Abstract
Abstract A configuration for a light-weight composite armor comprises an outer layer of high content carbon steel; an inner laminate of multiple plies of ballistic grade fabric; and an intermediate core material interconnecting the outer steel to the fabric laminate in an established spaced relationship to defeat armor piercing projectiles from the outside while providing a reverse offensive threat from the inside.
Inventors
- 👤 Robert M. Brown
- 👤 Patrick E. Turner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:01
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/10; B32B3/12; F; F41; F41H; F41H5/00; F41H5/02; F41H5/04; F41H5/0442; F41H5/0457; F41H5/0464; B32B15/00; B32B15/04; B32B15/043; B32B15/12; B32B15/14; B32B15/18; B32B15/20; B32B5/00; B32B5/02; B32B5/024; B32B5/22; B32B5/24; B32B5/26; B32B7/00; B32B7/04; B32B7/12; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; B32B2262/00; B32B2262/02; B32B2262/0261; B32B2262/0269; B32B2262/10; B32B2262/101; B32B2305/00; B32B2305/02; B32B2305/024; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; B32B2571/00; B32B2571/02; Y; Y10; Y10S; Y10S428/00; Y10S428/911; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
113 words
A composite armor to provide a defensive barrier against armor piercing threats from the outside while also providing a reverse offensive shrapnel effect to the outside when impacted from the inside comprising in combination: an outer lamina of high carbon steel; an aluminum alloy sheet bonded to an inward-facing surface of the steel; an inner laminated structure of multiple plies of a ballistic grade fabric in a resin matrix; and a honeycomb core positioned intermediate and bonded to the aluminum alloy sheet and to the inner laminated fabric structure to form a composite, said honeycomb core establishing a spaced relationship between the steel and laminated fabric of at least 62 mm (2.4 inches).
Claim 2
Dependent Claim
113 words
A composite armor to provide a defensive barrier against armor piercing threats from the outside while also providing a reverse offensive shrapnel effect to the outside when impacted from the inside comprising in combination: an outer lamina of high carbon steel; an aluminum alloy sheet bonded to an inward-facing surface of the steel; an inner laminated structure of multiple plies of a ballistic grade fabric in a resin matrix; and a honeycomb core positioned intermediate and bonded to the aluminum alloy sheet and to the inner laminated fabric structure to form a composite, said honeycomb core establishing a spaced relationship between the steel and laminated fabric of at least 62 mm (2.4 inches).
Claim 3
Dependent Claim
26 words
The composite armor as set forth in claim 1 wherein the inner laminated fabric comprises a ballistic grade fiberglass woven roving fabric in a resin matrix.
Claim 4
Dependent Claim
19 words
The composite armor as set forth in claim 1 wherein the laminated fabric comprises a ballistic grade aramid fabric.
Claim 5
Dependent Claim
19 words
The composite armor as set forth in claim 1 wherein the honeycomb core comprises a light-to-medium weight paper honeycomb.
Claim 6
Dependent Claim
17 words
The composite armor as set forth in claim 1 wherein the honeycomb core comprises an aramid honeycomb.
Claim 7
Dependent Claim
25 words
The composite armor as set forth in claim 2 wherein the laminated fabric comprises at least fourteen plies of ballistic grade fiberglass woven roving fabric.
Claim 8
Dependent Claim
29 words
The composite armor as set forth in claim 1 where the lamina of steel comprises a modified steel having a carbon content within the range of 0.44 to 0.49.
Claim 9
Dependent Claim
29 words
The composite armor as set forth in claim 7 wherein the thickness of steel is within the range of 5.5 mm to 6.5 mm (0.22 inches to 0.26 inches).
Claim 10
Dependent Claim
33 words
The composite armor as set forth in claim 1 wherein a polysulfide adhesive bonds the aluminum sheet to the lamina of steel while also providing a galvanic barrier between said aluminum and steel.
Claim 11
Dependent Claim
40 words
The composite as set forth in claim 1 wherein the steel has a carbon content within the range 0.44-0.49, the inner laminated structure comprises at least fourteen plies of ballistic fiberglass fabric, and the honeycomb core comprises a paper honeycomb.
Claim 12
Dependent Claim
124 words
A composite armor to provide a defensive barrier against armor piercing threats from the outside while also providing a reverse offensive shrapnel effect to the outside when impacted from the inside comprising in combination: an outer lamina of steel having a carbon content within the range of 0.44-0.49 and a gauge thickness within the range of 5.5 mm to 6.5 mm; an aluminum alloy sheet bonded to an inward-facing surface of the steel; an inner laminated structure of multiple plies of a ballistic grade woven roving fabric in a resin matrix; and an intermediate honeycomb core structure bonded to the aluminum alloy sheet and laminated fabric to establish a spaced relationship between the steel and laminated fabric of at least 62 mm (2.4 inches).
Claim 13
Dependent Claim
124 words
A composite armor to provide a defensive barrier against armor piercing threats from the outside while also providing a reverse offensive shrapnel effect to the outside when impacted from the inside comprising in combination: an outer lamina of steel having a carbon content within the range of 0.44-0.49 and a gauge thickness within the range of 5.5 mm to 6.5 mm; an aluminum alloy sheet bonded to an inward-facing surface of the steel; an inner laminated structure of multiple plies of a ballistic grade woven roving fabric in a resin matrix; and an intermediate honeycomb core structure bonded to the aluminum alloy sheet and laminated fabric to establish a spaced relationship between the steel and laminated fabric of at least 62 mm (2.4 inches).
Claim 14
Dependent Claim
23 words
The composite armor as set forth in claim 11 wherein the laminated structure comprises a fiberglass woven roving fabric in a resin matrix.
Claim 15
Dependent Claim
17 words
The composite armor as set forth in claim 11 wherein the honeycomb core comprises a paper honeycomb.
Claim 16
Dependent Claim
35 words
The composite armor as set forth in claim 11 wherein a polysulfide adhesive bonds the aluminum sheet to the steel and also serves as a barrier to galvanic action as between the aluminum and steel.
Claim 17
Dependent Claim
25 words
The composite armor as set forth in claim 11 wherein the inner laminated structure comprises multiple plies of an aramid fabric in a resin matrix.
Claim 18
Dependent Claim
20 words
The composite armor as set forth in claim 11 wherein the intermediate honeycomb core structure comprises an aramid honeycomb core.
Claim 19
Dependent Claim
77 words
The composite armor as set forth in claim 11 wherein the laminated structure comprises at least fourteen plies of a ballistic grade fiberglass woven roving fabric in a resin matrix and the intermediate honeycomb core structure comprises a paper honeycomb bonded to the aluminum alloy sheet on one of its face surfaces, said aluminum alloy sheet being bonded to the outer lamina of steel via a polysulfide adhesive that prevents galvanic action between the aluminum and steel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |