US4536204A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing coated flat glass
Assignee: AGC Glass Europe SA
•
Filing: 1984-05-09
•
Granted: 1985-08-20
•
Expires: 2004-05-09
Abstract
Abstract A metal or metal compound coating 6 is deposited on a face of a hot, freshly formed ribbon 1 of glass during the ribbon's forward travel through a coating station 5 between a forming installation 3 and an annealing lehr 4 by contacting the ribbon face with fluid coating precursor material e.g. sprayed from nozzle 17. Preparatory to the coating step, the ribbon 1 is passed through successive thermal conditioning zones comprising a zone 19 in which temperature gradients across the ribbon are reduced and a following zone in which heat is supplied substantially entirely to a surface layer of the glass at the face to be coated by exposing that face to one or more radiant heaters 22 having a black body temperature below 1100° C. to compensate at least partially for the cooling effect of the coating step on the ribbon 1.
Inventors
- 👤 Robert Van Laethem
- 👤 Albert Van Cauter
- 👤 Robert Terneu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:43
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/001; C03C17/002
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
264 words
A process for producing flat glass coated on one side with a coating comprised of one of a metal and a metal compound, wherein the glass is formed in a flat glass forming installation and subsequently annealed in an annealing installation, said process comprising: advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation; passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon; passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated; contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon; and wherein said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100° C. to compensate at least partially for the cooling effect of said contacting step, and said process further comprises monitoring the temperature of the ribbon surface at the coated side after said contacting step; and controlling the at least one radiant heater so that the coated side complies with predetermined temperature conditions prior to entering the annealing installation.
Claim 2
Dependent Claim
264 words
A process for producing flat glass coated on one side with a coating comprised of one of a metal and a metal compound, wherein the glass is formed in a flat glass forming installation and subsequently annealed in an annealing installation, said process comprising: advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation; passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon; passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated; contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon; and wherein said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100° C. to compensate at least partially for the cooling effect of said contacting step, and said process further comprises monitoring the temperature of the ribbon surface at the coated side after said contacting step; and controlling the at least one radiant heater so that the coated side complies with predetermined temperature conditions prior to entering the annealing installation.
Claim 3
Dependent Claim
26 words
A process according to claim 1, wherein at least one of said passing steps includes differentially heating the one side of the ribbon across its width.
Claim 4
Dependent Claim
44 words
A process according to claim 1, wherein said passing steps include heating the one side of the ribbon so that the temperature across the width of the one side before said contacting step does not vary by an amount in excess of 15° C.
Claim 5
Dependent Claim
37 words
A process according to claim 1, wherein said passing steps include heating the surface of the one side of the ribbon to a mean temperature in the range of 570° to 630° C. before said contacting step.
Claim 6
Dependent Claim
262 words
A process for producing flat glass coated on one side with a coating comprised of one of a metal and a metal compound, wherein the glass is formed in a flat glass forming installation and subsequently annealed in an annealing installation, said process comprising: advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation; passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon; passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated; contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon; and wherein said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100° C. to compensate at least partially for the cooling effect of said contacting step, and said process further comprises monitoring the temperature of opposite points on the respective surfaces of the ribbon after said contacting step; and controlling the at least one radiant heater in dependence upon any difference between the temperatures of such opposite points.
Claim 7
Dependent Claim
262 words
A process for producing flat glass coated on one side with a coating comprised of one of a metal and a metal compound, wherein the glass is formed in a flat glass forming installation and subsequently annealed in an annealing installation, said process comprising: advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation; passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon; passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated; contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon; and wherein said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100° C. to compensate at least partially for the cooling effect of said contacting step, and said process further comprises monitoring the temperature of opposite points on the respective surfaces of the ribbon after said contacting step; and controlling the at least one radiant heater in dependence upon any difference between the temperatures of such opposite points.
Claim 8
Dependent Claim
26 words
A process according to claim 5, wherein at least one of said passing steps includes differentially heating the one side of the ribbon across its width.
Claim 9
Dependent Claim
44 words
A process according to claim 5, wherein said passing steps include heating the one side of the ribbon so that the temperature across the width of the one side before said contacting step does not vary by an amount in excess of 15° C.
Claim 10
Dependent Claim
37 words
A process according to claim 5, wherein said passing steps include heating the surface of the one side of the ribbon to a mean temperature in the range of 570° to 630° C. before said contacting step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-19 | 1989-02-18 | 1989-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-19 | 1993-02-18 | 1993-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-19 | 1997-02-18 | 1997-08-20 | $7700.00 | Window Closed / Lapsed |