Polycarboxylic-alkyleneimine resinous composition and coating composition containing same
Assignee: Nippon Paint Co Ltd
•
Filing: 1983-12-30
•
Granted: 1985-08-13
•
Expires: 2003-12-30
Abstract
Abstract A resinous composition for coating use comprising a resin obtained by the reaction of base resin having as essential groups, both carboxyl groups derived from a polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value and a functional group reactive with a crosslinking agent, and an alkyleneimine compound in an amount equivalent to resinous acid value of 0.01 to 50, the resinous acid value based on said polycarboxylic acid in the final composition being 2 to 50. This is useful for the preparation of a coating composition having improved curing property, storage stability and time color stability.
Inventors
- 👤 Hirotoshi Umemoto
- 👤 Hisaki Tanabe
- 👤 Shinji Nakano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 12:06
CPC Classifications
C; C09; C09D; C09D201/00; C09D201/02; C09D201/06; C09D201/08; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0804; C08G18/0819; C08G18/0823; C09D167/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
128 words
A resinous composition for coating use having a resinous acid value based on the carboxyl groups of a polycarboxylic acid whose tritation midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value of 2 to 50, obtained by the reaction of (A) a basic resin having as essential functional groups both carboxyl groups derived from polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value, and groups reactive with a crosslinking agent and (B) an alkyleneimine compound having at least one alkyleneimine ring of 2 to 3 carbon atoms, in an amount equivalent to a resinous acid value of 0.01 to 50.
Claim 2
Dependent Claim
128 words
A resinous composition for coating use having a resinous acid value based on the carboxyl groups of a polycarboxylic acid whose tritation midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value of 2 to 50, obtained by the reaction of (A) a basic resin having as essential functional groups both carboxyl groups derived from polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value, and groups reactive with a crosslinking agent and (B) an alkyleneimine compound having at least one alkyleneimine ring of 2 to 3 carbon atoms, in an amount equivalent to a resinous acid value of 0.01 to 50.
Claim 3
Dependent Claim
32 words
The composition according to claim 1 wherein the basic resin is selected from the group consisting of acrylic resin, alkyd resin, polyester resin, epoxy resin, polyurethane resin, polyamide resin and polycarbonate resin.
Claim 4
Dependent Claim
160 words
A coating composition being excellent in storage stability, time color stability and low temperature curing properties, comprising (C) a resinous composition having a resinous acid value based on carboxyl groups of a polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value of 2 to 50, obtained by the reaction of (A) a basic resin having as essential functional groups both carboxyl groups derived from a polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value and groups reactive with a crosslinking agent, and (B) an alkyleneimine compound having at least one alkyleneimine ring of 2 to 3 carbon atoms, in an amount equivalent to a resinous acid value of 0.01 to 50, and (D) a crosslinking agent, the solid weight ratio of (C) to (D) being 95-45 to 5-55.
Claim 5
Dependent Claim
160 words
A coating composition being excellent in storage stability, time color stability and low temperature curing properties, comprising (C) a resinous composition having a resinous acid value based on carboxyl groups of a polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value of 2 to 50, obtained by the reaction of (A) a basic resin having as essential functional groups both carboxyl groups derived from a polycarboxylic acid whose titration midpoint potential in non-aqueous potentiometric titration is more than -300 mV in a state capable of developing a resinous acid value and groups reactive with a crosslinking agent, and (B) an alkyleneimine compound having at least one alkyleneimine ring of 2 to 3 carbon atoms, in an amount equivalent to a resinous acid value of 0.01 to 50, and (D) a crosslinking agent, the solid weight ratio of (C) to (D) being 95-45 to 5-55.
Claim 6
Dependent Claim
33 words
The coating composition according to claim 3 wherein the basic resin is selected from the group consisting of acrylic resin, alkyd resin, polyester resin, epoxy resin, polyurethane resin, polyamide resin and polycarbonate resin.
Claim 7
Dependent Claim
14 words
The coating composition according to claim 3 wherein the crosslinking agent is an aminoplast.
Claim 8
Dependent Claim
14 words
The coating composition according to claim 4 wherein the crosslinking agent is an aminoplast.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |