Two coat one bake method for substrates which have metal and plastic component
Assignee: Kansai Paint Co Ltd
•
Filing: 1984-11-19
•
Granted: 1985-07-16
•
Expires: 2004-11-19
Abstract
Abstract A method of coating automotive outer parts having components made of metals and of plastics by a system of two coating steps and one baking step, the method comprising coating the surface of the metal and plastics components with a single base coat composition; coating the base coat over the metal component with a clear topcoat composition prepared for metal components and the base coat over the plastics component with a clear topcoat composition prepared for plastics components; and thermally curing the base coat and the topcoats, the two topcoat compositions being capable of fulfilling the following requirements: (i) the base resin for the topcoat composition for the metal components has a glass transition temperature higher by about 10° to about 100° C. than the base resin for the topcoat composition for plastics components; and (ii) (a) there is a difference of 0 to 4 dyne/cm in surface tension as measured upon application between the topcoat composition for metal components and the topcoat composition for plastics components; and/or (b) the topcoat composition for metal components contains 1 to 50 parts by weight of the base resin for the topcoat composition for plastics components per 100 parts by weight of the base resin for the topcoat composition for metal components and/or the topcoat composition for plastics components contains 1 to 50 parts by weight of the base resin for the topcoat composition for metal components per 100 parts by weight of the base resin for the topcoat composition for plastics components.
Inventors
- 👤 Yasuhiro Fujii
- 👤 Masaru Mitsuzi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:28
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/53; B05D7/532; B05D7/56; B05D7/57; B05D7/577; C; C08; C08J; C08J7/00; C08J7/04; C08J7/043
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
255 words
A method of coating automotive outer parts having components made of metals and those made of plastics by a system of two coating steps and one baking step, the method comprising the steps of coating the surface of the metal and plastics components with a single base coat composition; coating the base coat over the metal component with a clear topcoat composition prepared for metal components and the base coat over the plastics component with a clear topcoat composition prepared for plastics components; and thermally curing the base coat and the topcoats, the two topcoat compositions being capable of fulfilling the following requirements: (i) the base resin for the topcoat composition for the metal components has a glass transition temperature higher by about 10° to about 100° C. than the base resin for the topcoat composition for plastics components; and (ii) (a) there is a difference of 0 to 4 dyne/cm in surface tension as measured upon application between the topcoat composition for metal components and the topcoat composition for plastics components; and/or (b) the topcoat composition for metal components contains 1 to 50 parts by weight of the base resin for the topcoat composition for plastics components per 100 parts by weight of the base resin for the topcoat composition for metal components and/or the topcoat composition for plastics components contains 1 to 50 parts by weight of the base resin for the topcoat composition for metal components per 100 parts by weight of the base resin for the topcoat composition for plastics components.
Claim 2
Independent Claim
255 words
A method of coating automotive outer parts having components made of metals and those made of plastics by a system of two coating steps and one baking step, the method comprising the steps of coating the surface of the metal and plastics components with a single base coat composition; coating the base coat over the metal component with a clear topcoat composition prepared for metal components and the base coat over the plastics component with a clear topcoat composition prepared for plastics components; and thermally curing the base coat and the topcoats, the two topcoat compositions being capable of fulfilling the following requirements: (i) the base resin for the topcoat composition for the metal components has a glass transition temperature higher by about 10° to about 100° C. than the base resin for the topcoat composition for plastics components; and (ii) (a) there is a difference of 0 to 4 dyne/cm in surface tension as measured upon application between the topcoat composition for metal components and the topcoat composition for plastics components; and/or (b) the topcoat composition for metal components contains 1 to 50 parts by weight of the base resin for the topcoat composition for plastics components per 100 parts by weight of the base resin for the topcoat composition for metal components and/or the topcoat composition for plastics components contains 1 to 50 parts by weight of the base resin for the topcoat composition for metal components per 100 parts by weight of the base resin for the topcoat composition for plastics components.
Claim 3
Dependent Claim
47 words
A coating method as defined in claim 1 in which the glass transition temperature of the base resin for the topcoat composition for metal components is higher by about 20° to about 50° C. than that of the base resin for the topcoat composition for plastics components.
Claim 4
Dependent Claim
47 words
A coating method as defined in claim 1 in which the topcoat deposited on the base coat over the metal components has a surface tension which is different by 0 to 2 dyne/cm from that of the topcoat deposited on the base coat over the plastics components.
Claim 5
Dependent Claim
50 words
A coating method as defined in claim 1 in which the topcoat composition for metal components contains 1 to 20 parts by weight of the base resin for the topcoat composition for plastics components per 100 parts by weight of the base resin for the topcoat composition for metal components.
Claim 6
Dependent Claim
50 words
A coating method as defined in claim 1 in which the topcoat composition for plastics components contains 1 to 20 parts by weight of the base resin for the topcoat composition for metal components per 100 parts by weight of the base resin for the topcoat composition for plastics components.
Claim 7
Dependent Claim
91 words
A coating method as defined in claim 1 in which the topcoat composition for metal components contains 1 to 15 parts by weight of the base resin for the topcoat composition for plastics components per 100 parts by weight of the base resin for the topcoat composition for metal components and the topcoat composition for plastics components contains 1 to 15 parts by weight of the base resin for the topcoat composition for metal components per 100 parts by weight of the base resin for the topcoat composition for plastics components.
Claim 8
Dependent Claim
21 words
A coating method as defined in claim 1 in which the base coat has a dry thickness of 10 to 20μ.
Claim 9
Dependent Claim
37 words
A coating method as defined in claim 1 in which the topcoat composition for metal components and the topcoat composition for plastics components are capable of giving topcoats each having a dry thickness of 30 to 60μ.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |