, with the following percent by weight: CaO, 50 to 60; Al 2 O 3 , 28 to 37; Fe 2 O 3 , 0.01 to 1; SiO 2 , 0.1 to 8; Na 2 O, 0.1 to 1; K 2 O, 0.1 to 0.5; H 2 O, 3 to 12; and having the following grain-size distribution: 85 to 99% by weight of a fraction with a particle size below 80 μm and 1 to 15% by weight of a fraction with a particle size of from 80 to 200 μm.
Claim 3
Dependent Claim 83 words
A method for preparing a cement according to claim 1, comprising heat-treating calcium hydroalumosilicate containing at most 8% by weight of SiO 2 at a temperature within the range of from 250° to 600° C., disintegrating the heat-treated product to obtain a fraction with a particle size of below 80 μm in an amount of 85 to 99% by weight and a fraction with a particle size of from 80 to 200 μm in an amount of from 1 to 15% by weight.
Claim 4
Dependent Claim 38 words
A method according to claim 2, wherein the heat-treatment of calcium hydroalumosilicate is carried out in the presence of at least one additive selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and calcium hydrocarboaluminate.
Claim 5
Dependent Claim 59 words
A method according to claim 3, wherein the additive is at least one member selected from the group consisting of calcium oxide and calcium hydroxide introduced in an amount of from 1 to 10% by weight, calcium carbonate in an amount of 1 to 50% by weight calcium hydrocarboaluminate in an amount of from 1.5 to 30% by weight.

References Cited (Backward Citations)

US2081558A Cited
US2887392A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1988-08-19 1989-02-18 1989-08-20 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1992-08-19 1993-02-18 1993-08-20 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1996-08-19 1997-02-18 1997-08-20 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag