Abstract A process for producing a curable resin comprises reacting (a) at least one cyanate ester compound selected from the group consisting of polyfunctional cyanate esters having 2 or more cyanato groups per one molecule, prepolymers of the cyanate esters or mixtures thereof with (b) at least one compound having 1,2-epoxy group(s) and radical-polymerizable unsaturated double bond(s) in its molecule, the cyanate ester compound (a) and the compound (b) being used so that the ratio of the cyanato group to the 1,2-epoxy group is in the range of about 1:0.25 to about 1:2, in the presence of (c) a radical polymerization inhibitor at a temperature of about 90°--about 140° C. The curable resin produced according to the present invention is capable of giving cured products having excellent heat resistance and electrical properties.
A process for producing a curable resin which comprises reacting (a) at least one cyanate ester compound selected from the group consisting of polyfunctional cyanate esters having 2 or more cyanate groups per one molecule, prepolymers of the cyanate esters or mixtures thereof with (b) at least one compound having at least one 1,2-epoxy group and at least one radical-polymerizable unsaturated double bond, the ratio of the cyanate group of (a) to the 1,2-epoxy group of (b) being in the range of about 1:0.25 to about 1:2, in contact with (c) a radical polymerization inhibitor at a temperature of about 140° C.
Claim 2
Dependent Claim
102 words
A process for producing a curable resin which comprises reacting (a) at least one cyanate ester compound selected from the group consisting of polyfunctional cyanate esters having 2 or more cyanate groups per one molecule, prepolymers of the cyanate esters or mixtures thereof with (b) at least one compound having at least one 1,2-epoxy group and at least one radical-polymerizable unsaturated double bond, the ratio of the cyanate group of (a) to the 1,2-epoxy group of (b) being in the range of about 1:0.25 to about 1:2, in contact with (c) a radical polymerization inhibitor at a temperature of about 140° C.
Claim 3
Dependent Claim
18 words
The process as defined in claim 1 wherein compound (a) is 2,2-bis(4-cyanatophenyl)propane and compound (b) is glycidyl methacrylate.
Claim 4
Dependent Claim
19 words
The process as defined in claim 1 wherein compound (a) is 1,4-dicyanato benzene and compound (b) is glycidyl acrylate.
Claim 5
Dependent Claim
14 words
The process as defined in claim 1 wherein the radical polymerization inhibitor is phenothiazine.
Claim 6
Dependent Claim
13 words
The process as defined in claim 1 wherein air is sparged into mixture.
Claim 7
Dependent Claim
30 words
The process as defined in claim 1 wherein the ratio of the cyanate group of (a) to the 1,2-epoxy group of (b) is in the range of 1:0.5 to 1:1.5.
Claim 8
Dependent Claim
16 words
The process as defined in claim 1 the reaction temperature is between 95° and 130° C.
Claim 9
Dependent Claim
17 words
The process as defined in claim 7 wherein the reaction temperature is between 100° and 125° C.