Polymer foam, thermoformed shapes thereof and methods of forming same
Assignee: Pactiv LLC
•
Filing: 1983-12-12
•
Granted: 1985-08-13
•
Expires: 2003-12-12
Abstract
Abstract A foam structure having a density of less than about 20 lbs/ft 3 . The method of forming the same comprising forming a homogeneous melt blend under pressure of a polymer member selected from the group consisting of polyetherimide resin particles, polycarbonate resin particles, a polymer blend of polyphenylene oxide and polystyrene in particle form imbibed with a blowing agent, followed by extrusion of the same into a lower pressure atmosphere. A composition comprising said particles imbibed with methylene chloride, chloroform, 1,1,2-trichloroethane or mixtures thereof. A method of thermoforming said foam in sheet form.
Inventors
- 👤 Charles M. Krutchen
- 👤 Wen-Pao Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:46
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J9/143; C08J9/144; C08J9/145; B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B29C51/00; B29C51/002; B29K; B29K2079/00; C08J2379/00; C08J2379/04; C08J2379/08; Y; Y10; Y10S; Y10S264/00; Y10S264/66; Y10S521/00; Y10S521/918
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
87 words
A polymer in foam form having a density of less than about 20 lbs/ft 3 , wherein said polymer is a solvent imbibable polyetherimide, wherein said solvent is a member selected from the group consisting of methylene chloride, chloroform, 1,1,2-trichloroethane and mixtures thereof wherein said polyetherimide is a polymer of the following structure: ##STR3## wherein n is a positive integer, Ar is a divalent radical containing from 6-20 carbon atoms, R is a bivalent radical selected from the group consisting of aliphthatic, cycloaliphatic aromatic and araliphatic groups.
Claim 2
Dependent Claim
87 words
A polymer in foam form having a density of less than about 20 lbs/ft 3 , wherein said polymer is a solvent imbibable polyetherimide, wherein said solvent is a member selected from the group consisting of methylene chloride, chloroform, 1,1,2-trichloroethane and mixtures thereof wherein said polyetherimide is a polymer of the following structure: ##STR3## wherein n is a positive integer, Ar is a divalent radical containing from 6-20 carbon atoms, R is a bivalent radical selected from the group consisting of aliphthatic, cycloaliphatic aromatic and araliphatic groups.
Claim 3
Dependent Claim
17 words
The foam of claim 1 wherein the precursor of Ar is Bisphenol A and R is phenylene.
Claim 4
Dependent Claim
19 words
A polymer of claim 1 in foam form having a density of less than about 5 lbs/ft 3 .
Claim 5
Dependent Claim
124 words
A thermoformed structure of a polyetherimide foam prepared by the method comprising: (a) subjecting a sheet of said foam having a density of less than 20 lbs./ft 3 to a first temperature sufficient to permit a shape formation to be effected therein; (b) effecting a shape in said sheet while at said temperature; and (c) reducing the temperature of said sheet to a second temperature permitting permanent retention of said shape in said sheet at or below said second temperature wherein said polyetherimide is a polymer of the following structure: ##STR4## wherein n is a positive integer, Ar is a divalent radical containing from 6-20 carbon atoms, R is a bivalent radical selected from the group consisting of aliphthatic, cycloaliphatic, aromatic and araliphatic groups.
Claim 6
Dependent Claim
124 words
A thermoformed structure of a polyetherimide foam prepared by the method comprising: (a) subjecting a sheet of said foam having a density of less than 20 lbs./ft 3 to a first temperature sufficient to permit a shape formation to be effected therein; (b) effecting a shape in said sheet while at said temperature; and (c) reducing the temperature of said sheet to a second temperature permitting permanent retention of said shape in said sheet at or below said second temperature wherein said polyetherimide is a polymer of the following structure: ##STR4## wherein n is a positive integer, Ar is a divalent radical containing from 6-20 carbon atoms, R is a bivalent radical selected from the group consisting of aliphthatic, cycloaliphatic, aromatic and araliphatic groups.
References Cited (Backward Citations)
US3249561A
Cited
US3290261A
Cited
US3277029A
Cited
US3962154A
Cited
US3903224A
Cited
US4263409A
Cited
US4065401A
Cited
US4097425A
Cited
US4280950A
Cited
US4334030A
Cited
US4315076A
Cited
US4361453A
Cited
US4367296A
Cited
US4360486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |