Corrosion resisting copper alloy
Assignee: Granges Metallverken AB
•
Filing: 1980-09-29
•
Granted: 1985-07-30
•
Expires: 2000-09-29
Abstract
Abstract PCT No. PCT/EP80/00106 Sec. 371 Date May 27, 1981 Sec. 102(e) Date May 27, 1981 PCT Filed Sep. 29, 1980 PCT Pub. No. WO81/00860 PCT Pub. Date Apr. 2, 1981.A corrosion resisting copper alloy, especially suitable for use in fabricating heat exchangers, comprises 25 to 38% by weight zinc, 0.005 to 0.04% by weight phosphorus, the remainder of the alloy being copper, the alloy having a recrystallized grain size within the range of 2 mu to 10 mu .
Inventors
- 👤 Tatsuo Miura
- 👤 Kazuhiro Ohta
- 👤 Yoshiharu Hasegawa
- 👤 Takao Yoneyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:57
CPC Classifications
F; F28; F28F; F28F21/00; F28F21/08; F28F21/081; F28F21/085; C; C22; C22C; C22C9/00; C22C9/04; Y; Y10; Y10S; Y10S165/00; Y10S165/905
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
140 words
A method of producing a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of the alloy, 0.005 to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, comprising the steps of preparing said alloy in the form of an element having a small cross-section to permit rapid heating thereof; heating said alloy to a temperature of between 450 and 600 degrees for a period of time between 5 seconds and 5 minutes to recrystallize grain size and maintain the phosphorus in a substantially uniform solid solution; and cooling said alloy, said alloy being recrystallized with a grain size of between 2 and 10 microns and having a depth of corrosion after a 30 day salt water test which is not greater than 34 microns.
Claim 2
Independent Claim
140 words
A method of producing a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of the alloy, 0.005 to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, comprising the steps of preparing said alloy in the form of an element having a small cross-section to permit rapid heating thereof; heating said alloy to a temperature of between 450 and 600 degrees for a period of time between 5 seconds and 5 minutes to recrystallize grain size and maintain the phosphorus in a substantially uniform solid solution; and cooling said alloy, said alloy being recrystallized with a grain size of between 2 and 10 microns and having a depth of corrosion after a 30 day salt water test which is not greater than 34 microns.
Claim 3
Dependent Claim
13 words
A method according to claim 1, wherein said temperature is approximately 550° C.
Claim 4
Dependent Claim
13 words
A method according to claim 1, wherein said time is approximately 30 seconds.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein the alloy is annealed in the form of a strip having a thickness of less than 0.25 mm.
Claim 6
Dependent Claim
13 words
A method according to claim 2, wherein said time is approximately 30 seconds.
Claim 7
Dependent Claim
113 words
A heat exchanger which comprises a plurality of tubes in which a heat exchanging medium may flow and which are composed of a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of said alloy, 0.005% to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, the recrystallized grain size of said alloy being within the range of 2μ to 10μ inclusive, the phosphorus being in a substantially uniform solid solution within the grain of the alloy and the alloy having a depth of corrosion after a 30 day salt water test which is not greater than 34μ.
Claim 8
Dependent Claim
113 words
A heat exchanger which comprises a plurality of tubes in which a heat exchanging medium may flow and which are composed of a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of said alloy, 0.005% to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, the recrystallized grain size of said alloy being within the range of 2μ to 10μ inclusive, the phosphorus being in a substantially uniform solid solution within the grain of the alloy and the alloy having a depth of corrosion after a 30 day salt water test which is not greater than 34μ.
Claim 9
Dependent Claim
27 words
A heat exchanger according to claim 6, wherein the amount of phosphorus in said alloy is within the range 0.01% to 0.04% by weight of said alloy.
Claim 10
Dependent Claim
19 words
A heat exchanger according to claim 6, wherein said recrystallized grain size is within the range 3μ to 6μ.
Claim 11
Dependent Claim
19 words
A heat exchanger according to claim 7, wherein said recrystallized grain size is within the range 3μ to 6μ.
Claim 12
Dependent Claim
140 words
A heat exchanger which comprises a plurality of tubes in which a heat exchanging medium may flow and which are composed of a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of said alloy, 0.005% to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, the recrystallized grain size of said alloy being within the range of 2μ to 10μ inclusive, the phosphorus being in a substantially uniform solid solution within the grain of the alloy, the alloy having been recrystallized by having been heated to a temperature of between 450° and 600° C. for a period of time between 5 seconds and five minutes, and having a depth of corrosion after a 30 day salt water test which is not greater than 34μ.
Claim 13
Dependent Claim
140 words
A heat exchanger which comprises a plurality of tubes in which a heat exchanging medium may flow and which are composed of a copper alloy exhibiting corrosion resisting properties, said alloy consisting essentially of 25 to 38 percent zinc by weight of said alloy, 0.005% to 0.04 percent phosphorus by weight of said alloy, the balance of said alloy being copper, the recrystallized grain size of said alloy being within the range of 2μ to 10μ inclusive, the phosphorus being in a substantially uniform solid solution within the grain of the alloy, the alloy having been recrystallized by having been heated to a temperature of between 450° and 600° C. for a period of time between 5 seconds and five minutes, and having a depth of corrosion after a 30 day salt water test which is not greater than 34μ.
Claim 14
Dependent Claim
27 words
A heat exchanger according to claim 10, wherein the amount of phosphorus in said alloy is within the range 0.01% to 0.04% by weight of said alloy.
Claim 15
Dependent Claim
19 words
A heat exchanger according to claim 10, wherein said recrystallized grain size is within the range 3μ to 6μ.
Claim 16
Dependent Claim
19 words
A heat exchanger according to claim 11, wherein said recrystallized grain size is within the range 3μ to 6μ.
References Cited (Backward Citations)
CA543830A
Cited
US2131437A
Cited
FR894529A
Cited
US2224095A
Cited
US2261975A
Cited
US3615922A
Cited
GB1285561A
Cited
FR2249173A1
Cited
GB1437056A
Cited
JPS544814A
Cited
JPS54102226A
Cited
JPS54123520A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-29 | 1989-01-28 | 1989-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-29 | 1993-01-28 | 1993-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-29 | 1997-01-28 | 1997-07-30 | $7700.00 | Window Closed / Lapsed |