Flexibilized chemically resistant epoxy resin
Assignee: Ameron Inc
•
Filing: 1983-01-21
•
Granted: 1985-07-30
•
Expires: 2003-01-21
Abstract
Abstract A method for flexibilizing an epoxy resin is disclosed which comprises (a) preparing a dicarboxy-terminated prepolymer by reacting a carboxylic anhydride with a polybutadiene having a minor amount of pendant vinyl groups at a temperature from about 125° to about 140° F.; (b) reacting the prepolymer with an excess of liquid epoxy resin at a temperature from about 180° to about 200° F.; (c) adding a vinyl monomer in an amount of about 2% to about 25% of the mixture; and (d) adding epoxy and vinyl polymerization catalysts to cure the mixture.
Inventors
- 👤 James A. Seneker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:39
CPC Classifications
C; C08; C08F; C08F290/00; C08F290/08; C08F290/12; C08F290/128; C08C; C08C19/00; C08C19/30; C08C19/34; C08C19/38; C08G; C08G59/00; C08G59/02; C08G59/12
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
215 words
A method for flexibilizing an epoxy resin having at least two terminal epoxy groups comprising: (a) preparing a dicarboxy-terminated prepolymer by reacting a stoichiometric excess of a carboxylic anhydride with each hyroxyl equivalent of a polybutadiene having terminal allylic hydroxyl groups and a minor amount of pendent vinyl groups, at a temperature of from about 125° to about 140° and for a time sufficient for substantially all of the terminal hydroxyl groups to form first ester linkages with anhydride molecules resulting in a prepolymer having a functional carboxyl group at each end; (b) reacting an excess of a liquid epoxy resin with each carboxyl equivalent of the dicarboxy-terminated prepolymer at a temperature of from about 180° F. to about 200° F. for a time sufficient to yield an elastomerically modified resin having at least two terminal epoxy groups, the epoxy resin in such elastomerically modified resin being linked to the prepolymer via a second ester linkage; (c) mixing a vinyl monomer in an amount of from about 2% to about 25% by weight of the elastomerically modified resin with the elastomerically modified resin to yield an uncured product; and (d) mixing epoxy and vinyl polymerization catalysts to the uncured product to effect epoxy copolymerization and vinyl copolymerization to thereby yield a cured flexibilized resinous mass.
Claim 2
Independent Claim
215 words
A method for flexibilizing an epoxy resin having at least two terminal epoxy groups comprising: (a) preparing a dicarboxy-terminated prepolymer by reacting a stoichiometric excess of a carboxylic anhydride with each hyroxyl equivalent of a polybutadiene having terminal allylic hydroxyl groups and a minor amount of pendent vinyl groups, at a temperature of from about 125° to about 140° and for a time sufficient for substantially all of the terminal hydroxyl groups to form first ester linkages with anhydride molecules resulting in a prepolymer having a functional carboxyl group at each end; (b) reacting an excess of a liquid epoxy resin with each carboxyl equivalent of the dicarboxy-terminated prepolymer at a temperature of from about 180° F. to about 200° F. for a time sufficient to yield an elastomerically modified resin having at least two terminal epoxy groups, the epoxy resin in such elastomerically modified resin being linked to the prepolymer via a second ester linkage; (c) mixing a vinyl monomer in an amount of from about 2% to about 25% by weight of the elastomerically modified resin with the elastomerically modified resin to yield an uncured product; and (d) mixing epoxy and vinyl polymerization catalysts to the uncured product to effect epoxy copolymerization and vinyl copolymerization to thereby yield a cured flexibilized resinous mass.
Claim 3
Dependent Claim
44 words
A method according to claim 1 further comprising prior to step (d): diluting the elastomeric modified resin with sufficient additional epoxy resin to yield an uncured mass wherein the polybutadiene moiety comprises from about 15% to about 50% by weight of the uncured mass.
Claim 4
Dependent Claim
26 words
A method according to claim 2 wherein the concentration of the polybutadiene moiety is from about 20% to about 30% by weight of the uncured mass.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein the vinyl monomer is selected from the group consisting of vinyl versatate, styrene, vinyl toluene, and mixtures thereof.
Claim 6
Dependent Claim
24 words
A method according to claim 1 wherein the concentration of vinyl monomer is from about 5% to 10% by weight of the resinous mass.
Claim 7
Dependent Claim
25 words
A method according to claim 1 wherein the epoxy copolymerization catalyst is selected from the group consisting of aromatic amines, polymides, imidazolines, and Lewis acids.
Claim 8
Dependent Claim
24 words
A method according to claim 1 wherein the vinyl copolymerization catalyst is selected from the group consisting of peroxides, azobisisobutyronitrile, and free radical generators.
Claim 9
Dependent Claim
15 words
A method according to claim 1 wherein the carboxylic anhydride contains a carbon-carbon unsaturated bond.
Claim 10
Dependent Claim
25 words
A method according to claim 1 wherein the reaction of step (a) is performed at a temperature of from about 130° C. to 135° C.
Claim 11
Dependent Claim
18 words
A method according to claim 9 wherein the reaction of step (a) is performed for about two hours.
Claim 12
Independent Claim
196 words
A method for flexibilizing an epoxy resin comprising: (a) ester linking a liquid epoxy resin having at least two terminal epoxy groups with a polybutadiene moiety having at least two terminal hydroxyl groups and a minor amount of pendent vinyl groups to thereby form an elastomerically modified resin by reacting each hydroxyl equivalent of the polybutadiene moiety with a stoichiometric excess of a carboxylic anhydride at a temperature sufficiently low to essentially prevent the evolution of water to thereby generate a precursor having a functional carboxyl group at each end, and then, reacting an excess of the epoxy resin with each carboxyl equivalent of the precursor at a sufficient temperature and for a time sufficient to reduce the acid value of the reaction mixtures to less than about 10 to thereby generate the elastomerically modified resin; (b) mixing a vinyl monomer in an amount of from about 2% to about 25% by weight of the elastomerically modified resin with the formed elastomerically modified resin to form an uncured mass; and (c) concurrently copolymerizing epoxy groups and copolymerizing vinyl groups by adding epoxy and vinyl polymerization catalysts to the uncured mass to yield a flexibilized epoxy resin.
Claim 13
Independent Claim
196 words
A method for flexibilizing an epoxy resin comprising: (a) ester linking a liquid epoxy resin having at least two terminal epoxy groups with a polybutadiene moiety having at least two terminal hydroxyl groups and a minor amount of pendent vinyl groups to thereby form an elastomerically modified resin by reacting each hydroxyl equivalent of the polybutadiene moiety with a stoichiometric excess of a carboxylic anhydride at a temperature sufficiently low to essentially prevent the evolution of water to thereby generate a precursor having a functional carboxyl group at each end, and then, reacting an excess of the epoxy resin with each carboxyl equivalent of the precursor at a sufficient temperature and for a time sufficient to reduce the acid value of the reaction mixtures to less than about 10 to thereby generate the elastomerically modified resin; (b) mixing a vinyl monomer in an amount of from about 2% to about 25% by weight of the elastomerically modified resin with the formed elastomerically modified resin to form an uncured mass; and (c) concurrently copolymerizing epoxy groups and copolymerizing vinyl groups by adding epoxy and vinyl polymerization catalysts to the uncured mass to yield a flexibilized epoxy resin.
Claim 14
Dependent Claim
25 words
A method according to claim 11 wherein the vinyl monomer is selected from the group consisting of vinyl versatate, styrene, vinyl toluene, and mixtures thereof.
Claim 15
Dependent Claim
14 words
A method according to claim 11 wherein the anhydride contains a carbon-carbon unsaturated bond.
Claim 16
Dependent Claim
114 words
A curable resin composition comprising an admixture of a vinyl monomer and a prepolymer formed by reacting at a temperature of from about 180° to about 200° F. a liquid diepoxide resin with the product formed by reacting of a polybutadiene moiety having at least two terminal hydroxyl groups and a minor amount of pendent vinyl groups and a carboxylic anhydride at a temperature of from about 125° to about 140° F., wherein approximately one chemical equivalent of carboxylic anhydride is provided for each equivalent of terminal hydroxyl groups supplied by the polybutadiene moiety, and wherein at least two chemical equivalents of epoxide are provided by the diepoxide resin for each equivalent of anhydride.
Claim 17
Dependent Claim
114 words
A curable resin composition comprising an admixture of a vinyl monomer and a prepolymer formed by reacting at a temperature of from about 180° to about 200° F. a liquid diepoxide resin with the product formed by reacting of a polybutadiene moiety having at least two terminal hydroxyl groups and a minor amount of pendent vinyl groups and a carboxylic anhydride at a temperature of from about 125° to about 140° F., wherein approximately one chemical equivalent of carboxylic anhydride is provided for each equivalent of terminal hydroxyl groups supplied by the polybutadiene moiety, and wherein at least two chemical equivalents of epoxide are provided by the diepoxide resin for each equivalent of anhydride.
Claim 18
Dependent Claim
31 words
The resin composition of claim 14 wherein the anhydride is selected from the group consisting of tetrahydrophthalic anhydride and maleic anhydride, and the polybutadiene moiety is generated from a diolefin butadiene.
Claim 19
Dependent Claim
25 words
The resin composition of claim 14 wherein the vinyl monomer is selected from the group consisting of vinyl versatate, styrene, vinyl toluene, and mixtures thereof.
Claim 20
Dependent Claim
42 words
The resin composition of claim 14 further comprising an epoxy curing catalyst selected from the group consisting of aromatic amines, polyamides, imidazolines, and Lewis acids and a vinyl curing catalyst selected from the group consisting of peroxides, azobisisobutyronitrile and free radical generators.
Claim 21
Dependent Claim
23 words
The resin composition of claim 17 wherein the maximum concentration of the epoxy and vinyl curing catalysts is about 30 percent by weight.
Claim 22
Dependent Claim
24 words
The resin composition of claim 14 wherein the polybutadiene moiety is present in a concentration of from about 15 to about 50% by weight.
Claim 23
Dependent Claim
24 words
The resin composition of claim 14 wherein the polybutadiene moiety is present in a concentration of from about 20% to about 30% by weight.
Claim 24
Dependent Claim
76 words
A curable flexibilized epoxy resin composition comprising a vinyl monomer and a prepolymer of the general formula: ##STR5## wherein N is a polymerization index of the polybutadiene moiety and has a value of about 50; wherein R is the portion of a diepoxy resin moiety between the terminal epoxide groups; and wherein N and R are selected so that the polybutadiene moiety has a weight percent of from about 15 to about 50 of the prepolymer.
Claim 25
Dependent Claim
76 words
A curable flexibilized epoxy resin composition comprising a vinyl monomer and a prepolymer of the general formula: ##STR5## wherein N is a polymerization index of the polybutadiene moiety and has a value of about 50; wherein R is the portion of a diepoxy resin moiety between the terminal epoxide groups; and wherein N and R are selected so that the polybutadiene moiety has a weight percent of from about 15 to about 50 of the prepolymer.
References Cited (Backward Citations)
US3296186A
Cited
US3989610A
Cited
US4025578A
Cited
US4014771A
Cited
US4016022A
Cited
US4173593A
Cited
US4284753A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-29 | 1989-01-28 | 1989-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-29 | 1993-01-28 | 1993-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-29 | 1997-01-28 | 1997-07-30 | $7700.00 | Window Closed / Lapsed |